Unsaturated anhydride modified liquid nitrile rubber flexibilizer for unsaturated resin and preparation method thereof
A liquid nitrile rubber and acid anhydride modification technology, applied in the field of unsaturated acid anhydride modified liquid nitrile rubber toughening agent, can solve the problems of decreased strength and modulus, water resistance, aging resistance and fatigue resistance, etc. Achieve uniform and stable dispersion and reactivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] The unsaturated acid anhydride modified liquid acrylonitrile-butadiene rubber toughening agent for unsaturated resin described in embodiment 1 of the present invention is made up of unsaturated anhydride-modified liquid acrylonitrile-butadiene rubber addition polymer and ethylenically unsaturated monomer; The unsaturated acid anhydride modified liquid nitrile rubber addition polymer consists of catalyst, unsaturated anhydride and liquid nitrile rubber. The unsaturated acid anhydride is an unsaturated cyclic acid anhydride, and this embodiment uses maleic anhydride; the liquid nitrile rubber is a liquid nitrile rubber with a hydroxyl-terminated structure; the catalyst is a quaternary ammonium halide, and this embodiment uses benzyl triethyl chloride Ammonium. As the ethylenically unsaturated monomer, a styrene unsaturated monomer is used.
[0024] In addition, this embodiment 1 also relates to the technical scheme of the preparation method of the unsaturated acid anhydr...
Embodiment 2
[0031] Present embodiment 2 is modified on the basis of embodiment 1 to the preparation method of unsaturated acid anhydride modified liquid nitrile rubber toughening agent for unsaturated resin, specifically as follows:
[0032] Use an electronic balance to weigh qualified liquid nitrile rubber, preheat it at 80°C and add it to the reaction flask; then weigh maleic anhydride according to the mass ratio of maleic anhydride to liquid nitrile rubber of 1:10, and press the catalyst Weigh benzyltriethylammonium chloride at a mass ratio of 1:20 to liquid nitrile rubber and add it to the reaction flask. React in an oil bath at a temperature of 80°C to 150°C for 12 hours to obtain an addition polymer, lower the temperature, then weigh styrene according to the mass ratio of styrene to addition polymer of 1:3, and add it to the addition polymer , kept stirring at a temperature of 70°C for 6 hours, and the double bond content of the polymer mixture was detected to be 3.67%, and the mole...
Embodiment 3
[0034] Present embodiment 3 is to modify the preparation method of the unsaturated acid anhydride modified liquid nitrile rubber toughening agent for unsaturated resin on the basis of embodiment 1, as follows:
[0035]Weigh qualified liquid nitrile rubber with an electronic balance, preheat it at 80°C and add it to the reaction flask; then weigh maleic anhydride according to the mass ratio of maleic anhydride to liquid nitrile rubber of 1:10, and then press catalyst and The mass ratio of liquid nitrile rubber is 1:20. Weigh benzyltriethylammonium chloride and add it to the reaction flask. React in an oil bath at a temperature of 80°C to 150°C for 16 hours to obtain an addition polymer, lower the temperature, then weigh styrene according to the mass ratio of styrene to addition polymer 30:70, and add it to the addition polymer , insulated and stirred at 80°C for 7 hours, the double bond content of the polymer mixture was detected to be 3.57%, and the molecular weight was 43500....
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap