An anti-corrosion coating and impact-resistant technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as peeling, delamination, cracking and peeling, and achieve excellent resistance to medium penetration, good adhesion, and cost. low effect
Inactive Publication Date: 2011-12-14
陕西北方汇风能源科技有限公司
View PDF5 Cites 24 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The fillers in the paint are scientifically designed and selected, and the impact resistance of the paint layer is improved by adding fillers such as carbon fiber and glass fiber reinforced chopped strand mat. The disadvantage of poor adhesion strength improves the adhesion and corrosion resistance of the coating. Compared with the traditional vinyl ester resin glass flake coating, the impact resistance and adhesion index of the coating are greatly improved. , Small boiler flue gas wet desulfurization and dust removal integrated comprehensive equipment anti-corrosion requirements, and solve the vibration of the equipment in hoisting, transportation and operation caused by the traditional vinyl ester resin glass flake coating to form coating peeling, delamination, cracking and Physical corrosion damage such as detachment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] The specific composition and weight of an impact-resistant and anti-corrosion coating for a medium and small boiler flue gas wet desulfurization and dust removal integrated comprehensive equipment:
[0023] Impact-resistant anti-corrosion coating (primer) for flue gas wet desulfurization and dust removal integrated equipment
[0024]
[0025] Impact-resistant anti-corrosion coating (intermediate coating) for flue gas wet desulfurization and dust removal integrated equipment
[0026]
[0027] Impact-resistant anti-corrosion coating (surface coating) for flue gas wet desulfurization and dust removal integrated equipment
[0028]
Embodiment 2
[0030] The specific composition and weight of an impact-resistant anti-corrosion coating for integrated equipment for wet desulfurization and dust removal of medium and small boiler flue gas:
[0031] Impact-resistant anti-corrosion coating (primer) for flue gas wet desulfurization and dust removal integrated equipment
[0032]
[0033] Impact-resistant anti-corrosion coating (intermediate coating) for flue gas wet desulfurization and dust removal integrated equipment
[0034]
[0035] Impact-resistant anti-corrosion coating (surface coating) for flue gas wet desulfurization and dust removal integrated equipment
[0036]
[0037] The preparation of this coating is carried out according to the general preparation process, and its preparation process is as follows:
[0038] The preparation of impact-resistant anti-corrosion coating (primer) for flue gas wet desulfurization and dust removal integrated equipment: firstly, the vinyl resin, filler and solvent are prepared ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
surface roughness
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a special impact-resistant anti-corrosion coating, especially for the anti-corrosion of medium and small boiler flue gas wet desulfurization and dust removal integrated equipment, boilers, container tanks and other equipment, which can well solve the problems of anti-corrosion equipment. Physical corrosion damage such as peeling, delamination, cracking and falling off of the coating formed by the vinyl ester resin glass flake coating caused by tremors during hoisting, transportation and operation. The coating components are composed of: phenolic vinyl ester resin, additives, pigments, curing agents, accelerators, fillers, thixotropic agents, glass flakes, and solvents. The mass percentage range is: phenolic vinyl ester resin 20- 80%, auxiliary agent 2-5%, pigment 2-6%, curing agent 0.5-10%, accelerator 0.25-12%, thixotropic agent 0.5-5%, glass flake 0-45%, solvent 0-5% , the remaining fillers. Especially in the design and selection of fillers, carbon fiber, glass fiber reinforced chopped strand mat and other fillers are used to maximize the impact resistance of the coating. The coating of the present invention has good resistance to medium penetration, acid resistance, impact resistance, alkali resistance, wear resistance, small shrinkage rate when hardened, small thermal expansion coefficient, good adhesion to the substrate, and resistance to sudden temperature changes. Good, it can work at 185°C for a long time, and the maximum temperature can reach 235°C instantaneously, and it is convenient for construction, easy to repair, and low in cost.
Description
technical field [0001] The invention relates to an impact-resistant anti-corrosion coating, especially for the anti-corrosion of medium and small boiler flue gas wet desulfurization and dust removal integrated equipment, boilers, container tanks and other equipment, which can well solve the problem of hoisting anti-corrosion equipment Physical corrosion damage such as peeling, delamination, cracking and falling off of the coating formed by the phenolic vinyl ester resin glass flake coating caused by tremors during transportation and operation. Background technique [0002] At present, the wet flue gas desulfurization system has strict requirements on materials such as corrosion resistance, wear resistance, temperature resistance, and impermeability. Nowadays, flue gas desulfurization devices often use nickel-based alloys or carbon steel inner-coated titanium plates, which all exist It is prone to pitting corrosion, crevice corrosion, electrochemical corrosion, etc., destroyi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.