Formula of nylon/aramid fiber composite cord hanging glue for aircraft tire
A technology of aviation tires and nylon, applied in the direction of adhesives, adhesive types, natural rubber adhesives, etc., can solve the problem of insufficient adhesion of rubber materials, achieve high adhesion retention rate, safe use, and off-line Combined with strong effect
Active Publication Date: 2010-04-07
中国化工集团曙光橡胶工业研究设计院有限公司
View PDF5 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the aramid fiber in the nylon / aramid composite cord has the disadvantage of not having a high degree of adhesion to the rubber compound. Therefore, a new type of nylon / aramid composite cord with high bonding strength is designed, and the bond remains after heat aging. It is very important to have a high rate of hanging glue. At present, nylon / aramid composite cord hanging glue is still blank.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1 Embodiment 2 Embodiment 3
[0030] raw material name
[0031] Amount of each component Amount of each component Amount of each component
[0032] 1 # Smoked sheet glue 80 90 95
[0033] SBR 1500 20 10 5
[0034] High wear-resistant carbon black N330 or N375 50 45 40
[0035] Highly dispersed white carbon black Jcsil150 or Ultrasil7000GR 5 10 15
[0036] Silane coupling agent WD-40 or KH-845-4 2 2 2
[0038] Stearic acid 2 2 2
[0039] p-phenylenediamine antioxidant 4020 or 4010NA 2 2 2
[0040] Ketoamine antioxidant RD 1.5 1.5 1.5
[0041] Insoluble sulfur IS-60 or IS-90 2.0 2.5 1.5
[0042] Sulphenamide accelerator NOBS or NS or CZ 1.5 1.2 1.0
[0043] Adhesion Promoter AIR-101 and Adhesion Promoter AIR-1 9 9 9
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The present invention discloses a prescription of nylon and aramid fibre composite cord coating used for an aircraft tire and is characterized in that glue stock considers caoutchouc as the main material and contains the main auxiliary materials of styrene butadiene rubber, adhesion promoter, high abrasion furnace black, high dispersion white carbon black, silane coupling agent, indiscerptible sulfur and sulfenamide accelerant. The main material and the main auxiliary materials are mixed and milled by an internal mixer according to the certain proportion. The glue stock of the prescription hasthe advantages that the adhesion strength of the nylon and aramid fibre composite cord with the glue stock of rubber can be improved; the adhesion holding rate after thermal aging is high; a tread bracing layer part does not have the quality problems of glue-cord delamination and the delamination between layers when the glue stock is used under the rigorous using condition with high tensile strength, high tear strength and high load.
Description
Technical field: [0001] The invention relates to a polymer rubber material, in particular to the formulation of nylon / aramid composite cord hanging glue for aviation tires. Background technique: [0002] The skeleton materials used in the production of known aviation tires are mostly nylon cords. With the improvement of aircraft technical indicators, aviation tires are moving toward high speed, high load, light weight, long life, impact resistance, puncture resistance, and safer use. develop. Replacing nylon cords with nylon / aramid composite cords as the skeleton material of aircraft tires is a major breakthrough in aircraft tire manufacturing technology. The nylon / aramid composite cord has been patented separately. However, the aramid fiber in the nylon / aramid composite cord has the disadvantage of not having a high degree of adhesion to the rubber compound. Therefore, a new type of nylon / aramid composite cord with high bonding strength is designed, and the bond remains a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine