Cyanide leaching method for gold ores

A technology for cyanidation leaching and gold ore is applied in the field of cyanide leaching of refractory gold ore, which can solve problems such as difficulty in improving gold leaching effect, and achieve the effects of avoiding hidden dangers in operation safety, less investment and less environmental pollution.

Active Publication Date: 2010-07-28
BEIJING GENERAL RES INST OF MINING & METALLURGY
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method needs to go through flotation or classification before cyanide leaching after alkali leaching pretreatment, and it is difficult to improve the gold leaching effect for some refractory gold ore under normal temperature alkali pretreatment method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] For a refractory gold ore with a gold grade of 5.24g / t, the leaching rate obtained by direct application of the conventional cyanide leaching process is only 14.24%. After the ore is crushed and ground to -0.020mm, potassium permanganate and sodium hydroxide are added for heating and stirring pretreatment. The pretreatment conditions are: adding potassium permanganate 100kg / t -干矿 , sodium hydroxide 100kg / t -干矿 , the pulp concentration is 25%, the linear stirring speed is 5m / s, the heating temperature is 80°C, and the processing time is 8h. The gold leaching rate of 92.36% was obtained by applying the conventional cyanidation leaching process to the pretreated pulp after washing and filtering.

Embodiment 2

[0016] For a refractory gold ore with a gold grade of 9.06g / t, the leaching rate obtained by direct application of the conventional cyanide leaching process is only 17.73%. After the ore is crushed and ground to -0.003mm, potassium permanganate and sodium hydroxide are added for heating and stirring pretreatment. The pretreatment conditions are: adding potassium permanganate 30kg / t -干矿 , sodium hydroxide 200kg / t -干矿 , the pulp concentration is 15%, the linear stirring speed is 8m / s, the heating temperature is 60°C, and the processing time is 24h. After the pretreated pulp was washed and filtered, the conventional cyanidation leaching process was applied to obtain a gold leaching rate of 95.68%.

Embodiment 3

[0018] For a refractory gold ore with a gold grade of 3.92g / t, the leaching rate obtained by direct application of the conventional cyanide leaching process is only 8.84%. After the ore is crushed and ground to -0.008mm, potassium permanganate and sodium hydroxide are added for heating and stirring pretreatment. The pretreatment conditions are: adding potassium permanganate 150kg / t -干矿 , sodium hydroxide 50kg / t -干矿 , the pulp concentration is 55%, the linear stirring speed is 4m / s, the heating temperature is 90°C, and the processing time is 3h. After the pretreated pulp was washed and filtered, the conventional cyanidation leaching process was applied to obtain a gold leaching rate of 82.61%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a cyanide leaching method for gold ores, and relates to a cyanide leaching method for refractory gold ores. The method is characterized by comprising the following steps: firstly crashing ores, grinding, adding potassium permanganate and sodium hydroxide and carrying out the heating and stirring pretreatment, then washing and filtering the treated ore pulp, and carrying out the cyanide leaching process. The method has the advantages of simple flow, easy operation, low investment, low operation cost and less environmental pollution, and can greatly improve the cyanide leaching rate of the gold ores difficult to leach.

Description

technical field [0001] The invention relates to a cyanide leaching method of gold ore, which relates to a cyanide leaching method of refractory gold ore. Background technique [0002] The reserves of refractory gold ore account for 60% of the world's total gold reserves. With the depletion of easy-leachable gold ore resources, the recovery of gold from refractory gold ore is increasingly showing its importance. At present, one-third of the world's gold production More than one percent is from refractory gold deposits, and the proportion is still increasing. [0003] At present, the pretreatment methods for refractory gold ore mainly include roasting, pressurized oxidation, bacterial oxidation and chlorination. Among them, roasting and pressure oxidation have been widely used in industry at home and abroad. Roasting is a traditional and effective pretreatment method, but its treatment cost is high and it pollutes the environment seriously. Pressurized oxidation requires a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B11/08
Inventor 王福良魏明安贺政罗科华赵志强周东琴
Owner BEIJING GENERAL RES INST OF MINING & METALLURGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com