Transfer printing ink for polypropylene plastics, and preparation method and application thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of polypropylene and chlorinated polypropylene, applied in the direction of ink, application, printing, etc., can solve the problem that pad printing ink cannot be pad printed, and achieve fast drying speed, strong three-dimensional effect and good effect
Active Publication Date: 2012-04-11
CHINA PAINT MFG CO SHENZHEN
View PDF1 Cites 20 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The object of the present invention is to provide a kind of connecting material is chlorinated polypropylene resin and its preparation method a
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0043] Chlorinated polypropylene resin 15KG
[0044] Thermoplastic acrylic resin 15KG
[0045] Polyketone resin 5KG
[0046] Micro powder wax 1.5KG
[0047] Cobalt naphthenate 0.05KG
[0048] Chlorinated Polyolefin 8.5KG
[0049] Titanium dioxide 32KG
[0050] Cyclohexanone 12KG
[0051] Dibasic acid ester 5KG
[0052] Ethylene glycol butyl ether 5.75KG
[0053] Polycarboxylic acid polymer 0.2KG
[0054] Dissolve chlorinated polypropylene resin, thermoplastic acrylic resin and polyketone resin in cyclohexanone, bivalent ester and ethylene glycol butyl ether, then add fine powder wax, cobalt naphthenate and chlorinated polyolefin in sequence , titanium dioxide and polycarboxylic acid polymer are stirred to make them fully wet, and after mixing evenly, they are ground on a three-roller machine until the fineness is qualified, and then the po...
Embodiment 2
[0056] Chlorinated polypropylene resin 20KG
[0057] Thermoplastic acrylic resin 20KG
[0058] Polyketone resin 7KG
[0059] Micro powder wax 1.5KG
[0060] Cobalt naphthenate 0.05KG
[0061] Chlorinated Polyolefin 8.5KG
[0062] Carbon black 7.5KG
[0063] Cyclohexanone 20KG
[0064]Dibasic acid ester 10KG
[0065] Ethylene glycol butyl ether 4.65KG
[0066] Polycarboxylic acid polymer 0.8KG
[0067] Its preparation method is the same as that of Example 1, and the performance of printed matter is as described in Table 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a transfer printing ink for polypropylene plastics, and a preparation method and application thereof. The transfer printing ink for polypropylene plastics is composed of the following components: 15-35% chlorinated polypropylene resin, 20-30% thermoplastic acrylic resin, 5-15% polyketone resin, 1-2% stuffing, 4-20% pigment, 5-10% auxiliaries, and 20-40% solvent. The transfer printing ink is high in drying speed and stable, high in color concentration and stable in colloid properties; the transfer printing ink has good effects if being applied to direct transfer printing on the surface of the polypropylene plastics without pre-treatment; besides, the transfer printing ink is good in continuous printability, free of wire drawing, convenient for cleaning, clear in printed patterns, good in third dimension and excellent in adhesion.
Description
technical field [0001] The invention relates to a transfer ink, in particular to a pad printing ink for polypropylene plastic and its preparation method and application. Background technique [0002] At present, it is not possible to directly pad-print on polypropylene plastic in China. The reason is that polypropylene has high stereoregularity, is easy to crystallize, and has low surface polarity. It uses general ink for pad printing, and its adhesion is extremely poor. Therefore, it is usually necessary to use complex acid mixed solution etching, surface corona or flame treatment, and plasma treatment before pad printing. These pretreatments require large-scale machinery and equipment, and the treatment methods are unsafe and pollute the environment. [0003] Therefore, the existing technology needs further development. Contents of the invention [0004] The object of the present invention is to provide a kind of connecting material is chlorinated polypropylene resin an...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more