Sulfur-tolerant methanation catalyst and its preparation method

A technology for sulfur-resistant methanation and catalyst, which is applied in the field of sulfur-resistant methanation catalyst and its preparation, and can solve the problems of low methane selectivity and low CO conversion rate, etc.

Inactive Publication Date: 2012-05-23
ENN SCI & TECH DEV
View PDF10 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent US4491639 mentions that adding Zr, Ce, etc. to the sulfide catalyst of V, Mo or W can enhance the stability of the catalyst. This patent clearly points out that the sulfide of the above metal is directly used as the catalyst instead of using a porous substance as ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sulfur-tolerant methanation catalyst and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The second aspect of the present invention is the preparation method of the sulfur-tolerant methanation catalyst described in the first aspect of the present invention, which generally includes a co-impregnation step, a drying step and a calcination step. Specifically, step a is to prepare an impregnation solution, the solution contains molybdenum precursors and cobalt precursors, and at least one of zirconium precursors, cerium precursors or lanthanum precursors. Since this solution is used to impregnate the support, it is called an impregnation solution. Wherein, the solvent is water, the molybdenum precursor is a water-soluble molybdate, the cobalt precursor is a water-soluble cobalt salt, and the zirconium precursor is a water-soluble zirconium salt or a water-soluble zirconate or zirconate, The cerium precursor is a water-soluble cerium salt, and the lanthanum precursor is a water-soluble lanthanum salt.

[0033]Wherein the water-soluble molybdate is selected from...

Embodiment 1

[0054] Weigh 18.42g (NH 4 ) 6 Mo 7 o 24 4H 2 O, 9.67g Co(NO 3 ) 2 ·6H 2 O, 5.06gCe(NO 3 ) 3 ·6H 2 O was dissolved in 60mL of high-purity water, and N-diethanolamine complex stabilizer was added. 100g Al 2 o 3 (The Al 2 o 3 γ-Al 2 o 3 , its physical properties are as follows: specific surface area ≥ 200m2 / g, pore volume ≥ 0.40mL / g, water absorption ≥ 52%, bulk density 0.65-0.72g / mL, crushing strength ≥ 80N / grain, particle size 3- 5mm, the same below) was put into the prepared mixed impregnation solution, left overnight, dried naturally, then dried at 120°C for 8h, and finally calcined at 450°C for 3h to obtain the MoCoCe-a catalyst. Take 5mL catalyst for evaluation test, the results of catalyst activity evaluation and heat resistance evaluation experiment are shown in Table 1.

Embodiment 2

[0056] Weigh 18.42g (NH 4 ) 6 Mo 7 o 24 4H 2 O, 9.67g Co(NO 3 ) 2 ·6H 2 O, 5.26g ZrOCl 2 ·8H 2 O was dissolved in 60mL high-purity water, and citric acid complex stabilizer was added. 100gAl 2 o 3 Put it into the prepared mixed impregnation solution, let it stand overnight, dry it naturally, then dry it at 120°C for 8 hours, and finally calcinate it at 450°C for 3 hours to obtain the MoCoZr-a catalyst. Take 5mL catalyst for evaluation test, the results of catalyst activity evaluation and heat resistance evaluation experiment are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a sulfur-tolerant methanation catalyst and its preparation method, and relates to a sulfur-tolerant methanation catalyst which can be used under a wide operation condition particularly at high temperature and its preparation method, and the sulfur-tolerant methanation catalyst contains a carrier and an active component loaded on the carrier. The carrier is selected from alumina, silica, zirconium dioxide, active carbon or molecular sieve, the active component comprises a molybdenum oxide taken as a main active component, a cobalt oxide taken as a first auxiliary agent; and a zirconium oxide, a cerium oxide or a lanthanum oxide, or a mixture composed of at least two above oxides which is taken as a second auxiliary agent. The invention also discloses the preparation method of the sulfur-tolerant methanation catalyst which is composed of a dipping step, a drying step and a calcining step.

Description

technical field [0001] The invention relates to a methanation catalyst and a preparation method thereof, in particular to a sulfur-resistant methanation catalyst suitable for wide operating conditions, especially at high temperatures, and a preparation method thereof. Background technique [0002] As a low-carbon, high-efficiency, and safe clean energy, natural gas will account for an increasing proportion of primary energy consumption. The amount of natural gas that can be exploited is very limited, and the crisis of gas sources has caused the price of natural gas to rise nationwide. Therefore, many domestic and foreign companies and R&D institutions use coal or heavy oil and other fossil raw materials to produce natural gas, and my country has also carried out many coal-to-natural gas projects. The simple process of coal-to-natural gas is as follows: coal gasification to produce synthesis gas (CO, H 2 ), then carry out desulfurization and decarbonization and water gas sh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/887B01J23/882C07C9/04C07C1/04
Inventor 王会芳张荣毕继诚甘中学
Owner ENN SCI & TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap