Method for making aluminum foil adhesive tape

A production method and adhesive tape technology, applied in the direction of adhesives, film/sheet adhesives, etc., can solve the problems of large amount of raw materials, high production costs, and restrictions on the high temperature resistance of adhesive tapes, and shorten the production process , save raw materials, and ensure the effect of high temperature resistance

Inactive Publication Date: 2012-01-11
苏州振宇材料科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But above-mentioned patent still has shortcoming, the one, although have saved release paper, because any kind of film in polyethylene (PE) or polyester (PET) or biaxially stretched polypropylene (BOPP) is made earlier One side of the surface is compounded to the surface of the aluminum foil substrate coated with a composite adhesive layer, specifically see the description of step C of the patent, and then the other side of the aforementioned film or the back is coated with a treatment agent
Therefore, the production process is relatively cumbersome; second, because the aforementioned PE or PET or BOPP film is compounded on the surface of the aluminum foil substrate, the high temperature resistance of the finished adhesive tape is restricted; Large amount of raw materials and high production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making aluminum foil adhesive tape
  • Method for making aluminum foil adhesive tape
  • Method for making aluminum foil adhesive tape

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A). Select high-quality aluminum foil substrate 1;

[0022] B). Use a coating machine to coat the surface of one side of the aluminum foil substrate 1 with silicone oil, and while coating, it is dried in an oven at a temperature of 90°C, so that the surface of one side of the aluminum foil substrate 1 forms silicone oil. Layer 2, wherein: silicone oil is composed of 1 part of dibutyltin dilaurate, 2 parts of ethyl orthosilicate, 9 parts of silicone oil, 9 parts of yellow resin, 20 parts of silicone rubber, 60 parts of polyethylene resin, 120 parts of acetone 100 parts and 600 parts of toluene at normal temperature and pressure with the organic silicone oil that is evenly stirred by hand or mechanical stirring mode, the yellow resin as the silicone oil preferably adopts the brand that is produced by China Shanghai Resin Research Institute and is 107 yellow resin. The silicone rubber is commercially available grade 107 silicone rubber;

[0023] C). Place it at room tempe...

Embodiment 2

[0027] A). Select high-quality aluminum foil substrate 1;

[0028] B). Use a coating machine to coat the surface of one side of the aluminum foil substrate 1 with silicone oil, and while coating, it is dried in an oven at a temperature of 115°C, so that the surface of one side of the aluminum foil substrate 1 forms silicone oil. Layer 2, wherein: silicone oil is composed of 1 part of dibutyltin dilaurate, 1.5 parts of ethyl orthosilicate, 11 parts of silicone oil, 25 parts of silicone rubber, 65 parts of polyethylene resin, 130 parts of acetone 107 parts and 650 parts of toluene at normal temperature and pressure with manual or mechanical stirring of organic silicone oil, the yellow resin as silicone oil preferably adopts the brand of 107 yellow resin produced by China Shanghai Resin Research Institute, said The silicone rubber is commercially available grade 107 silicone rubber;

[0029] C). Place it at room temperature for 50 hours after winding out of the drying tunnel as ...

Embodiment 3

[0033] A). Select high-quality aluminum foil substrate 1;

[0034] B). Use a coating machine to coat the surface of one side of the aluminum foil substrate 1 with silicone oil, and while coating, it is dried in an oven at a temperature of 125°C, so that the surface of one side of the aluminum foil substrate 1 forms silicone oil. Layer 2, wherein: silicone oil is composed of: 1 part of dibutyltin dilaurate, 1.8 parts of ethyl orthosilicate, 12 parts of silicone oil or yellow resin, 28 parts of silicone rubber, 68 parts of polyvinyl chloride resin, acetone 145 parts and 700 parts of toluene are uniformly stirred by manual or mechanical stirring at normal temperature and pressure. The yellow resin used as the silicone oil is preferably 107 yellow resin produced by the Shanghai Resin Research Institute of China. The silicone rubber described is commercially available grade 107 silicone rubber;

[0035] C). Place it at room temperature for 64 hours after winding out of the drying ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for manufacturing aluminium foil adhesive tape for cementing refrigerating installations such as a condenser pipe of a refrigerator or a refrigerator and the inner container of the box body of a refrigerator or the outer wall of the inner container of the refrigerator body of a refrigerator, the method comprises the following steps: choosing aluminium foil material, coating silicone oil on the surface one side of aluminium foil substrate, and drying by a drying channel as soon as coating, placing in ageing effect under normal temperature after getting out of a drying channel and being winded up, and coating pressure-sensitive adhesive on the surface of the other side of the aluminium foil substrate after placing in aging effect, and dying by a drying channel as soon as coating, winding up, parting cut, and getting aluminium foil adhesive tape end products. The manufacturing method has the advantages that since thin film and aluminium foil substrate are not needed to composite, therefore the method can not be restricted by high temperature resistance shortage, which is beneficial for guaranteeing high-temperature resisting property of products, saving raw material, and shortening manufacture process, the combining rate of adhesive tape products which are got by the method and polyurethane foaming material can reach100%, stripping strength can reach16-20N / cm, and persistent adhesivity time can reach more than 1000hs.

Description

technical field [0001] The invention relates to a method for making an aluminum foil adhesive tape, more specifically, a method for bonding a condensation pipe of a refrigeration device such as a refrigerator or a freezer to the inner liner of a refrigerator or to the outer wall of the inner liner of a freezer The production method of aluminum foil adhesive tape. Background technique [0002] Chinese patent authorization announcement number CN1208416C discloses a processing method of aluminum foil adhesive tape. Deficiencies exhibited by insulating aluminum foil adhesive tape. Regarding the lack of these two adhesive tapes, since the objective evaluation has been made in the background technology column of the above-mentioned patent, the applicant will not repeat them. But above-mentioned patent still has shortcoming, the one, although have saved release paper, but because any one film in polyethylene (PE) or polyester (PET) or biaxially oriented polypropylene (BOPP) One ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/02
Inventor 王振明
Owner 苏州振宇材料科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com