Method for extracting proanthocyanidin from pine bark by taking water as solvent
A technology of proanthocyanidins and pine bark, applied in the direction of organic chemistry, etc., can solve the problems of poor product safety, high production cost, complicated extraction process, etc., and achieve the effects of less loss, no chemical residue, and high extraction efficiency.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] Weigh 100g of clean, decayed and moldy pine bark, crush it to 60 mesh, add 1000mL of distilled water, perform ultrasonic extraction for 30min under the conditions of ultrasonic power of 100W, frequency of 20KHz, and temperature of 50℃, repeat the extraction once, and combine The extract was centrifuged at 4000 rpm for 20 minutes to obtain a clear extract. The clarified extract was filtered with a 0.45μm microporous membrane to obtain a microfiltration permeate. The microfiltration permeate is ultrafiltered with a hollow fiber ultrafiltration membrane with a relative molecular weight of 100 000 Daltons. Under room temperature, the pressure of the reflux valve is adjusted to 0.1Mpa, and the ultrafiltration permeate is collected. The ultrafiltration permeate was concentrated with a roll nanofiltration membrane with a cut-off relative molecular mass of 200 Daltons. At room temperature, the control pressure of the reflux valve was adjusted to 1.6Mpa, and the...
Example Embodiment
[0023] Example 2
[0024] Weigh 10kg of clean, decayed and moldy pine bark, crush it to 40 mesh, add 100L of deionized water, under the conditions of ultrasonic power of 1000W, frequency of 40KHz, temperature of 45℃, ultrasonic extraction for 40min, repeat extraction once , Combine the two extracts, use a centrifuge for solid-liquid separation, remove solid impurities, and obtain a clear extract. The clarified extract is sent to the microfiltration device through the booster pump, and the 0.5μm tubular ceramic microporous filter membrane is used for microfiltration. The temperature of the material liquid is controlled at about 35°C. The control pressure of the reflux valve is adjusted to 0.6Mpa, and the microfiltration permeation is collected. liquid. The microfiltration permeate is sent to the ultrafiltration device through the booster pump, and the hollow fiber ultrafiltration membrane with the intercepted molecular weight of 100 000 Dalton is used for ultrafiltration. The tem...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap