Composite fiber fabric and method for manufacturing same

A synthetic fiber and fiber technology, applied in the direction of fabric, fabric surface trimming, heating/cooling fabric, etc., can solve the problem of not giving basic information such as the type and specification of textile fiber, and achieve the effect of high strength and easy recycling

Inactive Publication Date: 2010-06-16
丁晨妍
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, basic information such as types and specifications of these textile fibers are not given

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 95 parts of cowhide fiber and 3 parts of heat-shrinkable fiber that have been opened and pre-treated for anti-corrosion, mothproof, mildew, fatliquoring, fragrance and waterproof, and polyester fiber with nanocellulose fixed on the surface by chemical bond 1 After opening, mixing, carding, drawing, and twisting into yarn, the rapier weaving machine will form a smooth fabric. material.

[0022] The fabric material obtained by weaving is passed through a heat setting machine and treated at a high temperature of 150°C. The fabric material becomes denser due to thermal shrinkage, and the strength is also significantly improved.

Embodiment 2

[0024] 90 parts of pigskin fiber and 5 parts of heat-shrinkable fiber that have been opened and pre-treated for anti-corrosion, mothproof, mildew, antistatic, flame retardant and lubrication, and polyester fiber with nano cellulose fixed on the surface by chemical bond 2 parts, 0.75 parts of nylon fiber, 0.75 parts of polypropylene fiber, and 1.5 parts of viscose fiber are put into the opener, and are opened, mixed, carded into strips, drawn and twisted into yarn A.

[0025] 95 parts of pigskin fiber and 2 parts of heat-shrinkable fiber that have been opened and pre-treated for anticorrosion, mothproof, mildew, antistatic, flame retardant and lubrication, and polyester fiber with nanocellulose fixed on the surface by chemical bond 1 part, 0.75 part of nylon fiber, 0.75 part of polypropylene fiber, and 0.5 part of viscose fiber are put into the opener, after opening, mixing, carding into strips, drawing and twisting into yarn B.

[0026] The above-mentioned spun pigskin yarn A and p...

Embodiment 3

[0029] 50 parts of sheepskin fiber and 5 parts of heat-shrinkable fiber that have been opened and pre-treated for anti-corrosion, mothproof, mildew, antistatic, flame retardant and lubrication, and polyester fiber with nano cellulose fixed on the surface by chemical bond 2.5 1.5 parts of polyester fiber, 40.5 parts of nylon and 0.5 part of soybean fiber with nano-chitosan fixed on the surface with chemical bonds are put into the opener, and are opened, mixed, carded into strips, drawn and twisted into yarn A.

[0030] Put 75 parts of sheepskin fiber, 5 parts of heat-shrinkable fiber, and 20 parts of nylon that have been pre-treated with anticorrosion, mothproof, mildew, antistatic, flame retardant and lubrication into the opening machine. After opening, Blending, carding into sliver, drawing, twisting into yarn B.

[0031] 95 parts of sheepskin fiber and 3 parts of heat-shrinkable fiber that have been opened and pre-treated for anti-corrosion, mothproof, mildew, antistatic, flame r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite fiber fabric and a method for manufacturing the same and belongs to the technical field of textile industry. The method manly comprises: mixing hide fibers difficult to spin with other fibers and then spinning yarns with the mixed fibers; and weaving an extremely breathable and moisture-penetrable fabric with the yarns. Due to the contractibility of the blended high-contractibility fibers under a heating condition in post processing, the yarns and fabrics made of the mixed fibers containing the hide fibers have a compact structure and aqueous strength and can be used for cleaning cloth, basic cloth, filter cloth and the like.

Description

Technical field [0001] The invention relates to a fabric made of composite fibers and a method for preparing the same, in particular to a fabric composed of leather fibers and other fiber composites and a method for preparing the same. Background technique [0002] With the continuous improvement of people's living standards, leather products are used more and more widely, and the amount of use is increasing year by year. Every year in the process of manufacturing leather products, a large amount of scrap is generated. The number of various types of leather products discarded every year due to damage or outdated styles is also quite amazing. In particular, the recycling of waste leather shoes has been incinerated in the past. During this process, the Cr(III) in the leather will be oxidized to Cr(VI) carcinogens, causing great harm to human health. Therefore, the recycling and utilization of leather corner waste and waste leather products have also attracted people's attention. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D04B1/14D04B21/14D02G3/04D06C7/00B32B5/00D03D15/20D03D15/208D03D15/217D03D15/225D03D15/233D03D15/283D03D15/47D03D15/50
Inventor 丁晨妍
Owner 丁晨妍
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com