Method for manufacturing high-alumina-quality high-temperature crucible pot

A high-temperature-resistant, high-alumina technology, which is applied in the field of preparation of high-alumina high-temperature-resistant crucibles, can solve the problems of strong target use, high equipment requirements, and high raw material costs, so as to save the cost of mechanical equipment, reduce production costs, The effect of long service life

Active Publication Date: 2011-03-16
中铝矿业有限公司 +1
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above existing technologies have disadvantages such as high cost of raw materials, high requirements for equipment, and strong pertinence to objects of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0017] The bauxite clinker (cooked ore aluminum content above 88%, particle size 100 mesh) 63.5%, α-Al 2 o 3 (Alpha alumina particle size 1-2 microns) 24%, Suzhou soil 5%, silicon carbide (500 mesh) 1.5%, cooked talc 3%, zircon 3%, binder gum arabic dry powder 0.5%, etc. According to 6: 2.5∶0.5∶0.2∶0.3∶0.3∶0.05, weigh them together, put them into a ball mill and mix them for 20 hours. After grinding and mixing evenly, add 40% water and mix them with water. After the slurry is evenly mixed, use injection Slurry molding, the slurry is injected into the designed model to form, after curing and drying, it is calcined at 1570°C for 10 hours in a high-temperature furnace, and a high-alumina clinker high-temperature-resistant crucible with good performance can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a high alumina heat resistant crucible, relating to a method for preparing the high alumina ceramic crucible which is applied to experiment manufacturing processes such as the high temperature sintering and high temperature chemical synthesis. The method is characterized by comprising the following steps that: raw materials of alumyte grog refractory,alpha-Al2O3, Suzhou clay, carborundum, cooked pencil stone, zirconite, an appropriate amount of a caking agent of Arabian gum dry powder are subject to matching, grinding and watering to prepare slurry; after the casting process, the proximate matter is dried and calcined so that the high alumina heat resistant crucible is prepared. The high alumina heat resistant crucible has good chemical stability, good thermal physics properties such as the heat-resistant stability and the quake-resistance stability, long service life and easy popularization in industry.

Description

technical field [0001] A method for preparing a high-alumina high-temperature-resistant crucible relates to a method for preparing a high-alumina ceramic crucible used in experimental production processes such as high-temperature sintering and high-temperature chemical synthesis. Background technique [0002] High-temperature sintering of many materials and chemical reactions at high temperatures need to be carried out in a high-temperature furnace in a high-temperature-resistant crucible. Such ceramic crucibles are made of corundum, spinel, mullite, cordierite, clay and carbon. Ceramic crucibles have the advantages of good chemical stability, high temperature resistance, corrosion resistance, etc., and are widely used. However, this type of crucible also has fatal shortcomings, that is, poor toughness, high brittleness, and low thermal shock resistance. In order to improve this shortcoming, carbides and carbides are often used as the main raw material to prepare high-tempe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C04B35/14C04B35/622
Inventor 杨建平全玉闫晋钢杨燕崔建奇
Owner 中铝矿业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com