Nano-zinc compound anion environmentally-friendly latex paint and preparation method thereof

An environmentally friendly latex and compound technology, used in latex paints, biocide-containing paints, antifouling/underwater coatings, etc., can solve the problems of large pH value, inability to achieve industrialization, and unenvironmental protection, to eliminate toxic and harmful Substances and odors, improving people's living environment, and purifying indoor air

Inactive Publication Date: 2012-12-26
黑龙江省玉琦装饰涂料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the relatively high solubility of zinc oxide in water, it has high selectivity to dispersants, thickeners and pigments and fillers. It is greatly affected by the pH value and the stability of the coating is poor, which also limits its promotion in coatings.
Existing commercially available coating products are generally not environmentally friendly, cannot effectively eliminate toxic and harmful substances and odors; cannot realize industrialization, and have poor negative ion release, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-zinc compound anion environmentally-friendly latex paint and preparation method thereof
  • Nano-zinc compound anion environmentally-friendly latex paint and preparation method thereof
  • Nano-zinc compound anion environmentally-friendly latex paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0018] Specific embodiment one: the nano-zinc compound negative ion environment-friendly latex paint of this embodiment is made of 20~100kg of deionized water, 1~8kg of hydroxyethyl cellulose, 1~8kg of dispersant, 1~6kg of wetting agent, 1 ~4kg antifungal agent, 1~4kg fungicide, 1~8kg pH regulator, 1~6kg defoamer, 5~20kg antifreeze, 80~250kg titanium dioxide, 30~60kg environmental protection function Materials Anion element, 100-400kg nano-zinc compound, 1-6kg rheology modifier, 48-100kg kaolin, 50-100kg heavy calcium powder, 5-20kg film-forming aid, 1-4kg Whitening agent, 150-350kg of acrylic resin and 2-8kg of alkali-swellable thickener; wherein the nano-zinc compound is mixed with nano-zinc oxide and zinc sulfide in a volume ratio of 1:1; the particle size of the nano-zinc compound is 10~30nm; antifreeze is propylene glycol.

[0019] Hydroxyethyl cellulose used in this embodiment: purchased from Germany. Klein anthracene, the model is EM30-M;

[0020] Dispersant: purchase...

specific Embodiment approach 2

[0036] Specific embodiment two: what this embodiment is different from specific embodiment one is that nano-zinc compound anion environmental protection latex paint is made of 20kg deionized water, 1kg hydroxyethyl cellulose, 1kg dispersant, 1kg wetting agent, 1kg 1kg antifungal agent, 1kg fungicide, 1kg pH regulator, 1kg defoamer, 5kg antifreeze, 80g titanium dioxide, 30kg environmental functional material negative ion element, 100kg nano zinc compound, 1kg rheology modifier, 48kg of kaolin, 50kg of heavy calcium powder, 5kg of film-forming aids, 1kg of whitening agent, 150kg of acrylic resin and 2kg of alkali-swellable thickener. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0037]Specific embodiment three: what this embodiment is different from specific embodiment one is that nano-zinc compound anion environmental protection latex paint is made of 100kg deionized water, 8kg hydroxyethyl cellulose, 8kg dispersant, 6kg wetting agent, 4kg Antifungal agent of 4kg, bactericide of 4kg, pH regulator of 8kg, defoamer of 6kg, antifreeze of 20kg, titanium dioxide of 250kg, negative ion element of 60kg of environmental protection functional material, nanometer zinc compound of 400kg, rheology of 6kg Modifier, 100kg of kaolin, 100kg of heavy calcium powder, 20kg of coalescent, 4kg of whitening agent, 350kg of acrylic resin and 8kg of alkali swelling thickener. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a nano-zinc compound anion environmentally-friendly latex paint and a preparation method thereof. The preparation method comprises: (1) weighing raw materials; (2) mixing and stirring deionized water, a dispersant, a wetting agent, a mildew preventive, a bactericide and an antifreeze, then adding titanium dioxide and an environmentally-friendly negative ion functional material, stirring, adding kaolin, heavy calcium carbonate powder and nano-zinc compounds, continuing stirring, adding a rheology modifier and a whitening agent and continuing stirring; (3) adding a defoamer and hydroxyethyl cellulose, mixing and stirring, then adding a film-forming aid, grinding and standing to obtain slurry; and (4) adding acrylic resins, stirring, then adding a pH regulating agent and a base swelling thickener and continuing stirring. The product provided by the invention has the advantages of strong hiding capability, convenience in construction, no toxicity and odor, no environmental pollution, and bactericidal and mildew-proof effects; and the wall paint can sustainably release negative ions, effectively eliminate the toxic and hazardous substances and odor and achieve industrialization, and has scrubbing resistance and high release amount of negative oxygen ions.

Description

technical field [0001] The invention relates to a latex paint and a preparation method thereof. Background technique [0002] Environmentally friendly architectural decorative coatings are a high-tech industry that has been booming in China in the past ten years. With the needs of the construction industry and architectural decoration, latex paints are widely used on the surface of walls, some for exterior walls, and some for interior. For walls, the environmental protection requirements for interior walls are usually higher than those for exterior walls. Because the indoor ventilation is lower than that of the outdoors, people put forward low-toxicity requirements indoors. The most basic requirement is that the latex paint should not volatilize directly toxic substances to humans or animals, or have a low volatile value. Therefore, a large number of latex paints are currently required to be environmentally friendly. type latex paint. [0003] The preparation of environmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D5/02C09D5/14C09D7/12
Inventor 安洋苗卿华王秉刚安玉奇安冬
Owner 黑龙江省玉琦装饰涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products