Co-Mo-RE high-strength heat resistant aluminum alloy material and preparation method thereof
An aluminum alloy material, co-mo-re technology, applied in the field of aluminum alloy materials of microalloying elements and rare earth elements and its preparation, can solve the problem of extensive melt treatment process, low product yield, waste material and slag recycling Poor usability and other issues
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0103] Example 1: Cu-1.0%, characteristic microalloying elements-Co, Mo, basic microalloying rare earth element-lanthanum La
[0104] (1) Weigh the required alloy elements according to the ingredient calculation table, as follows.
[0105]
[0106] (2) Add an appropriate amount of aluminum ingot to the melting furnace, heat it to melt completely and keep it at 700~800℃; in order to prevent the melt from inhaling too much air, the melting process should be as short as possible and in a closed environment carry out.
[0107] (3) Add Al-Mn, Al-Ti, Al-Co, Al-Mo, Al-Zr master alloy or mixed metal additives (including salt compounds) according to the formula ratio, and then add Cu pure metal and Al-Cd master alloy or mixed metal additives, then add B and rare earth element La, and stir evenly.
[0108] Mixed metal additives refer to cake or block non-sintered powder metallurgy products used for adding and adjusting alloy components, including manganese, copper, zirconium, cobalt, molybdenu...
Embodiment 2
[0114] Example 2: Cu-4.2%, characteristic microalloying elements-Co, Mo, basic microalloying rare earth elements La, Ce mixed rare earth
[0115] (1) Weigh the required alloy elements according to the ingredient calculation table, as follows.
[0116]
[0117] (2) Add an appropriate amount of aluminum ingot to the melting furnace, heat it to melt completely and keep it at 700~800℃; in order to prevent the melt from inhaling too much air, the melting process should be as short as possible and in a closed environment carry out.
[0118] (3) Add Al-Mn, Al-Ti, Al-Co, Al-Mo, Al-Zr master alloy or mixed metal additives (including salt compounds) according to the formula ratio, and then add Cu pure metal and Al-Cd master alloy or mixed metal additives, then add B and rare earth elements La and Ce mixed rare earths, and stir well.
[0119] Mixed metal additives refer to cake or block non-sintered powder metallurgy products used for adding and adjusting alloy components, including manganese, ...
Embodiment 3
[0125] Example 3: Cu-5.1%, characteristic microalloying elements-Co, Mo, basic microalloying rare earth element Eu
[0126] (1) Weigh various alloy elements required according to the following ingredients calculation table, as follows.
[0127]
[0128] (2) Add an appropriate amount of aluminum ingot to the melting furnace, heat it to melt completely and keep it at 700~800℃; in order to prevent the melt from inhaling too much air, the melting process should be as short as possible and in a closed environment carry out.
[0129] (3) Add Al-Mn, Al-Ti, Al-Co, Al-Mo, Al-Zr master alloy or mixed metal additives (including salt compounds) according to the formula ratio, and then add Cu pure metal and Al-Cd master alloy or mixed metal additives, then add B and rare earth element Eu, and stir evenly.
[0130] Mixed metal additives refer to cake or block non-sintered powder metallurgy products used for adding and adjusting alloy components, including manganese, copper, zirconium, cobalt, moly...
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com