Water-based aluminized film composite glue and preparation method thereof

A technology of composite glue and aluminized film, applied in the direction of adhesive type, ester copolymer adhesive, etc., can solve the problems of low bonding strength, poor coating property, poor stability, etc., and achieve improved wetting Effects of leveling, cost reduction, and coating improvement

Active Publication Date: 2011-08-03
NANTONG GAOMENG NEW MATERIAL
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the general emulsion-type composite adhesives on the market are mainly water-based acrylic, including pure acrylic emulsion, styrene-acrylic emulsion, vineg

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based aluminized film composite glue and preparation method thereof
  • Water-based aluminized film composite glue and preparation method thereof
  • Water-based aluminized film composite glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This embodiment provides a kind of water-based aluminized film composite glue, which is used in the preparation of aluminized film composite paper. Ionized water is used as raw material, and the composite glue with a solid content of 40-50% is prepared after pre-emulsification, seed reaction, polymerization reaction and compounding.

[0020] The monomers in the above-mentioned composite rubber raw materials include hard monomers, soft monomers and functional monomers; wherein, the hard monomers adopt styrene (St) and vinyl acetate (VAc); the soft monomers adopt butyl acrylate ester (BA); the functional monomer is composed of any one of acrylic acid (AA) or methacrylic acid (MAA), any one of hydroxyethyl acrylate (HEA) or hydroxypropyl acrylate (HPA) and N - Methylolacrylamide (NMA) composition.

[0021] The amount of each raw material in the monomer is calculated by weight percentage: styrene 20-40%, vinyl acetate 10-30%, butyl acrylate 30-50%, acrylic acid or methacry...

Embodiment 2

[0035] This embodiment provides a kind of water-based aluminized film composite glue, which is used to prepare aluminized film composite paper. The water-based aluminized film composite glue takes various raw materials according to the following formula, including:

[0036]

[0037]

[0038] The preparation method comprises the following steps:

[0039](1) Pre-emulsification: put into the emulsification kettle the deionized water accounting for 50% of the total weight of deionized water, the alkyl ether ammonium sulfate accounting for 60% of the total weight of alkyl ether ammonium sulfate, and the alkylphenol polyoxyethylene ether accounting for Alkylphenol polyoxyethylene ether with a total weight of 80%, all sodium vinyl sulfonate, and all monomers are stirred and emulsified for more than 30 minutes to obtain a pre-emulsion;

[0040] (2) Seed reaction: drop into the polymerization reactor and account for 40% of the total weight of deionized water, deionized water, rem...

Embodiment 3

[0044] This embodiment provides a kind of water-based aluminized film composite glue, which is used to prepare aluminized film composite paper. The water-based aluminized film composite glue takes various raw materials according to the following formula, including:

[0045]

[0046] The preparation method comprises the following steps:

[0047] (1) Pre-emulsification: put 45wt% deionized water into the emulsification tank, alkyl ether ammonium sulfate accounting for 55wt% of the total weight of alkyl ether ammonium sulfate, and alkyl phenol polyoxyethylene ether accounting for 75wt% of the total weight Phenol polyoxyethylene ether, all sodium vinyl sulfonate, and all monomers, started stirring and emulsifying for more than 30 minutes to obtain a pre-emulsion;

[0048] (2) Seed reaction: put 45wt% deionized water, the remaining alkyl ether ammonium sulfate and the remaining alkylphenol polyoxyethylene ether, buffer into the polymerization reactor, start stirring and heat up,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses water-based aluminized film composite glue and a preparation method thereof, and belongs to the field of adhesive manufacture. The composite glue with 45 to 50 percent of solid content is prepared from monomers, composite emulsifier, initiator, buffering agent, pH regulator, water-based auxiliary agents and deionized water serving as raw materials by pre-emulsifying, seed reaction, polymerization reaction and compounding; the monomers comprise hard monomer, soft monomer and functional monomer, wherein the hard monomer consists of styrene and vinyl acetate; the soft monomer consists of butyl acrylate; and the functional monomer consists of any one of acrylic acid and methacrylic acid, any one of hydroxyethyl acrylate and hydroxypropyl acrylate, and N-hydroxymethyl acrylamide. The composite glue has good stability and low cost, and can improve the adhesive force and the peeling strength of an adhesive film on an adhesive base material. By adding various water-based aids with excellent performance, the foam of the composite glue in use is reduced, and the wetting leveling property of the emulsion on the surface of the aluminized film is improved so that the coating property of the glue is improved and the transparence is better after the film is formed.

Description

technical field [0001] The invention belongs to the field of adhesive manufacturing, and in particular relates to a novel water-based aluminized film composite adhesive and a preparation method thereof. Background technique [0002] Aluminized film composite paper has a very beautiful effect, and is now widely used in the packaging of various high-end toothpaste boxes, cosmetic boxes, jewelry boxes and cigarette boxes. It combines various aluminized films (or laser films) with cardboard or coated paper, and uses the bright appearance of the aluminized film (or laser film) to increase the aesthetic effect of the packaging box, improve the packaging grade, and attract consumers' attention , where the adhesive plays a very important role. [0003] At present, there are mainly two types of aluminized film composite adhesives: emulsion type and solvent type. Solvent type composite adhesives have environmental protection and safety problems due to the use of organic substances su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C08F220/18C08F218/08C08F212/08C08F220/06C08F220/28C08F220/58C08F2/24
Inventor 陈小锋沈峰邓煜东
Owner NANTONG GAOMENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap