Wet-rub resistant styrene-acrylic emulsion and preparation thereof

A styrene-acrylic emulsion and moisture-resistant technology, applied in the field of polymer emulsions, can solve problems such as failure to meet requirements, and achieve the effects of easy control, simple process and stable polymerization system

Inactive Publication Date: 2011-05-18
传化智联股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, people such as Zhou Yan published an article "The Development of Styrene Acrylic Emulsion for Architectural Coatings" in the 2nd issue of "Colloid and Polymer" in 2005, which adjusted the ratio of soft and hard monomers and changed the amount of acrylic acid monomers. And adding functional monomers such as hydroxyethyl acrylate, N-methylol acrylamide and other means to improve the wet rub resistance of styrene-acrylic emulsion, although this method has improved the wet rub resistance of styrene-acrylic emulsion to a large extent, but in Some conditions that require high wet rub resistance still fail to meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 1. The raw material formula of styrene-acrylic emulsion is as follows:

[0016] Raw material name Core-shell distribution Feed ratio (%)

[0017] Styrene (St) 2 / 3 as the core layer component, 1 / 3 as the shell layer component 21

[0018] Butyl acrylate (BA) 2 / 3 as the core layer component, 1 / 3 as the shell layer component 21

[0019] Methyl methacrylate (MMA) 2 / 3 as core layer component, 1 / 3 as shell layer component 2

[0020] Acrylic (AA) shell component 0.7

[0021] Methacrylamidoethylethyleneurea (MAEEU) shell component 0.2

[0022] OP-10 1.1

[0023] Sodium dodecyl sulfate (SDS) 0.8

[0024] Sodium bicarbonate (NaHCO 3 ) 0.2

[0025] Ammonium persulfate (APS) 0.3

[0026] Deionized water 52.7

[0027] Two, the preparation method of styrene-acrylic emulsion is as follows:

[0028] First, dissolve 2 / 3 of the emulsifier SDS and OP-10 in water, then mix with 2 / 3 of styrene (St), butyl acrylate (BA), and methyl methacrylate (MMA), and stir vigorously for 30 minu...

Embodiment 2

[0030] 1. The raw material formula of styrene-acrylic emulsion is as follows:

[0031] Raw material name Core-shell distribution Feed ratio (%)

[0032] Styrene (St) 1 / 2 as the core layer component, 1 / 2 as the shell layer component 21

[0033] Butyl acrylate (BA) 1 / 2 as the core layer component, 1 / 2 as the shell layer component 21

[0034] Methyl methacrylate (MMA) 2 / 3 as core layer component, 1 / 3 as shell layer component 2

[0035] Acrylic (AA) shell component 0.7

[0036] Methacrylamidoethylethyleneurea (MAEEU) shell component 0.3

[0037] TX-10 1.1

[0038] Sodium dodecyl sulfate (SDS) 0.8

[0039] Sodium bicarbonate (NaHCO 3) 0.2

[0040] Ammonium persulfate (APS) 0.3

[0041] Deionized water 52.6

[0042] Two, the preparation method of styrene-acrylic emulsion is as follows:

[0043] First, dissolve 1 / 2 of the emulsifier SDS and TX-10 in water, and then mix with 1 / 2 and 1 / 3 of methyl methacrylate (MMA) of styrene (St) and butyl acrylate (BA). Stir for 30 minute...

Embodiment 3

[0045] 1. The raw material formula of styrene-acrylic emulsion is as follows:

[0046] Raw material name Core-shell distribution Feed ratio (%)

[0047] Styrene (St) 1 / 2 as the core layer component, 1 / 2 as the shell layer component 15

[0048] Butyl acrylate (BA) 1 / 2 as the core layer component, 1 / 2 as the shell layer component 21

[0049] Methyl methacrylate (MMA) 1 / 2 as the core layer component, 1 / 2 as the shell layer component 8

[0050] Acrylic (AA) shell component 0.5

[0051] Methacrylamidoethylethyleneurea (MAEEU) shell component 0.4

[0052] TX-10 1.1

[0053] Sodium dodecyl sulfate (SDS) 0.8

[0054] Sodium bicarbonate (NaHCO 3 ) 0.2

[0055] Ammonium persulfate (APS) 0.4

[0056] Deionized water 52.6

[0057] Two, the preparation method of styrene-acrylic emulsion is as follows:

[0058] First, dissolve 1 / 2 of the emulsifier SDS and TX-10 in water, then mix with 1 / 2 of styrene (St), butyl acrylate (BA), and methyl methacrylate (MMA), and stir vigorously for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wet-rub resistant styrene-acrylic emulsion and the preparation method. The existing styrene-acrylic emulsion still can not reach the requirements under the conditions with high wet-rub resistance. The invention is takes styrene, butyl acrylate, methyl methacrylate and acrylic acid as the polymeric monomer of the system, the functional monomers containing ureido as the modified monomer of the system, compound emulsifiers as the emulsifier of the system, and thermal decomposition initiators as the initiator of the system, so as to prepare and obtain the wet-rub resistant styrene-acrylic emulsion through core-shell polymerization. The invention adopts the core-shell polymerization technology to enable the functional monomer components to be mainly distributed in theshell layers by controlling the dropping rate, so as to achieve the purpose of modifying the styrene-acrylic emulsion. The styrene-acrylic emulsion obtained through such a method has better wet-rub resistant performance and can be used as the base material of interior and exterior wall coatings, which has good prospects for development.

Description

technical field [0001] The invention relates to a polymer emulsion, in particular to a wet rub-resistant styrene-acrylic emulsion and a preparation method thereof. Background technique [0002] Styrene-acrylic emulsion is a copolymerized emulsion of styrene and acrylate monomers. The styrene-acrylic emulsion paint formulated with it as the main film-forming substance is non-toxic, non-environmental polluting, and has good weather resistance, color retention, and water resistance. , Alkali resistance, so it has been widely used in latex paint for interior and exterior walls and other water-based paints. my country began to develop styrene-acrylic emulsion in the 1970s, and it was officially put into use in the 1980s. Up to now, there are still some problems in the actual application process, especially compared with similar foreign products, there is still a considerable gap, such as The minimum film forming temperature is high, the stability of calcium particles is low, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F220/18C08F2/24C08F4/30C08F220/14C08F220/06
Inventor 张高奇原玉锋王小君罗巨涛
Owner 传化智联股份有限公司