Method for preparing fiber toughness SiO2 aerogel composite material in normal pressure drying condition

A technology of atmospheric drying and composite materials, applied in the direction of silicon dioxide and silicon oxide, which can solve the problems of excessive equipment conditions, achieve the effects of reducing production costs, mild reaction conditions, and broad application prospects

Inactive Publication Date: 2010-03-17
HARBIN INST OF TECH
View PDF3 Cites 57 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a method for preparing fiber tough SiO by normal pressure drying 2 Airgel composite method to solve supercritical drying method to prepare large-scale fiber-strong and tough SiO 2 Airgel has too high requirements on equipment conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing fiber toughness SiO2 aerogel composite material in normal pressure drying condition
  • Method for preparing fiber toughness SiO2 aerogel composite material in normal pressure drying condition

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0009] Specific implementation mode 1: In this implementation mode, dry under normal pressure to prepare fiber tough SiO 2 The method of airgel composite material is to carry out as follows: one, carry out hydrolysis reaction 48h after mixing ethyl orthosilicate, dehydrated alcohol, oxalic acid and water, wherein the mol ratio of ethyl orthosilicate and water is 1:1, the molar ratio of ethyl orthosilicate to absolute ethanol is 1:7, the molar ratio of ethyl orthosilicate to oxalic acid is 1:9×10 -4 2. Add water, N, N-dimethylformamide and ammonia water, inject the fiber mat until the fiber mat is submerged, and leave it for 24-48 hours to obtain a fiber mat-reinforced gel composite; 3. Step 2 The prepared fiber mat-reinforced gel composite is placed in a drying oven at 20-60°C for 2-6 hours, then placed in an aqueous solution of 80% ethanol by volume, and aged at 40-60°C for 12-24 hours. Then place it in a mixture of tetraethyl orthosilicate and ethanol with a volume ratio of...

specific Embodiment approach 2

[0011] Embodiment 2: The difference between this embodiment and the embodiment is that the fiber mat described in step 1 is short quartz fiber mat, continuous quartz fiber mat, high silica fiber mat or carbon fiber mat.

specific Embodiment approach 3

[0012] Embodiment 3: The difference between this embodiment and Embodiment 1 or 2 is that the drying temperature in Step 3 is 30-50°C. Other steps and parameters are the same as those in Embodiment 1 or Embodiment 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

A method for preparing fiber toughness SiO2 aerogel composite material in normal pressure drying condition relates to a preparation method of fiber toughness SiO2 aerogel composite material. The method solves the problem that a supercritical drying method for preparing large-size fiber toughness SiO2 aerogel has over-high requirements on device conditions. The preparation method of fiber toughnesscomposite material comprises the following steps: obtaining fiber toughness SiO2 aerogel composite material after sol-gel, ageing, solvent displacement, surface decoration, washing and drying processing. The method is characterized by low production cost, low requirements on device, good safety and the like. The fiber toughness SiO2 aerogel composite material prepared by the method can be made into flexible and rigid composite material according to the form and characteristics of a fiber prefabricated part, has complete block and low thermal conductivity, and is hydrophobing. The fiber toughness SiO2 aerogel composite material has wide application prospect in the heat preservation and insulation field.

Description

technical field [0001] The invention relates to a fiber tough SiO 2 Preparation method of airgel composite material. Background technique [0002] Existing fiber tough SiO 2 Airgel composite materials are prepared by supercritical drying method, the equipment system is complex and expensive, and it needs to work under high temperature and high pressure, which is highly dangerous. In addition, this method is useful in the preparation of large-scale fiber-strength SiO 2 In terms of airgel composite materials, the requirements for high temperature and high pressure equipment are more stringent, so the application is greatly restricted. Contents of the invention [0003] The invention provides a method for preparing fiber tough SiO by normal pressure drying 2 Airgel composite method to solve supercritical drying method to prepare large-scale fiber-strong and tough SiO 2 Airgel has a problem with high requirements on equipment conditions. [0004] Fabrication of fiber-str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/14
Inventor 贾德昌左军超段小明杨治华周玉
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap