Epoxy polyurethane zinc phosphor antiseptic paint and preparation thereof

A technology of epoxy polyurethane and anti-corrosion paint, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as unsatisfactory weather resistance, achieve long-term anti-corrosion ability, fast drying speed, and corrosion-inhibiting effects

Inactive Publication Date: 2009-01-14
WUXI HUHUANG PAINT
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Alkyd coatings were mostly used earlier, and chlorosulfonated polyethylene coatings and chlorinated rubber coatings were popularized in recent years, but the weather resistance of these coatings is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A kind of epoxy polyurethane zinc phosphorus anticorrosion paint, comprises the component of following parts by weight:

[0050] Component A:

[0051] Aliphatic hexamethylene diisocyanate 12 parts

[0052] 8 parts of polybasic dibasic acid ester

[0053] Component B:

[0054] Bisphenol A type epoxy resin 30 parts

[0055] Tetrasalt chromate 8 parts

[0056] Zinc phosphate 15 parts

[0057] 30 parts of polybasic acid ester

[0058] Basic urethane copolymer 6 parts

[0059] Fluorinated silicone 3 parts

[0060] Polysiloxane polyether copolymer 6 parts

[0061] Flake talcum powder 15 parts

[0062] The production method is as follows:

[0063] Component A: Mix according to the formula ratio at 1200 rpm for 30 minutes.

[0064] Component B

[0065] 1. Add bisphenol A type epoxy resin in formula quantity, polybasic dibasic acid ester in formula quantity of 85%, basic urethane copolymer in formula quantity, fluorinated silicone in formula quantity and formula A l...

Embodiment 2

[0070] A kind of epoxy polyurethane zinc phosphorus anticorrosion paint, comprises the component of following parts by weight:

[0071] Component A:

[0072] Aliphatic biuret 10 parts

[0073] S100 aromatic solvent 5 parts

[0074] Component B:

[0075] Bisphenol A type epoxy resin 25 parts

[0076] Zinc yellow 6 parts

[0077] Aluminum phosphate 12 parts

[0078] S100 aromatic solvent 25 parts

[0079] 4 parts polycarboxylic acid containing amine derivative

[0080] Fluorinated silicone 2 parts

[0081] Polysiloxane polyether copolymer 5 parts

[0082] Barium sulfate 10 parts

[0083] The production method is as follows:

[0084] Component A: Mix according to the formula ratio at 1000 rpm for 20 minutes.

[0085] Component B

[0086] 1. Add bisphenol A type epoxy resin in formula quantity, S100 aromatic solvent in 85% formula quantity, polycarboxylic acid containing amine derivative in formula quantity, fluorinated silicone in formula quantity and poly Silicone pol...

Embodiment 3

[0091] A kind of epoxy polyurethane zinc phosphorus anticorrosion paint, comprises the component of following parts by weight:

[0092] Component A:

[0093] Aliphatic hexamethylene diisocyanate 15 parts

[0094] S150 aromatic solvent 10 parts

[0095] Component B:

[0096] Bisphenol A type epoxy resin 35 parts

[0097] Tetrasalt chromate 10 parts

[0098] Zinc phosphate 18 parts

[0099] S150 aromatic solvent 35 parts

[0100] Basic urethane copolymer 8 parts

[0101] Fluorinated silicone 4 parts

[0102] Polysiloxane polyether copolymer 7 parts

[0103] 20 parts flake talcum powder

[0104] The production method is as follows:

[0105] Component A: Mix according to the formula ratio at 1200 rpm for 25 minutes.

[0106] Component B

[0107] 1. Add bisphenol A type epoxy resin in formula quantity, S150 aromatic solvent in 85% formula quantity, basic urethane copolymer in formula quantity, fluorinated silicone in formula quantity and Polysiloxane polyether copolyme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact resistanceaaaaaaaaaa
Login to View More

Abstract

The invention provides an epoxy polyurethane zinc phosphorus anti-corrosive paint, the components of the anti-corrosive paint are as follows: a first component which comprises aliphatics solidifying agent and environmental protective solvent, a second component which comprises macromolecular epoxy resin, anti-corrosive pigment I, anti-corrosive painting II, the environmental protective solvent, dispersing agent, anti-foaming agent, leveling agent and filler. When the the first component and the second component are used, the mixed ratio of the weight of the first component and the second component is 1:5. The invention also discloses a preparation method of the epoxy polyurethane zinc phosphorus anti-corrosive paint. The epoxy polyurethane zinc phosphorus anti-corrosive paint has the advantages that the epoxy polyurethane zinc phosphorus anti-corrosive paint of the invention adopts macromolecular epoxy resin and adipose polyisocyanate reaction, the adhesive force of the paint film is good, the drying speed is quick, and the thermal-resistant temperature of the paint reaches over 150 DEG C, because the tetroxy chromate and xinc phosphate compound anti-corrosive high-efficient pigment are adopted, the anti-corrosive paint has the long-time anti-corrosive performance; the surface treatment of the backing material is not required strictly, the construction is convenient, and the environmental protective solvent can not cause pollution to the environment; the paint film has good acid resistance and alkali resistance and solvent resistance; the preparation method is simple, and the large-scale production is easy.

Description

technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to an epoxy polyurethane zinc phosphorus anticorrosion paint and a preparation method thereof. Background technique [0002] Material corrosion is the great enemy of human beings, and it brings huge economic losses to all countries in the world. Therefore, it will be of great significance to study high-performance and effective anti-corrosion materials. [0003] There are many kinds of anti-corrosion paints at home and abroad, mainly alkyd paints, chlorinated rubber paints and chlorosulfonated polyethylene paints. Alkyd coatings were used earlier, and chlorosulfonated polyethylene coatings and chlorinated rubber coatings were popularized in recent years, but the weather resistance of these coatings is not ideal. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide an epoxy polyurethane zinc phosphorus anti-corrosio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/02C09D5/08
Inventor 牛清平孙小清
Owner WUXI HUHUANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com