High temperature resistant thermosensitive paper

A warm and high-resistance technology, applied in temperature recording method, printing, duplication/marking method, etc., can solve the problem of thermal paper not being able to withstand high temperature, and achieve the effect of improving the finish, solving the problem of not being able to withstand high temperature and avoiding heat loss.

Active Publication Date: 2010-11-24
HENAN JIANGHE PAPER
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the shortcomings of the existing...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature resistant thermosensitive paper
  • High temperature resistant thermosensitive paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] (1) Pre-coating formula and production method of pre-coating:

[0018] 10Kg of styrene-butadiene latex, 30Kg of calcium carbonate, 30Kg of calcined earth, 20Kg of acrylic hollow sphere resin, 5Kg of lubricant, 5Kg of oxidized starch, are mixed into a coating solution with a solid content of 40-50% under high-speed stirring. Use a knife coater to coat on the thermal base paper, the coating amount is 7-9g / m 2 .

[0019] (2) The formula for the chromonic layer and the method of making the chromatic layer:

[0020] Component A: oxidizer: 4,4'-dihydroxydiphenylsulfone 10Kg, sensitizer: 2-naphthol benzyl ether 15Kg, adhesive: polyvinyl alcohol 5Kg, lubricant: zinc stearate 8Kg, calcined Soil 15Kg, mixed into a 30%-40% solid content mixed liquid under high-speed stirring, and ground to 2-5 micron particles in a bedroom sand mill.

[0021] B component: leuco dye: 2-(2-4-xylamino)-3-methyl-6-diethylaminofluoran (B-15) 45Kg, adhesive: polyvinyl alcohol 15Kg, anti- Oxidant: 6Kg of methy...

Embodiment 2

[0027] (1) Pre-coating formula and production method of pre-coating:

[0028] 10Kg of styrene-butadiene latex, 30Kg of calcium carbonate, 30Kg of calcined earth, 20Kg of acrylic hollow sphere resin, 5Kg of lubricant, 5Kg of oxidized starch, are mixed into a coating solution with a solid content of 40-50% under high-speed stirring. Use a knife coater to coat on the thermal base paper, the coating amount is 7-9g / m 2 .

[0029] (2) The formula for the chromonic layer and the method of making the chromatic layer:

[0030] Component A: oxidizer: 2,4'-dihydroxydiphenyl sulfone 15Kg, sensitizer: β-naphthol benzyl ether 12Kg, adhesive: acrylic latex 12Kg, lubricant: paraffin wax 8Kg, calcined clay 12Kg, Under high-speed stirring, it is mixed into a 30%-40% solid content mixed liquid, which is ground to 2-5 micron particles in a bedroom sand mill.

[0031] Component B: Leuco dye: 2-(2-4-xylamino)-3-methyl-6-diethylaminofluoran (B-15) 60Kg, adhesive: paraffin 6Kg, antioxidant: 2,6-Di-tert-but...

Embodiment 3

[0037] (1) Pre-coating formula and production method of pre-coating:

[0038] 10Kg of styrene-butadiene latex, 30Kg of calcium carbonate, 30Kg of calcined earth, 20Kg of acrylic hollow sphere resin, 5Kg of lubricant, 5Kg of oxidized starch, are mixed into a coating solution with a solid content of 40-50% under high-speed stirring. Use a knife coater to coat on the thermal base paper, the coating amount is 7-9g / m 2 .

[0039] (2) The formula for the chromonic layer and the method of making the chromatic layer:

[0040] Component A: oxidizer: 2,4'-dihydroxydiphenyl sulfone 10Kg, sensitizer: 2-naphthol benzyl ether 18Kg, adhesive: acrylic latex 15Kg, lubricant: paraffin 10Kg, calcined clay 10Kg, at high speed Under stirring, mix into 30%-40% solid content mixed liquid, and grind to 2-5 micron particles in bedroom sand mill.

[0041] Component B: Leuco dye: 2-(2-4-xylamino)-3-methyl-6-diethylaminofluoran (B-15) 30Kg, adhesive: paraffin 6Kg, antioxidant: 2,6-Di-tert-butyl-4 cresol 15Kg, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is high temperature resistant thermosensitive paper, a precoating is applied on the original thermosensitive paper; hollow ball resin is added in the precoating paint, a chromogenic layer is applied on the paper with the precoating; and a protective layer is applied on the paper with the chromogenic layer. The chromogenic layer comprises leuco dye, oxidant, sensitizer, lubricant, adhesive, filling calcining soil and anti-aging preparation. The protective layer is acrylamide and epichlorohydrin. In the novel thermosensitive paper process, color development occurs at 180 DEG C, and the bottom color occurs at 150 DEG C so as to solve the problem that common thermosensitive paper does not resist high temperature.

Description

Technical field [0001] The invention relates to a thermal paper, in particular to a high temperature resistant thermal paper. Background technique [0002] Thermal paper is widely used in logistics, labels, supermarket cooked food, etc. Some fields require thermal paper to have high temperature resistance, but currently domestically produced thermal paper has reached a high color density at 90 degrees Celsius, and Under the condition of 60 degrees Celsius, there is a background color. The barcode printed on thermal paper will show color at high temperature, resulting in illegible handwriting, and the barcode scanner cannot recognize the shortcomings, and it does not have the conditions for high temperature resistance. Summary of the invention [0003] The technical problem to be solved by the present invention is to overcome the shortcomings of the existing thermal paper that is not resistant to high temperature and provide a high temperature resistant thermal paper. [0004] To so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B41M5/42B41M5/30B41M5/337
Inventor 姜丰伟刘铸红曾云胡年喜
Owner HENAN JIANGHE PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap