Non-woven fabrics composite economy master batch and its producing method and device

A kind of production equipment and non-woven fabric technology, applied in the field of non-woven fabric composite economic masterbatch, can solve the problems of long residence time of materials, high production process requirements, poor dispersion and mixing, and achieve the effect of saving energy and reducing material costs

Inactive Publication Date: 2008-02-13
胡国川
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, some processes require the use of low-boiling substances that are immiscible with the mediator to dissolve and separate the additives required in the product from the blend. If the current usual process and equipment are used, the process will be complicated and costly. Time-consuming and labor-intensive, there are constraints on production, for which these processes require the use of new processes and equipment modifications
[0004] The currently used single-screw extruder usually compresses the material entering the feeding section according to a certain compression ratio according to the direction of screw rotation, and then mixes and disperses in the mixing section. The devolatilization effect is poor, and it needs to go through two or The dispersion and devolatilization requirements of the final performance can be completed only after three times of repeated processing
The twin-screw extruder used is an effective equipment that can complete the blending and homogenization and devolatilization process of various blending logistics systems, but the co-rotating twin-screw extrusion has a large shearing effect on the material. The period is under high temperature and high pressure, especially after the material has completed various properties, its fluid is still extruded at a very high temperature, which will have an adverse effect on certain properties of the product, and the high temperature extruded product has poor density. , easy to absorb water twice
At the same time, the self-cleaning property of the twin-screw extruder is poor, resulting in a long residence time of the material, poor dispersion and mixing, and extremely high requirements on the production process, which limits their respective applications in production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-woven fabrics composite economy master batch and its producing method and device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] 1. Preparation

[0043] Weigh 15kg of polypropylene resin with a melting index of 90, 8kg of polypropylene resin with a melting index of 3, 60kg of nano-scale activated calcium carbonate, 9kg of polyethylene wax, 0.6kg of composite antioxidant, 2kg of zinc stearate, titanate 2kg, white oil 1.7kg, rutile titanium dioxide 1.7kg.

[0044] 2. Ingredients

[0045] Put the above-mentioned raw materials in a stirring container according to the proportion, and stir and mix evenly.

[0046] 3. Forming

[0047] Send the well-mixed compound into the twin-screw extruder to make it fully mixed, melted, dispersed and extruded. During this process, the temperature is controlled by circulating water.

[0048] 4. Granulation

[0049] The molded product extruded by the twin-screw extruder is sent to the single-screw extruder, and the finished non-woven fabric is obtained through melt extrusion, pelletizing, and vibrating sieve screening, and can be packaged.

Embodiment 2

[0051] 1. Preparation

[0052] Weigh 15kg of polypropylene resin with a melting index of 60, 8kg of polypropylene resin with a melting index of 30, 60kg of nano-scale activated calcium carbonate, 9kg of polyethylene wax, 0.6kg of composite antioxidant, 2kg of zinc stearate, titanate Coupling agent 2kg, white oil 1.7kg, rutile titanium dioxide 1.7kg.

[0053] The rest are the same as Example 1.

[0054] The above-mentioned production process adopted a stepped screw extruder, the structure of which is shown in Figure 1. The stepped screw extruder consists of a first-stage twin-screw extruder and a second-stage single-screw extruder. The first-stage twin-screw extruder and the second-stage single-screw extruder are arranged in a "T" shape, and the outlet of the first-stage twin-screw extruder is connected to the inlet of the second-stage single-screw extruder. The material ends are connected.

[0055]The first-stage twin-screw extruder is mainly composed of a driving motor I1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
aspect ratioaaaaaaaaaa
Login to view more

Abstract

The invention relates to a non-woven composite economical masterbatch and its production method and equipment. The masterbatch formula is: 12-18 parts of polypropylene resin with a melting index of 60-90, and polypropylene with a melting index of 3-30 Resin 6-10, nano-scale activated calcium carbonate 55-65, polyethylene wax 8-10, composite antioxidant 0.5-0.7, zinc stearate 1.5-2.5, titanate 1.5-2.5, white oil 1.5-2, Rutile titanium dioxide 1.5-2; the masterbatch production method is as follows: the raw materials are fully mixed and sent to the twin-screw extruder, and then sent to the single-screw extruder, and the finished non-woven fabric is obtained through melt extrusion, pelletizing and screening; The production equipment used is a stepped screw extruder, including a first-stage twin-screw extruder and a second-stage single-screw extruder, and the two extruders are arranged in a "T" shape. The present invention uses nano-scale active calcium carbonate to partially replace the PP material for non-woven fabrics, and adds the present invention to the raw material PP used for non-woven fabrics, which can greatly reduce the cost of materials under the premise of ensuring continuous fibers by melt-blowing and calendering, and Can save a lot of energy.

Description

Technical field: [0001] The invention relates to a nonwoven fabric. In particular, it relates to a non-woven composite economical masterbatch used as non-woven fabric, which partially replaces PP, and a production method and equipment thereof. The invention belongs to the technical field of materials for nonwoven fabrics and special production equipment thereof. Background technique: [0002] The raw materials for making non-woven fabrics used to be PP (polypropylene). PP is a by-product of petroleum, which is expensive and consumes a lot of energy. [0003] At present, the processing technology of filling modification, functional masterbatch, and color masterbatch is generally: use a high-speed rotary mixer to fully mix the mediator and various additives with inorganic substances, dehydrate and activate to form a semi-dissolved mass, and then use crushing After the extruder is crushed, the granulation process is completed with a single-screw or twin-screw extruder. With ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K5/09C08L23/06C08K3/26C08K3/22
Inventor 胡国川
Owner 胡国川
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products