Subnanometer enhanced and toughened transparent master batch and preparation method thereof

A reinforced and toughened, sub-nanometer technology, applied in the field of sub-nanometer reinforced and toughened transparent masterbatch and its preparation, can solve the problems of decreased light transmittance and transparency, and decreased mechanical properties, so as to achieve improved stiffness, improved mechanical properties, and improved Effect of screw speed

Inactive Publication Date: 2011-07-13
宁波益可达新材料有限公司
View PDF6 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a sub-nanometer reinforced toughened transparent masterbatch and its preparation method in view of the above-mentioned current state of the art, so as to solve the problem that the mechanical properties of the plastic film in the prior art decrease after using a common masterbatch, especially It is the problem of the decrease of light transmittance and transparency; while reducing the cost, it can improve the mechanical properties of film products, and at the same time achieve reinforcement and toughening, and can be used in the fields of food and medicine

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Raw materials are taken by weight: 70 kilograms of subnanometer precipitated barium sulfate with an average particle diameter of 100 nanometers, 2.3 kilograms of polyethylene wax, 2 kilograms of stearic acid, 0.3 kilograms of EBS, 0.3 kilograms of zinc stearate, 0.1 kilogram of 1010 antioxidant, Linear polyethylene LLDPE 25 kg.

[0053] Put the sub-nanometer precipitated barium sulfate into the high-speed mixer and heat it to 110°C, then add stearic acid coupling agent for three minutes, then add EBS, zinc stearate, 1010 antioxidant, and finally add polyethylene Wax and linear polyethylene LLDPE, after the current of the high-speed mixer suddenly increases, the material is discharged and cooled, and then crushed, added to a single-screw extruder to extrude at 140°C to 170°C, water-stretched strands are pelletized to obtain finished masterbatch products.

Embodiment 2

[0055] Weigh raw materials by weight: average particle size 200 nanometers subnanometer precipitated barium sulfate 75 kg, oxidized polyethylene wax 2 kg, aluminate 1.5 kg, modified EBS 0.5 kg, calcium stearate 0.5 kg, 1076 antioxidant 0.2 kg, low density polyethylene LDPE 20.3 kg.

[0056] Put the sub-nanometer precipitated barium sulfate into the high-speed mixer and heat it to 110°C, then add aluminate coupling agent for three minutes, then add modified EBS, calcium stearate, 1076 antioxidant, and finally add Oxidized polyethylene wax and low-density polyethylene LDPE, after the current of the high-speed mixer suddenly increases, the materials are discharged and cooled, and then crushed, put into a reciprocating extruder and extruded at 140°C to 170°C, water-stretched strands are pelletized to obtain the mother finished product.

Embodiment 3

[0058] Raw materials are taken by weight: 80 kg of sub-nanometer precipitated barium sulfate with an average particle size of 300 nanometers, 2 kg of EVA wax, 2 kg of titanate, 0.5 kg of oleic acid amide, 0.5 kg of barium stearate, 0.3 kg of 264 antioxidant, High-density polyethylene HDPE14.7 kg.

[0059] Put the sub-nanometer precipitated barium sulfate into the high-speed mixer and stir at high speed and heat it to 110°C, add titanate coupling agent for three minutes, then add oleic acid amide, barium stearate, 264 antioxidant, and finally add EVA wax and high-density polyethylene HDPE, after the current of the high-speed mixer suddenly increases, the material is cooled, then crushed, put into a twin-screw extruder and extruded at 110°C to 150°C, air-cooled and eagerly cut to obtain the finished masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a subnanometer enhanced and toughened transparent master batch and a preparation method thereof. The subnanometer enhanced and toughened transparent master batch comprises the following components in percentage by weight: 70-85 percent of subnanometer powder, 1-5 percent of dispersing agent, 0.3-1 percent of lubricating agent, 1-3 percent of coupling agent, 0.3-0.5 percent of thermal stabilizing agent, 0.1-0.5 percent of antioxidant and 10-25 percent of carrier resin. The preparation method comprises the following steps of: putting the subnanometer powder into a high speed mixer, selecting a high gear for stirring and heating, adding the coupling agent and treating for three minutes, then adding other raw materials, discharging and cooling after the raw materials are evenly stirred and mixed by the high speed mixer, then crushing, and extruding and pelleting through an extruding and pelleting device. The invention solves the problem that the mechanical performance of a plastic film is reduced after the common master batch is used in the prior art, in particular the problem that the light transmittance and the transparency are reduced; the mechanical performance of a film product is improved at the same time of reducing the cost; meanwhile, the invention achieves the purposes of enhancing and toughening and can be used in the fields of foods and medicines.

Description

technical field [0001] The invention relates to the field of inorganic powder modified high molecular polymers, in particular to a sub-nanometer reinforced toughened transparent masterbatch and a preparation method thereof. Background technique [0002] Plastic filled modified masterbatch has been put into the market since the early 1980s. Due to its low price and excellent product performance, it can improve some physical properties of plastic products and replace synthetic resins. The production process is simple and the investment is small. It has significant economic and social benefits. Therefore, plastic filling modified masterbatch is the fastest growing new industry in the plastics industry in recent years, and has become an important part of the plastics processing industry and one of the main additives for plastic products. [0003] my country has become the world's largest country in the production of plastic products, second only to the United States, with an an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K3/30C08K5/098C08J3/22
Inventor 李若沛刘学习
Owner 宁波益可达新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com