Preparation of carbon/carbon mould for hot-pressed sintering furnace
A hot-press sintering furnace and mold technology, which is applied in the field of hot-press sintering furnace molds, can solve the problems of isostatic graphite source and quantity instability, isostatic graphite is difficult to purchase, and service life is low, so as to achieve effective expansion The effect of using space, shortening the production cycle, and improving production efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0013] Example one:
[0014] 1. Using 6K carbon fiber as the reinforcing material, the preform is prepared by the weaving process;
[0015] 2. Put the preform on the graphite mold for chemical vapor deposition, the propylene flow rate is 3.0m 3 / h, deposition temperature 1100℃, deposition time 190 hours;
[0016] 3. Vacuum and pressure impregnation curing treatment: using furfurone resin as the impregnant, first preheat the furfurone resin, the preheating temperature is 55℃, and put the preform in step 1 into the impregnation tank, vacuum and preheat Heat, and then suck the resin into the impregnation tank, keep the pressure at 2.0MPa for 6 hours, fill the tank with nitrogen after the pressure is released, the pressure is 0.2MPa, return the impregnating liquid, and then proceed to curing operation, curing temperature 220 ℃ , Curing time 8 hours;
[0017] 4. Carbonization treatment: Put the solidified preform into a carbonization furnace, and carry out carbonization treatment under th...
Example Embodiment
[0021] Embodiment two:
[0022] 1. Use 12K carbon fiber as reinforcement material, and use weaving process to prepare preform;
[0023] 2. Put the preform on the graphite mold for chemical vapor deposition, the propylene flow rate is 2.0m 3 / h, deposition temperature is 1000℃, deposition time is 140 hours;
[0024] 3. Vacuum and pressure impregnation treatment: use asphalt as the impregnant, first melt the asphalt, heating temperature is 200 ℃, put the preform of step 1 into the impregnation tank, vacuum, preheat, and then put it into the impregnation tank Inhale the bitumen and keep the pressure at 2.5MPa for 6 hours. After releasing the pressure, fill the tank with nitrogen at a pressure of 0.3MPa and return the impregnating liquid. The product will be released when the furnace temperature drops below 150°C;
[0025] 4. Carbonization treatment: Put the bitumen-impregnated product into the carbonization furnace, and carry out carbonization treatment under the protection of high-purit...
Example Embodiment
[0029] Embodiment three:
[0030] 1. Using 6K carbon fiber as reinforcement material, the preform is prepared by acupuncture process;
[0031] 2. Put the preform on the graphite mold for chemical vapor deposition, the propylene flow rate is 2.5m 3 / h, deposition temperature is 1000℃, deposition time is 230 hours;
[0032] 3. Vacuum and pressure impregnation treatment: use asphalt as impregnant, first melt the asphalt, heating temperature is 200℃, and put the deposited product in step 1 into the impregnation tank, vacuum, preheat, and then impregnate Inhale bitumen into the tank, keep the pressure at 2.0MPa for 6 hours, fill the tank with nitrogen after releasing the pressure, the pressure is 0.3MPa, return the impregnation liquid, and the product will be released when the furnace temperature drops below 150℃;
[0033] 4. Carbonization treatment: Put the impregnated product into a carbonization furnace, and carry out carbonization treatment under the protection of high-purity nitrogen....
PUM
Property | Measurement | Unit |
---|---|---|
Hoop tensile strength | aaaaa | aaaaa |
Hoop tensile strength | aaaaa | aaaaa |
Hoop tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap