A nano-calcium sulfate and preparation process technology, applied in the field of preparation of nano-calcium sulfate, can solve the problems of low added value, incapable of industrial production, and high cost, and achieve the effect of reducing the preparation cost and reducing the preparation cost

Inactive Publication Date: 2011-11-09
陈胜明
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The main problem of using ferrous sulfate to prepare iron oxide series pigments is that a large amount of industrial alkali is used to neutralize the acid in the process, and the ammonium sulfate formed is difficult to recycle and has low added v

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Preparation raw materials: the concentration of the ammonium sulfate solution from the iron oxide pigment preparation process is 25%; the industrial lime calcium oxide, the calcium oxide content is greater than 95%.

[0032] 1. Take 210 kg of calcium oxide, add 80°C hot water, and prepare 1333 kg of calcium hydroxide emulsion with a calcium oxide content of 15%.

[0033] 2. Filter with a 200 mesh screen to separate the coarse particles of impurities in the calcium hydroxide emulsion to obtain a refined calcium hydroxide emulsion.

[0034] 3. Take 3% of the amount of calcium oxide and mix the sodium stearate and calcium oxide slurry to obtain a mixed slurry system containing the variable resistance agent.

[0035] 4. Take 1886 kilograms of ammonium sulfate solution with a concentration of 25%, add it to the calcium hydroxide slurry containing the resistance variable agent, and stir for 2 hours at room temperature. After the reaction is completed, nano calcium sulfate slurry and d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a process for preparing nano calcium sulfate by adopting lime and ammonium sulfate as raw materials. The preparation process comprises the following steps of: emulsification of lime calcium oxide; generation of nano calcium sulfate slurry by reacting a calcium hydroxide emulsion containing a change-inhibiting agent with an ammonium sulfate solution; filtering and washing; drying; and the like. The process is suitable for ammonium sulfate solution reclamation and ammonia recycling treatment in a process of producing ferric oxide series pigments by adopting ferrous sulfate as a raw material, and is a critical core technology of the process of preparing the ferric oxide series pigments by using the ferrous sulfate as the raw material. The change-inhibiting agent is introduced in the preparation process, superfine nano calcium sulfate particles formed by the ammonium sulfate and the calcium hydroxide are prevented from growing up in a liquid-phase environment, so that industrial production of a superfine nano calcium sulfate product by adopting a chemical method becomes a possibility.

Description

Technical field: [0001] The invention relates to the field of chemical industry, in particular to a technology for preparing nano calcium sulfate by using lime and ammonium sulfate as raw materials. The inventive technology is specially developed for the recycling of ammonium sulfate discharged from the process of preparing iron oxide pigments by using ferrous sulfate. technical background: [0002] The main problem of using ferrous sulfate to prepare iron oxide series pigments is that a large amount of industrial alkali is used to neutralize the acid in the process, and the ammonium sulfate formed is difficult to recycle and has low added value, which makes the production cost high and cannot be industrialized. [0003] Ammonium sulfate and lime are used to react the ammonia in the recovery system to realize the recycling of ammonia, and the gypsum calcium sulfate formed has little use value. [0004] Create a new ammonium sulfate recycling process technology, and realize ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01F11/46B82B3/00
Inventor 陈胜明
Owner 陈胜明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap