Soft hand feel coating and preparation method thereof

A hand-feeling and flexible technology, applied in the field of soft-feeling paint and its preparation, can solve the problems of lack of aesthetic feeling, high thermal conductivity, condensation of wall paint film, etc. Effect

Active Publication Date: 2010-01-06
GUANGDONG NATURAL COATING CHEM CO LTD
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing interior wall paint has a cold and stiff texture, lacks aesthetic feeling, and is not outstanding enough in function
In the low temperature season, the texture of the wall surface is cold, which makes people feel uncomfortable when touched, and the hand feel is not smooth enough; in the rainy season, due to the high ambient humidity, the wall paint film is prone to condensation, which cannot help adjust the indoor humidity
In addition, due to the dense internal structure of the existing wall paint film, the thermal conductivity is relatively large, and the speed of sound propagation in it is fast, so it cannot play the role of sound insulation and heat insulation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soft hand feel coating and preparation method thereof
  • Soft hand feel coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The soft touch coating consists of the following components by weight:

[0049] A. Expanded microsphere slurry 5-10,

[0050] B. Styrene-acrylic emulsion 15-30,

[0051] C. Auxiliary

[0052] Dispersant 0.3-0.5,

[0053] Wetting agent 0.1-0.3,

[0054] Coalescing aid 0.8-1.2,

[0055] Antifreeze 1.5-2.0,

[0056] Defoamer 0.2-0.3,

[0057] Thickener 0.3-0.5,

[0058] Antifungal agent 0.1-0.2,

[0059] Preservative 0.1-0.2,

[0060] D. Titanium dioxide 6-12,

[0061] E. Kaolin 8-15,

[0062]F. Heavy calcium 15-20,

[0063] G. Water 25-35.

[0064] Due to the low density of the expanded microspheres, it is not conducive to adding, and large dust is generated during the production process, which is not conducive to safe production. Therefore, it is necessary to pre-prepare the expanded microspheres into a slurry before adding them to the formula. The expanded microsphere slurry is composed of 10% to 15% by weight of expanded microspheres and 85 to 90% by weigh...

Embodiment 2

[0066] The soft touch coating consists of the following components by weight:

[0067] A. Expanded microsphere slurry 7-8,

[0068] B. Styrene-acrylic emulsion 16-18,

[0069] C. Auxiliary

[0070] Dispersant 0.35-0.45,

[0071] Wetting agent 0.15-0.25,

[0072] Coalescing agent 0.9-1.1,

[0073] Antifreeze 1.6-1.8,

[0074] Defoamer 0.23-0.28,

[0075] Thickener 0.35-0.45,

[0076] Antifungal agent 0.13-0.18,

[0077] Preservatives 0.13-0.17,

[0078] D. Titanium dioxide 8-10,

[0079] E. Kaolin 10-13,

[0080] F. Heavy calcium 16-19,

[0081] G. Water 28-33.

[0082] The expanded microsphere slurry is composed of 10% to 15% by weight of expanded microspheres and 85 to 90% by weight of water, and its preparation method is: in a closed container, the above 10% to 15% by weight of the expanded The microspheres are added into 85-90% by weight of water for stirring and mixing, and the expanded microsphere slurry is preformed.

[0083] Wherein, in above-mentioned emb...

Embodiment 3

[0104] The soft touch coating consists of the following components by weight:

[0105] A. Expanded Microsphere Slurry 6

[0106] B. Styrene-acrylic emulsion 23,

[0107] C. Auxiliary

[0108] GA40 (dispersant) 0.35,

[0109] CF10 (wetting agent) 0.1,

[0110] TEXONAL (coalescent aid) 1,

[0111] Ethylene glycol (antifreeze) 1.8,

[0112] CF245 (defoamer) 0.25,

[0113] QP15000 (thickener) 0.45,

[0114] M8 (mold inhibitor) 0.15,

[0115] LXE (preservative) 0.15,

[0116] D. Titanium dioxide 10.5,

[0117] E. Kaolin 9,

[0118] F. heavy calcium 18,

[0119] G. Water 29.25.

[0120] The expansion microsphere slurry is made up of the expansion microsphere of 15% by weight and the water of 85% by weight, and its preparation method is: in a closed container, the expansion microsphere of above-mentioned 15% by weight is added 85% by weight Stir and mix in water to pre-make the expanded microsphere slurry.

[0121]The preparation process of the invention includes the st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a soft hand feel coating which comprises expandable microsphere pulp, styrene-acrylate emulsion, dispersant, wetting agent, film-forming additive, anti-freezing agent, defoaming agent, thickener, anti-mildew agent, preservative, titanium dioxide, kaolin, triple(concentrated) superphosphate and water, wherein, the expandable microsphere pulp consists of 10%-15% of expandable microspheres and 85%-90% of water by weight percent. The process comprises the steps of pre-mixing, grinding, dispersing, adding the emulsion, adding the additives and adding the expandable microsphere pulp. The expandable microspheres added in the coating change the structure and the texture of the surface of a paint film and soften the touch; additionally, the expandable microspheres in the paint film improve the porosity of the paint film and reduce the spread-ability of heat and sound in the paint film, pores of the paint film can play the regulating role on water in the air, the water is absorbed when the humidity is high, and the water is released when the humidity is low.

Description

technical field [0001] The invention relates to the technical field of coatings for interior wall decoration and protection and their preparation, in particular to a soft hand-feeling coating with a smooth hand feel and texture like supple fabrics, capable of adjusting indoor humidity, sound insulation and heat insulation, and a preparation method thereof . Background technique [0002] In recent years, people's demand for interior wall coatings has become more and more personalized and functional. However, the existing interior wall coatings have a cold and stiff texture, lack aesthetic feeling, and are not prominent enough in functionality. In the low temperature season, the texture of the wall surface is cold, which makes people feel uncomfortable when touched, and the hand feel is not smooth enough; in the rainy season, due to the high ambient humidity, the wall paint film is prone to condensation, which cannot help adjust the indoor humidity . In addition, because th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D7/12C09D5/00
Inventor 刘薇薇王代民麦宗能张旭
Owner GUANGDONG NATURAL COATING CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com