Master batch used for preparing high heat-resisting polypropylene plastic as well as preparation method and application thereof

A polypropylene plastic, high heat resistance technology, used in the field of plastic processing to achieve the effect of improving heat resistance

Inactive Publication Date: 2009-11-18
中山市瑞邦红利塑料工业有限公司
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, research specific gravity of about 1.1 (less than 1.2), heat distortion temperature of 130 ℃ or above polypropylene special materials and its price is significantly lower than the use of high-priced nucleating agent composition, is the market demand for polypropylene varieties, and No relevant reports have been seen so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 100 parts of polypropylene, 11-30 parts of flake filler, 1-3 parts of nano-filler and 0.1-0.3 parts of polypropylene nucleating agent;

[0026] Pre-mix 1 part of nano-calcium stearate and 11 parts of 600-mesh muscovite in a high-speed mixer for 10 minutes, and evenly sprinkle 0.1 part of 2,2'-methylenebis(4,6-di-tert-butylphenyl ) an acetone solution of sodium phosphate ester, wherein the solute mass fraction is 0.1%. Use intermittent stirring method, every 2 minutes of stirring, stop for a while, let the powder fall, repeat the above stirring process 5 times, make all the powder mix evenly, and dry it.

[0027] Put 30 parts of the dried powder and 100 parts of PP in a kneader, melt and mix them for 8 minutes at a temperature of 185° C. to prepare a masterbatch of high heat-resistant polypropylene plastic. After crushing the mixed masterbatch, take 10 parts of the masterbatch and 100 parts of polypropylene (mass) to melt and extrude to prepare a heat-resistant composit...

Embodiment 2

[0037] Pre-mix 3 parts of nano-sodium stearate and 13 parts of 1200-mesh sericite in a high-speed mixer for 8 minutes, and evenly sprinkle 0.3 parts of 2,2'-methylenebis(4,6-di-tert-butylphenyl ) acetone solution of aluminum phosphate ester, wherein the solute mass fraction is 0.1%. Use intermittent stirring method, every 2 minutes of stirring, stop for a while, let the powder fall, repeat the above stirring process 5 times, make all the powder mix evenly, and dry it.

[0038] Put 45 parts of the dried powder and 100 parts of PP in a kneader, melt and mix them for 6 minutes at a temperature of 180° C. to prepare a masterbatch of high heat-resistant polypropylene plastic. After crushing the kneading masterbatch, take 5 parts of the masterbatch and 100 parts of PP (mass) to melt and extrude to prepare a heat-resistant composite material. The temperature of each zone of the extruder is 185, 200, 210, 220, 210°C respectively.

[0039] After testing the special material, the foll...

Embodiment 3

[0048]Pre-stir 2 parts of nano-zinc carbonate and 11 parts of 600-mesh muscovite in a high-speed mixer for 8 minutes, and evenly sprinkle 0.2 parts of 2,2'-methylenebis(4,6-di-tert-butylphenyl)phosphoric acid Acetone solution of ester sodium salt, wherein the solute mass fraction is 0.1%. Use intermittent stirring method, every 2 minutes of stirring, stop for a while, let the powder fall, repeat the above stirring process 5 times, make all the powder mix evenly, and dry it.

[0049] 40 parts (mass) of dried powder and 100 parts of PP were melted and mixed for 8 minutes at a temperature of 185° C. in a mixer to prepare a masterbatch of high heat-resistant polypropylene plastic. After crushing the mixed masterbatch, take 10 parts and 50 parts (by mass) of the masterbatch and melt extrude them with PP to prepare heat-resistant composite materials. The temperature of each zone of the extruder is 185, 200, 210, 220, 210°C respectively.

[0050] After testing the special material,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a master batch used for preparing high heat-resisting polypropylene plastic as well as a preparation method and an application thereof. The master batch is prepared by polypropylene and pulverized fodder with the proportion by weight of 100:30-45; the pulverized fodder is prepared by the following components according to parts by weight of: 11-30 parts of laminal filter, 1-3 parts of nano filter and 0.1-0.3 parts of polypropylene nucleating agent; the laminal filter is white mica or sericite. The preparation method of the master batch used for preparing high heat-resisting polypropylene plastic comprises the following steps: mixing the laminal filter and the nano filter; dissolving the nucleating agent by acetone and then evenly spraying into the mixed filter; mixing evenly and drying; mixing the dried pulverized fodder with the polypropylene fusion to prepare the master batch used for preparing high heat-resisting polypropylene plastic. The application of the master batch used for preparing high heat-resisting polypropylene plastic is as follows: 5-10 parts by weight of master batch are shattered, and are then extruded with 50-100 parts of polypropylene fusion to prepare high heat-resisting polypropylene plastic. The invention improves the heat resistance of polypropylene by the synergy of each component, and has wide market prospect.

Description

technical field [0001] The invention relates to a masterbatch for preparing high heat-resistant polypropylene plastic, a preparation method and application thereof, and belongs to the technical field of plastic processing. Background technique [0002] Compared with polyethylene, polypropylene (PP) is a plastic variety with great potential for application and development among the existing polyolefin plastic materials. It is light in weight, high in tensile and bending strength and modulus, good in comprehensive performance, cheap and easy to obtain, and easy to process. After modification, it has now replaced engineering plastics in many applications. Therefore, it has become one of the largest and most widely used plastic varieties in the world today. [0003] With the expansion and deepening of market applications, the performance requirements for polypropylene are also getting higher and higher. Among them, the heat-resistant temperature of polypropylene is increased ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K3/34C08K5/098C08K5/523
Inventor 黄仁勇
Owner 中山市瑞邦红利塑料工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com