Method for forming foam fireproof layer

A technology of foamable and refractory layers, which is applied in the field of formation of foamable refractory layers, can solve problems that have not yet been developed, and achieve the effect of excellent construction and excellent fire resistance

Active Publication Date: 2011-02-16
SK KAKEN CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] As mentioned above, although there is a demand for the development of a construction method that is not only easy to construct, but also exhibits excellent fire resistance performance on substrates with curved surfaces, it has not yet been developed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for forming foam fireproof layer
  • Method for forming foam fireproof layer
  • Method for forming foam fireproof layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0089] Examples and comparative examples are described below to further clarify the characteristics of the present invention. However, the present invention is not limited to these Examples.

[0090] (Manufacture of foamable refractory sheet)

[0091] (1) Foamable refractory sheet A

[0092] A raw material mixture containing 100 parts by weight of acrylic resin, 75 parts by weight of melamine, 75 parts by weight of dipentaerythritol, 370 parts by weight of ammonium polyphosphate, and 105 parts by weight of titanium oxide was fully kneaded with a kneader. Then, the kneaded product was rolled with a calender roll together with the fibrous sheet, thereby producing a foamable fireproof sheet A having a film thickness of 2 mm.

[0093] In addition, as the above-mentioned fibrous sheet, a sheet of nonwoven fabric in which polyester fibers were laminated on a glass mesh (thickness: 0.18 mm, mesh spacing: 10 mm×10 mm) was used.

[0094] (2) Foamable refractory sheet B

[0095] A r...

Embodiment 1

[0105] As the base material, a square steel pipe (150 mm×150 mm in cross section, 9 mm in thickness, and 1200 mm in length) subjected to antirust coating treatment was used. After fully coating the acrylic resin adhesive on the substrate with a roller, 3 foamable fireproof sheets A obtained by the above method, such as figure 2 As shown, glue the ends of the sheets to each other so that the seam width of the butt joint is 2mm. At this time, the foamable fire-resistant sheet A is pasted so that the surface on the side of the fibrous sheet is bonded to the base material. In addition, a moisture-curable polyurethane-based sealing material is filled with a spatula at the joint of the butt joint.

[0106] Then, brush the foamable refractory paint A on the entire outer peripheral surface (including the butt joint) pasted with the foamable fireproof sheet A, make the dry film thickness 0.5mm, and maintain and dry for 7 days.

[0107] A heating test was performed on the test body p...

Embodiment 2

[0126] Except having used the foamable fireproof sheet B as a foamable fireproof sheet, the test body was produced similarly to Example 1, and the heating test was performed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a method for forming a foaming flame retardant coating which is not only easy to be constructed but also exerts excellent fire resistance. The forming method of the foaming flame retardant coating is used to form the foaming flame retardant coating and the method is characterized in that the method comprises the working procedures of: (1) a first working procedure of using one piece or more than two piece of foaming fire-resistant sheet material, butt-jointing the end part of the sheet material to each other, and forming a sheet material layer which is formedby one layer or a plurality of layers at the substrate; and (2) a second working procedure of coating foaming fireproof coating to the sheet material layer with the mode that the foaming fireproof coating can be exerted to at least the butt-jointing part.

Description

technical field [0001] The present invention relates to a method for forming a foamable refractory layer. Background technique [0002] When structures such as buildings and civil engineering structures are exposed to high temperatures due to fire or the like, there is a problem that the mechanical strength of steel bars, concrete, etc., which are base materials of these structures, decreases rapidly. [0003] In response to this problem, for example, a foamable fire-resistant sheet has been proposed which delays the temperature rise of the base material and temporarily suppresses a decrease in the physical strength of the base material by forming a carbonized layer by foaming at a high temperature such as a fire. (Japanese Patent Laid-Open No. 8-60763). [0004] Advantages of such a foamable refractory sheet include the ability to form a thinner film thickness and ease of film thickness control during construction, compared with common refractory covering materials. Compa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04B1/94
CPCF16L59/20E04F13/0733E04B1/94
Inventor 轻贺英人山本将贵
Owner SK KAKEN CO LTD