Macromolecular polymer filling/sealing grouting material for underground engineering and construction technique thereof

A technology of polymer polymerization and grouting materials, which is applied in the field of safety and underground engineering safety, can solve the problems of short application time of grouting technology, etc., and achieve the effects of reducing labor intensity of workers, convenient underground transportation, and no flame spread

Inactive Publication Date: 2012-10-24
赵建军
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing grouting products and grouting technology have a short application time and are still in the development stage. Therefore, the development of advanced grouting products is an effective way to solve the safety problems of underground engineering

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0010] Embodiment 1: A polymer polymerization filling and sealing grouting material for underground engineering, the grouting material is composed of two low-viscosity liquids, resin and catalyst, wherein the components of the resin are: phenolic resin: 75 parts, hair Foam agent CFC141b: 18 parts, foam stabilizer SH-193: 5 parts, urea-formaldehyde resin: 20 parts; catalyst components are: 65% concentration of toluenesulfonic acid: 50 parts, polyethylene glycol: 20 parts , isopropyl ether: 35 parts, concentration is 85% phosphoric acid: 5 parts. The synthesis process of the resin is as follows: synthesize phenolic resin from phenol and formaldehyde, dehydrate under reduced pressure, add foaming agent CFC141b, foam stabilizer SH-193, urea-formaldehyde resin and stir in the reaction kettle for 3 hours. The synthesis process of the catalyst is as follows: adding 65% toluenesulfonic acid, polyethylene glycol, isopropyl ether, and 85% phosphoric acid into the reaction kettle accordi...

specific Embodiment approach 2

[0019] Specific embodiment two: a polymer polymerization filling and sealing grouting material for underground engineering, the grouting material is composed of two low-viscosity liquids, a resin and a catalyst, wherein the components of the resin are: phenolic resin: 75 parts, hair Foam agent CFC141b: 21 parts, foam stabilizer SH-193: 5 parts, urea-formaldehyde resin: 20 parts; catalyst components are: 65% concentration of toluenesulfonic acid: 50 parts, polyethylene glycol: 20 parts , isopropyl ether: 35 parts, concentration is 85% phosphoric acid: 6 parts. The synthesis process of the resin is as follows: synthesize phenolic resin from phenol and formaldehyde, dehydrate under reduced pressure, add foaming agent CFC141b, foam stabilizer SH-193, urea-formaldehyde resin and stir in the reaction kettle for 3 hours. The synthesis process of the catalyst is as follows: adding 65% toluenesulfonic acid, polyethylene glycol, isopropyl ether, and 85% phosphoric acid into the reaction...

specific Embodiment approach 3

[0028] Specific embodiment three: a polymer polymerization filling and sealing grouting material for underground engineering, the grouting material is composed of two low-viscosity liquids, resin and catalyst, wherein the components of the resin are: phenolic resin: 75 parts, hair Foam agent CFC141b: 25 parts, foam stabilizer SH-193: 5 parts, urea-formaldehyde resin: 20 parts; catalyst components are: 65% concentration of toluenesulfonic acid: 50 parts, polyethylene glycol: 20 parts , isopropyl ether: 35 parts, concentration is 85% phosphoric acid: 7 parts. The synthesis process of the resin is as follows: synthesize phenolic resin from phenol and formaldehyde, dehydrate under reduced pressure, add foaming agent CFC141b, foam stabilizer SH-193, urea-formaldehyde resin and stir in the reaction kettle for 3 hours. The synthesis process of the catalyst is as follows: adding 65% toluenesulfonic acid, polyethylene glycol, isopropyl ether, and 85% phosphoric acid into the reaction k...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a macromolecular polymer filling / sealing grouting material for underground engineering and a construction technique thereof. The macromolecular polymer filling / sealing grouting material for underground engineering is prepared from two low-viscosity liquid substances, including resin and catalyst, wherein the resin comprises 75 parts of phenolic resin, 18-25 parts of foaming agent CFC141b, 5 parts of foam stabilizer SH-193 and 20 parts of urea-formaldehyde resin; and the catalyst comprises 50 parts of 65% methylbenzenesulfonic acid, 20 parts of polyethylene glycol, 35 parts of isopropyl ether and 5-7 parts of 85% phosphoric acid. Since the grouting material provided by the invention is prepared from the two low-viscosity liquid substances, including resin and catalyst, the product has the advantage of low consumption for filling, is convenient for underground transportation, can implement hollow filling and tunnel / face fall filling, can form a sealing wall or fire wall within a set range, can quickly block off underground harmful gas, and can implement permanent sealing, thereby enhancing the safety level, work efficiency and economic benefit of undergroundengineering, such as coal mines, tunnels and the like.

Description

technical field [0001] The invention relates to the technical field of underground engineering safety, in particular to a grouting material for underground engineering, which is mainly used in coal mine underground safety engineering, and is also used in subway tunnels, submarine tunnels, railway tunnels, water conservancy and hydropower projects, dams, etc. security area. Background technique [0002] In underground engineering disasters such as coal mines and tunnels, the problems of stratum conditions, water gushing, gas and underground fire fighting have always been hidden dangers and problems that people take seriously and need to be solved urgently. At present, coal mine safety accidents still account for a high proportion of all kinds of safety accidents. Coal mine disasters such as: roof fall, partial side, flood, fire, gas outburst, explosion and other treatment measures and preventive measures urgently need to be improved. Traditional coal and rock mass reinforcem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/10C08L61/24C08L71/08C08K5/42C08K3/32C08K5/06C08J9/14E21D11/38E02B3/16
Inventor 赵建军封常升杜志福
Owner 赵建军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com