Silver-zinc zirconium phosphate composite germicide for paper money and preparation method thereof
A technology of compound antibacterial agent and zirconium phosphate, applied in the direction of adding inorganic compounds, paper, etc., to achieve the effect of no environmental pollution, high resistance to discoloration, and simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0018] Example 1
[0019] Prepare 300ml silver ammonia solution, weigh a certain quality of silver nitrate according to the initial silver content of 1.8wt%, dissolve it in deionized water and stir, add ammonia during the stirring process, wait until the aqueous solution changes from clear to turbid, and then clear again, that is Obtain silver ammonia solution; Disperse 30g zirconium phosphate powder (average particle size of 7μm) in the prepared silver ammonia solution, add zinc nitrate to the above solution according to the initial zinc content of 2wt%, stir at constant temperature for 2h, and filter After washing and drying at 90℃ for 4h, it is placed in an alumina crucible, placed in a muffle furnace, baked at 1000℃ for 2h, and naturally cooled to room temperature to obtain an inorganic antibacterial powder of silver and zinc supported by zirconium phosphate. The loading rate of zinc is 90% and 85%, the average particle size is less than 9μm, and the whiteness is 84.
Example Embodiment
[0020] Example 2
[0021] Prepare 300ml silver nitrate aqueous solution, weigh a certain mass of silver nitrate according to the initial silver content of 1.8wt%, dissolve it in deionized water and stir until it is completely dissolved to obtain silver nitrate aqueous solution; add 30g zirconium phosphate powder (average particle size of 7μm) 1) Disperse in the prepared silver nitrate aqueous solution, add zinc sulfate to the above solution according to the initial zinc content of 3wt%, stir at constant temperature for 5h, filter, wash, and dry at 120°C for 2h, then place it in an alumina crucible, In a muffle furnace, calcined at 1000°C for 2 hours and naturally cooled to room temperature to obtain an inorganic antibacterial powder of silver and zinc supported by zirconium phosphate. The loading rates of silver and zinc are 85% and 80%, respectively, and the average particle size is less than 9μm. The whiteness is 80.
Example Embodiment
[0022] Example 3
[0023] Prepare 300ml of silver complex aqueous solution formed by silver nitrate and monoethanolamine, weigh a certain mass of silver nitrate according to the initial silver content of 1.8wt%, dissolve it in deionized water and stir, add monoethanolamine during the stirring process, and wait until the aqueous solution is changed from The clarification becomes turbid, and then becomes clarified, that is, the silver complex aqueous solution formed by silver nitrate and monoethanolamine is obtained; 30g of zirconium phosphate powder (average particle size is 7μm) is dispersed in the silver formed by silver nitrate and monoethanolamine In the complex aqueous solution, zinc chloride was added to the above solution according to the initial zinc content of 4wt%, stirred at constant temperature for 4 hours, filtered, washed, and dried at 100°C for 3 hours, then placed in an alumina crucible and placed in a muffle furnace In the medium, calcined at 1000 ℃ for 2 hours, a...
PUM
Property | Measurement | Unit |
---|---|---|
Average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap