Waste Crumb rubber modified asphalt and preparation method thereof

A technology of waste rubber powder and modified asphalt, which is applied to building components, building insulation materials, buildings, etc., can solve the problems of difficult mixing operation, affecting the performance of modified asphalt, and poor dispersion, so as to save energy consumption and improve phase efficiency. Capacitive, high dispersion effect

Inactive Publication Date: 2009-09-23
CHINA RUBBER RESOURCE REGENERATION QINGDAO
View PDF3 Cites 49 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, judging from the research situation at home and abroad, there are the following problems in the production process of waste rubber powder modified asphalt: First, when waste rubber powder is added to asphalt to modify it, the viscosity of the system suddenly increases and the fluidity becomes poor , which makes the mixing operation difficult, and the dispersibility of the rubber powder in the asphalt is poor. Raising the stirring temperature can reduce the viscosity of the system, but both the rubber powder and the asphalt will hav

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waste Crumb rubber modified asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Use 100 parts by mass of base asphalt, 10 parts of 40-mesh waste rubber powder, and 3 parts of carboxylated nitrile rubber modifier. Mix evenly with an ordinary mixer at 150-170 ° C for about 15 minutes, and then use twin-screw extrusion Exit the machine for high-shear dispersion at a speed of 50 rad / min to obtain modified asphalt, and test the performance indicators of the modified asphalt. The results are shown in Table 2.

[0032] The equipment used is a twin-screw extruder with an aspect ratio of 50 and a diameter of 35 cm. From the feed inlet to the machine head, the temperature of the screw gradually increases and then decreases, and is between 150°C and 170°C.

Embodiment 2

[0034] Use 100 parts by mass of base asphalt, 15 parts of 80-mesh waste rubber powder, and 4 parts of ethylene-vinyl acetate copolymer modifier. Mix them uniformly with an ordinary mixer at 150-170 ° C for about 15 minutes, and then use The internal mixer is used for high-shear dispersion, and the mixing time is 5-10 minutes to obtain the modified asphalt, and the performance index of the modified asphalt is tested. The results are shown in Table 2, and then the aging performance is measured, and the results are shown in Table 3.

[0035] The technical parameters of the internal mixer used are: the capacity is 100 liters, the rotating speed is 80 rpm, and the temperature is controlled at 150-170°C.

Embodiment 3

[0037] Use 100 parts by mass of base asphalt, 20 parts of 120-mesh waste rubber powder, and 5 parts of modifier polyethylene. Mix evenly with an ordinary mixer at 150-170°C for about 15 minutes, and then use an internal mixer for high-shear Cut and disperse, and the mixing time is 5-10 minutes to obtain the modified asphalt, and test the performance index of the modified asphalt. The results are shown in Table 2.

[0038] The technical parameters of the internal mixer used are: the capacity is 100 liters, the rotating speed is 80 rpm, and the temperature is controlled at 150-170°C.

[0039] Table 2 Gained modified asphalt performance data of the present invention

[0040] Test indicators

unit

skills requirement ＊

Example 1

Example 2

Example 3

Penetration

0.1mm

40-60

58.9

57.6

58.7

5°C Ductility

cm

＞20

20.05

22.85

20.60

Softening Point

℃

＞60

60.2

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to waste crumb rubber modified asphalt and a preparation method thereof. The waste crumb rubber modified asphalt is prepared by high-shearing mixing of asphalt, a modifier and waste crumb rubber at a temperature of between 150 and 170 DEG C. The interface modifier is made to produce the highest efficacy and the compatibility between the waste crumb rubber and rubber is improved, so as to improve the high-low temperature performance and antiaging performance of the asphalt during use. At the same time, process simplification, cost reduction, waste recycling and environmental pollution reduction are realized.

Description

Technical field: [0001] The invention relates to a waste rubber powder modified asphalt and a preparation method thereof. Background technique: [0002] Petroleum asphalt has excellent plasticity and adhesion, and has a long history of being used as road paving materials. With the development of transportation, the traffic volume increases and the load capacity increases. The original asphalt pavement is easily damaged due to its small load capacity. Studies have found that the use of various polymers to modify asphalt can greatly improve the performance of asphalt pavement. Compared with ordinary asphalt, polymer-modified asphalt can greatly improve the high-temperature anti-flow and low-temperature anti-cracking ability, enhance the aging resistance and weather resistance, and enhance the adhesion ability to stone materials. The pavement paved with polymer modified asphalt can significantly improve the resistance to permanent deformation, temperature shrinkage cracking a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00B29B7/28B29C47/92C08L21/00C08L13/00C08L15/00C08L51/06C08L23/04B29C48/92
CPCB29C48/40B29C48/92B29C2948/9259B29C2948/92885
Inventor 张立群曹贵昌李晓林黄小溪刘毅毛立新伍社毛
Owner CHINA RUBBER RESOURCE REGENERATION QINGDAO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap