Hydrophobic self-cleaning sanitary ware glaze and preparation thereof

A self-cleaning technology for sanitary ware, which is applied in the glaze field of porcelain or stoneware sanitary ware, can solve the problems of poor wear resistance and shedding of the film layer, and achieve good hydrophobicity, reduce surface energy, and long-lasting self-cleaning effect

Inactive Publication Date: 2008-10-01
JINGDEZHEN CERAMIC INSTITUTE
View PDF1 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this process achieves the effect of hydrophobicity and improves the antifouling performance to a certain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophobic self-cleaning sanitary ware glaze and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-6

[0023] Prepare the raw materials according to the composition in Table 1-3, and process parameters in Table 4. After crushing, mixing ball milling, sieving, spraying the first layer of opaque glaze, drying, spraying the second layer of transparent glaze, drying, and firing to obtain the hydrophobic performance Self-cleaning sanitary ware glaze.

[0024] Table 1 The composition of opacified glaze material formula (mass fraction%)

[0025] raw material

Example 1

Example 2

Example 3

Example 4

Example 5

Example 6

quartz

40

32

34

36

32

40

Potassium feldspar

16

22

20

18

18

16

Aluminum oxide

2

3

3

4

3

2

Suzhou soil

6

7

8

6

6

4

Calcite

13

14

14

13

15

15

dolomite

3

3

4

4

5

5

Zinc oxide

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a self-cleaning sanitary ware glaze with hydrophobic property and a preparation method thereof. The self-cleaning sanitary ware graze comprises ground graze and cover glaze and is characterized in that: the cover glaze is added with fluoride and titanium oxide; refinement is done to the grain size of the glaze material which is burned at a time under the temperature of 1150 to 1300 DEG C, thus obtaining the self-cleaning sanitary ware glaze. The self-cleaning sanitary ware glaze of the invention has the advantage of ensuring the prepared sanitary ware has lucent and clean surfaces and lasting self-clean effect and the surfaces of the sanitary ware are easily cleaned with stain resistant.

Description

technical field [0001] The invention relates to a porcelain or stoneware sanitary ware glaze, in particular to a self-cleaning sanitary ware glaze with hydrophobic function and a preparation method thereof. Background technique [0002] Sanitary ware is widely used in daily life due to its beauty, practicality and other advantages. Although the glaze layer on the surface of the sanitary ware is quite dense and smooth, due to the limitation of the production process, there are still tiny pinholes and unevenness on the surface, which makes it contact with some pollutants during use, such as urine and urine. , Scale, urine scale, soap foam, fatty acid, amino acid, etc., under the action of various physical or chemical forces such as van der Waals force, capillary force, hydrogen bond, etc., are easy to accumulate on the unevenness of the surface of the sanitary ware or enter the micropores, resulting in sanitary ware pollution. The pollution on the surface of sanitary ware no...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 李月明黄丹廖润华顾幸勇
Owner JINGDEZHEN CERAMIC INSTITUTE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap