Organic-inorganic composite flame retardants with mesoporous molecular sieve and method for preparing same

A mesoporous molecular sieve and inorganic composite technology, which is applied in the polymer field to achieve the effects of improving thermal stability, preventing the migration of flame retardants, and improving thermal stability.

Inactive Publication Date: 2009-01-07
TORAY FIBER RES INST(CHINA) CO LTD
View PDF8 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Combining inorganic mesoporous molecular sieves with organic flame retardants to obt...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic-inorganic composite flame retardants with mesoporous molecular sieve and method for preparing same
  • Organic-inorganic composite flame retardants with mesoporous molecular sieve and method for preparing same
  • Organic-inorganic composite flame retardants with mesoporous molecular sieve and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Drying of mesoporous molecular sieves: Dry 21g of MCM-41 mesoporous molecular sieves at 250°C for 2 hours under a vacuum condition with a pressure less than 0.1MPa to remove moisture and small air molecules in the pores of the molecular sieves;

[0068] Flame retardant pretreatment: Thin the viscosity of 279g liquid RDP flame retardant at 100°C to obtain a flame retardant liquid with better fluidity;

[0069] Immersion of mesoporous molecular sieve powder and flame retardant: In vacuum conditions with a pressure less than 0.1MPa, introduce the pretreated RDP flame retardant liquid into the dried MCM-41 mesoporous molecular sieve, so that the flame retardant liquid and the medium Porous molecular sieves are fully soaked, soaked at 100°C for 3 hours, and at room temperature for 20 hours;

[0070] Post-treatment of the flame retardant: the obtained flame retardant vacuum-soaked mesoporous molecular sieve system was ultrasonically oscillated at a frequency of 59kHz for 1h, ...

Embodiment 2

[0072] Drying of mesoporous molecular sieves: Dry 36g of MCM-41 mesoporous molecular sieves at 250°C for 2 hours under vacuum conditions with a pressure less than 0.1MPa to remove moisture and small air molecules in the pores of the molecular sieves;

[0073] Flame retardant pretreatment: Thin the viscosity of 264g liquid RDP flame retardant at 100°C to obtain a flame retardant liquid with better fluidity;

[0074] Immersion of mesoporous molecular sieve powder and flame retardant: In vacuum conditions with a pressure less than 0.1MPa, introduce the pretreated RDP flame retardant liquid into the dried MCM-41 mesoporous molecular sieve, so that the flame retardant liquid and the medium Porous molecular sieves are fully soaked, soaked at 100°C for 3 hours, and at room temperature for 20 hours;

[0075]Post-treatment of the flame retardant: the obtained flame retardant vacuum-soaked mesoporous molecular sieve system was ultrasonically oscillated at a frequency of 59kHz for 1h, an...

Embodiment 3

[0077] Drying of mesoporous molecular sieves: Dry 21g of SBA-15 mesoporous molecular sieves at 220°C for 5 hours under vacuum conditions with a pressure less than 0.1MPa to remove moisture and small air molecules in the pores of the molecular sieves;

[0078] Flame retardant pretreatment: Thin the viscosity of 279g of liquid IPPP flame retardant at 100°C to obtain a flame retardant liquid with better fluidity;

[0079] Immersion of mesoporous molecular sieve powder and flame retardant: In vacuum conditions with a pressure less than 0.1MPa, introduce the pretreated IPPP flame retardant liquid into the dried SBA-15 mesoporous molecular sieve, so that the flame retardant liquid and the medium Porous molecular sieves are fully soaked, soaked at 90°C for 2 hours, and at room temperature for 25 hours;

[0080] Post-treatment of the flame retardant: the obtained flame retardant vacuum-soaked mesoporous molecular sieve system was oscillated with ultrasonic waves at a frequency of 100k...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an organic-inorganic composite flame retardant agent containing a mesopore molecular sieve. The flame retardant agent comprises 0.1-50 weight percent of mesopore molecular sieve and 50-99.9 weight percent of organic flame retardant agent. The preparation method of the flame retardant agent and flame retardant resin containing the flame retardant agent are also disclosed. The composite flame retardant agent obtained through the invention plays roles of both the self-flame retardant function of organic flame retardant molecules and the mesopore molecular sieve and the synergistic effect between the organic flame retardant molecules and the mesopore molecular sieve. The flame retardant efficacy is improved greatly. In addition, the mesopore molecular sieve can also play a releasing role of a microcapsule. As a novel highly efficient halogen-free composite flame retardant agent, the organic-inorganic composite flame retardant agent can be widely applied to the polymer material flame retarding field.

Description

technical field [0001] The invention belongs to the field of macromolecules, and in particular relates to a composite flame retardant containing mesoporous molecular sieve, a preparation method thereof, and a flame-retardant resin containing the flame retardant. Background technique [0002] In recent years, polymers and their alloy materials have been widely used in various fields such as electronics, communication cables, transportation, and construction. However, since most polymer materials are combustible, if flame retardancy is not considered, accidents with large losses such as fires will often be caused. In order to reduce the flammability of polymer materials, prevent fire accidents and reduce economic losses, people pay more and more attention to flame retardant technology. [0003] Generally, adding flame retardants to polymer materials can make them flame retardant. At present, among the flame retardants that have been developed, halogen flame retardants such a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K21/00C08K13/02C08L69/00C08L77/00C08L67/00C08L71/12C08L55/02
Inventor 孙培育刘拥华吴彤杨扬陈桥王惠吴刚
Owner TORAY FIBER RES INST(CHINA) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap