Heat resistant aluminum color epoxy organosilicon paint and preparation method thereof

A silicone and heat-resistant paint technology, applied in the direction of metal-free paints, coatings, polyamide coatings, etc., can solve the problem of low proportion of epoxy resin, limit the application of epoxy silicone resin or paint, and cannot meet the use requirements And other issues

Active Publication Date: 2012-06-27
天津灯塔涂料工业发展有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The key reason is that the commercially available epoxy-modified silicone resin has a low proportion of epoxy resin (generally epoxy: silicone is 3:7), which cannot meet the requirements of specific products.
Thus limiting the application of epoxy silicone resin or lacquer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] An aluminum-colored epoxy silicone heat-resistant paint, comprising self-made H61-1 epoxy-modified silicone resin, polyamide curing agent, and floating aluminum powder, by weight (g)

[0041] Ingredient one:

[0042] H61-1 Epoxy Modified Silicone Resin 100

[0043] Ingredient two:

[0044] Polyamide resin 80-100

[0045] Toluene 40-50

[0046] Butanol 40-50

[0047] Cyclohexanone 10-20

[0048] Ingredient three:

[0049] Floating aluminum powder 20

[0050] Component 1: Component 2: Component 3 = 100:30:20;

[0051] Of which: H61-1 epoxy modified silicone resin

[0052] Monomethyltrichlorosilane 2-15

[0053] Dimethyldichlorosilane 2-15

[0054] Monophenyltrichlorosilane 5-15

[0055] Diphenyldichlorosilane 2-15

[0056] Xylene 15-30

[0057] Ethanol 10-30

[0058] Water 40-50

[0059] 601 epoxy resin 20-35

[0060] Cyclohexanone 10-20

[0061] Xylene 20-50 .

Embodiment 2

[0063] An aluminum-colored epoxy silicone heat-resistant paint, comprising self-made H61-1 epoxy-modified silicone resin, polyamide curing agent, and floating aluminum powder, by weight (g)

[0064] Ingredient one:

[0065] H61-1 Epoxy Modified Silicone Resin 100 g

[0066] Ingredient two:

[0067]Polyamide resin 80 g

[0068] Toluene 40 g

[0069] Butanol 40 g

[0070] Cyclohexanone 10 g

[0071] Ingredient three:

[0072] Floating aluminum powder 20 g

[0073] Component 1: Component 2: Component 3 = 100:30:20;

[0074] Of which: H61-1 epoxy modified silicone resin

[0075] Monomethyltrichlorosilane 2 g

[0076] Dimethyldichlorosilane 2 g

[0077] Monophenyltrichlorosilane 5 g

[0078] Diphenyldichlorosilane 2 g

[0079] Xylene 15 g

[0080] Ethanol 10 g

[0081] water 40 g

[0082] 601 epoxy resin 20 g

[0083] Cyclohexanone 10 g

[0084] Xylene 20 g.

Embodiment 3

[0086] An aluminum-colored epoxy silicone heat-resistant paint, consisting of self-made H61-1 epoxy-modified silicone resin, polyamide curing agent, and floating aluminum powder, by weight (g)

[0087] Ingredient one:

[0088] H61-1 Epoxy Modified Silicone Resin 100 g

[0089] Ingredient two:

[0090] Polyamide resin 100 g

[0091] Toluene 50 g

[0092] Butanol 50 g

[0093] Cyclohexanone 20 g

[0094] Ingredient three:

[0095] Floating aluminum powder 20 g

[0096] Component 1: Component 2: Component 3 = 100:30:20;

[0097] Of which: H61-1 epoxy modified silicone resin

[0098] Monomethyltrichlorosilane 15 g

[0099] Dimethyldichlorosilane 15 g

[0100] Monophenyltrichlorosilane 15 g

[0101] Diphenyldichlorosilane 15 g

[0102] Xylene 30 g

[0103] Ethanol 30 g

[0104] water 50 g

[0105] 601 epoxy resin 35 g

[0106] Cyclohexanone 20 g

[0107] Xylene 50 g.

[0108]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a heat resistant aluminum color epoxy organosilicon paint. The paint is characterized in that the paint comprises, by weight, 100 parts of a component I which is an H61-1 epoxy modified organosilicon resin; 30 parts of a component II which comprises 80-100 parts of a polyamide resin, 40-50 parts of toluene, 40-50 parts of butanol and 10-20 parts of cyclohexanone; and 20 parts of a component III which is floating aluminum powder. The invention also relates to a preparation method of the paint. The preparation method comprises the following steps: 1, preparing the H61-1 epoxy modified organosilicon resin; 2, adding the polyamide resin, toluene, butanol and cyclohexanone to a burdening basin, stirring them for 15min at a low-medium speed of 200-400r / min, and packaging after the solid test qualification; 3, packaging the floating aluminum powder after examining; and 4, mixing the component I, the component II and the component III according to a ratio of 100:20:20, allowing them to stand for 20min, and packaging them after examining. The paint has the following beneficial effect: the paint possess excellent physical and chemical performances of decorativeness, heat resistance, salt spray resistance, salt water resistance, water resistance, cold resistance, oil resistance, hydrocarbon solvent resistance, adhesion force, impact, flexibility and the like.

Description

technical field [0001] The invention belongs to chemical coatings, in particular to an aluminum-colored epoxy organic silicon heat-resistant paint and a preparation method. Background technique [0002] Existing epoxy silicone resins or paints can meet general decoration, heat resistance and protection requirements, but special performance requirements such as salt spray resistance, damp heat resistance, cold resistance, salt water resistance, lubricating oil resistance, hydrocarbon liquid resistance , heat resistance above 500 ℃ and other properties can not meet the requirements. Epoxy modified silicone resin as a film-forming material of heat-resistant paint has excellent high temperature resistance, atmospheric resistance and humidity and heat resistance, and has good adhesion to metal, which is indispensable for special purposes such as high-temperature anti-corrosion and high-temperature insulation. Material. The key reason is that the proportion of commercially avail...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/10C09D177/00C09D5/38C08G77/42
Inventor 刘建颖王宏心王洪鹏
Owner 天津灯塔涂料工业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap