Low-alloy steel resistant to carbon dioxide corrosion

A low-alloy steel, carbon dioxide technology, applied in earth-moving drilling, drilling equipment, drill pipes, etc., can solve the problems of poor corrosion resistance, oil field economic losses, easy failure, etc., and achieve simple manufacturing process, cost saving, and simple manufacturing process. Effect

Active Publication Date: 2010-12-29
BAOSHAN IRON & STEEL CO LTD
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, ordinary J55 carbon steel pipes used in these shallow wells are prone to failure due to poor corrosion resistance under the compound acidic corrosion environment conditions containing carbon dioxide and chloride ions, which will lead to economic losses in oil fields.
[0007] At present, there is no anti-CO 2 55ksi steel grade economical tubing and casing products with corrosion effect and relatively simple production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-alloy steel resistant to carbon dioxide corrosion
  • Low-alloy steel resistant to carbon dioxide corrosion
  • Low-alloy steel resistant to carbon dioxide corrosion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The characteristics of the present invention are described in more detail below through the examples.

[0025] Table 1 is the chemical composition of the steels of the examples and comparative examples of the present invention. Among them, A1-A6 are alloy steels of the present invention, and B1-B2 are comparative steel types, all of which are J55 steel pipes currently commonly used in oil fields.

[0026] Table 2 shows the mechanical properties and corrosion properties of the tested steels.

[0027] Table 1

[0028]

[0029] Table 2

[0030]

[0031] Note: The test condition is Na + +K + : 19673mg / L, HCO 3 - : 85.4mg / L, Cl - : 31700.8mg / L, SO 4 2- : 95.1mg / L, Ca 2+ : 1306.6mg / L, Mg 2+ : 210.2mg / L, PH=6.0, test temperature: 60℃, CO 2 Partial pressure: 1.5Mpa, flow rate: 1.0m / s.

[0032] It can be seen from the data in Table 2 that the steel of the present invention has certain carbon dioxide corrosion resistance. figure 1 It is the test surface morpho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a low-alloy steel resistant to carbon dioxide corrosion, which comprises the following chemical components in percentage by weight: 0.20-0.35% of C, 0.10-1.0% of Si, 0.20-1.5% of Mn, 0.5-1.5% of Cr, being more than or equal to 0.35% of Ni, being more than or equal to 0.35% of Cu, 0.01-0.10% of Al, and the balance of Fe and inevitable impurities, wherein the total content of impurity elements is lower than 0.05 wt%. In manufacturing process of the alloy steel, heat treatment is not carried out after smelting, continuous casting, hot rolling and air cooling. The strength of the oil well pipe prepared by the alloy steel is 55 ksi, thus the oil well pipe prepared by the alloy steel is suitable for shallow wells resistant to carbon dioxide corrosion.

Description

technical field [0001] The invention relates to a low-alloy steel, especially low-alloy steel for carbon dioxide corrosion-resistant 55ksi steel grade oil well pipes and a manufacturing method thereof. Background technique [0002] During the development of oil and gas fields, CO 2 Corrosion is a significant and long-standing problem. From the perspective of material corrosion protection, for high CO 2 , Chloride ions, produced water, iron ion content, low PH value, and strong corrosive environment formed by high pressure and fluid erosion in the well. To ensure safe and efficient production in the oil field, the use of expensive super 13Cr stainless steel pipes is the most effective way. However, most oilfields in my country are lean ore and low-permeability oilfields, and the production life is relatively short, mostly less than 10 years. At present, ordinary carbon steel pipes are still used in the oil field, which has caused many serious CO emissions in the oil field. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/42C22C38/40C22C38/20C22C38/18E21B17/00C21D8/10C22C33/04B22D11/00
Inventor 谭谆礼蔡海燕孙元宁
Owner BAOSHAN IRON & STEEL CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com