Composite material for recycling waste vehicle nylon products and preparation method thereof

A technology for composite materials and automobiles, which is applied in the field of composite materials and its preparation, can solve problems such as high energy consumption, difficult control of the production process, and complicated procedures, and achieve an easy-to-control effect

Inactive Publication Date: 2010-08-04
GUANGZHOU SUPER DRAGON ENG PLASTICS +1
View PDF6 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above method consumes a lot of energy, the production process is not easy to control, and the process is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] (1) Recycle 41.3g PA6M2800 (produced by Xinhui Meida, with a viscosity of 2.8), 40g PA6 material (melt index is 0.1, mainly containing glass fiber with a mass fraction of 30%), 0.1g nucleating agent polyadipyl Butylenediamine resin, 0.1g chain breaker M1420 (produced by Bruggemann, Germany), 0.1g antioxidant 1098, 0.2g antioxidant 168 and 0.2g ethylene bisstearamide at a high speed of 350 to 1300rpm Mix evenly to obtain a mixture;

[0057](2) Add the compound obtained in step (1) from the main feeding port of the twin-screw extruder, add 18g glass fiber 988A (Jushi Glass Fiber Factory) from the second feeding port of the twin-screw extruder, Mix evenly in the machine, and then extrude and cut into pellets to obtain composite materials. The processing conditions of the extruder are as follows: the rotation speed of the main engine is 250-500 rpm, the temperature of the barrel is 240-270°C, and the temperature of the water tank is 20-60°C; the speed of the pelletizer is ...

Embodiment 2

[0060] (1) 80g reclaimed PA6 material (melt index is 70, mainly containing the glass fiber that mass fraction is 15%), 0.2g nucleating agent polybutylene adipamide resin, 0.3g chain extender (Brugge, Germany Man company production), 1g ethylene-octene copolymer-maleic anhydride graft (Guangdong Bochen Polymer New Material Company), 0.1g antioxidant 1098, 0.2g antioxidant 168 and 0.2g ethylene bishard Fatty amide is mixed evenly at a high speed of 350-1300rpm to obtain a mixture;

[0061] (2) Add the mixture obtained in step (1) from the main feeding port of the twin-screw extruder, add 18g glass fiber (Great Wall Plastic Reinforcement Material Factory) from the second feeding port of the twin-screw extruder, Mix evenly in the machine, and then extrude and cut into pellets to obtain composite materials. The processing conditions of the extruder are as follows: the rotation speed of the main engine is 250-500 rpm, the temperature of the barrel is 240-270°C, and the temperature ...

Embodiment 3

[0064] (1) 41.2g PA66EPR27 (viscosity is 2.7, produced by Shenma Group Co., Ltd.), 40g PA66 recycled material (melt index is 0.1, mainly contains glass fiber with a mass fraction of 30%), 0.1g nucleating agent polyethylene glycol Diamide butanediamine resin, 0.2g chain breaker M1420 (produced by Bruggemann, Germany), 0.1g antioxidant 1098, 0.2g antioxidant 168 and 0.2g ethylene bis stearamide at a speed of 350~ 1300rpm high speed mixing evenly to get the mixture;

[0065] (2) Add the compound obtained in step (1) from the main feeding port of the twin-screw extruder, add 18g glass fiber 988A (Jushi Glass Fiber Factory) from the second feeding port of the twin-screw extruder, Mix evenly in the machine, and then extrude and cut into pellets to obtain composite materials. The processing conditions of the extruder are as follows: the rotation speed of the main engine is 250-500 rpm, the temperature of the barrel is 240-270°C, and the temperature of the water tank is 20-60°C; the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite material for recycling waste vehicle nylon products and a preparation method thereof. The composite material comprises the following components by weight percent: 0-85 percent of PA original material, 10-95 percent of recovered PA material, 5-40 percent of glass fiber, 0-2 percent of nucleating agent, 0-0.5 percent of chain extender, 0-5 percent of chain breaking agent, 0-30 percent of toughening agent, 0-2 percent of heat stabilizer and 0-1 percent of processing aid. The method comprises the following steps of: mixing the PA original material, the PA material, the nucleating agent, the chain extender, the chain breaking agent, the toughening agent, the heat stabilizer and the processing aid at high speed to obtain a mixed material; adding the mixed material from a main feeding port of a twin-screw extruder, adding the glass fiber from a second feeding port of the twin-screw extruder, and mixing the mixed material and the glass fiber in the twin-screw extruder; and extruding and pelletizing the mixture to obtain the composite material. The composite material for recycling nylon products is simple and convenient, is easy to control and can protect environment.

Description

technical field [0001] The invention relates to the technical field of chemical materials, in particular to a composite material for recycling waste automobile nylon parts and a preparation method thereof. Background technique [0002] Nylon (PA) is currently one of the most widely used engineering plastics in engineering plastics. Each car uses about 15 kg of PA materials, which are widely used in engine cooling fans and windshields, radiator water tanks, headlight lamp rings, and power steering tanks. , engine cover, rocker cover, intake manifold, shift module, brake release handle, mirror assembly and connector, etc., the above materials are all made of PA66 or PA6 with additives such as glass fiber and heat stabilizer. obtained composite material. As the number of scrapped cars increases year by year (the National Development and Reform Commission announced that the number of scrapped cars in my country in 2009 was about 2.7 million), the reasonable and efficient recycl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08K13/04C08K7/14B29B9/06B29C47/92B29C48/40B29C48/92
CPCB29C48/04B29C48/40
Inventor 郝源增王冲郝建鑫任萍
Owner GUANGZHOU SUPER DRAGON ENG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap