Electric locomotive pantograph carbon slide plate

A pantograph carbon sliding plate, electric locomotive technology, applied in the fields of subway, urban rail transit, mining locomotive, can solve the problem of high wear and tear of catenary wires, achieve long service life, prolong the repair period, and reduce the bonding resistance.

Active Publication Date: 2012-05-02
河北翔九石墨股份有限公司
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Metal-impregnated carbon skateboard is made of carbon skateboard impregnated with copper alloy under hot isostatic pressing. It has g...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric locomotive pantograph carbon slide plate
  • Electric locomotive pantograph carbon slide plate
  • Electric locomotive pantograph carbon slide plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1: Electric locomotive pantograph carbon slide plate, made of the following raw materials in parts by weight: 5.3 parts of semi-reinforcing carbon black, 2.5 parts of -398 flake graphite, 1.8 parts of 599 flake graphite, 1 part of charcoal powder and melted coal 5.6 parts of asphalt.

[0027] The process steps of the preparation method are: (1) Thermal mixing: Add semi-reinforcing carbon black, -398 flake graphite, 599 flake graphite and charcoal powder in the above raw materials into a 500 liter kneader according to the weight ratio for thermal mixing, and heat Mix for 50-60 minutes, when the temperature is higher than 130°C, add melted coal tar pitch, then heat mix for 2-3 hours, when the temperature reaches 170-180°C, unload;

[0028] (2) Rolled sheet: control the thickness of the rolled sheet within 2mm;

[0029] (3) Grinding: use 3R pendulum mill for grinding, control particle size: -240 mesh pass rate 55-75%;

[0030] (4) Pressing: use a 500-ton hydrauli...

Embodiment 2

[0051] Embodiment 2: Electric locomotive pantograph carbon slide plate, adopt the following raw materials to make by weight: 4.3 parts of semi-reinforcing carbon black, 1.5 parts of -398 flake graphite, 0.8 part of 599 flake graphite, 0.5 part of charcoal powder and melted coal 4.6 parts of asphalt.

[0052] The preparation method is the same as in Example 1.

Embodiment 3

[0053] Embodiment 3: electric locomotive pantograph carbon slide plate, adopt the following raw materials to make by weight: 6.3 parts of semi-reinforcing carbon black, 3.5 parts of -398 flake graphite, 2.8 parts of 599 flake graphite, 1.5 parts of charcoal powder and melted coal 6.6 parts of asphalt.

[0054] The preparation method is the same as in Example 1.

[0055] Below is the inspection report of the product of the present invention by the Product Quality Supervision and Inspection Center of the Ministry of Railways:

[0056]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an electric locomotive pantograph carbon slide plate, which is made of the following raw materials in parts by weight: 4.3-6.3 parts of semi-reinforcing hydrocarbon black, 1.5-3.5 parts of 398 crystalline flake graphite, 0.8-2.8 parts of 599 crystalline flake graphite, 0.5-1.5 parts of charcoal powder, and 4.6-6.6 parts of melting coal pitch. The preparation method comprises technical steps of: hot mixing, rolling, grinding, pressing, roasting, impregnating, graphitizing, rough machining, impregnating, solidifying, finish machining, impregnating, bonding by adhesive, solidifying and product inspecting. The electric locomotive pantograph carbon slide plate has the advantages of unique wear resisting and self-lubricating performance; low resistivity, small bonding resistance, strong ability for inhibiting spark, and good current carrying capacity, thus being suitable for working condition of high power and high current; uniform and compact structure, relatively high mechanical strength and impact resistance; and good corrosion resistance, thus being suitable for working in various environmental and climate conditions.

Description

technical field [0001] The invention relates to a pantograph carbon slide plate of an electric locomotive, which is suitable for the technical fields of urban rail transit, subway, and mining locomotives. Background technique [0002] Electric locomotive pantograph carbon skateboard is an important current-collecting part for locomotives to import electric energy. With the development of electrified railways and high-speed railways, the subject of reducing wear of railway catenary wires and improving the wear-resistant and self-lubricating properties of skateboards has always been an extremely important issue in the development of the world's railways. important research project. [0003] There are three main types of pantograph slides: powder metallurgy slides, carbon slides, and metal-impregnated carbon slides. Industrially developed countries have successively developed carbon slides to replace powder metallurgy slides, effectively reducing the wear on catenary wires and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/532C04B35/622
Inventor 张继江
Owner 河北翔九石墨股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap