Preparation method for cordierite
A cordierite and prefabricated technology, applied in the field of ceramic material preparation, can solve the problems of high cost, low cordierite density, complicated preparation process, etc., and achieve the effects of low cost, suitable for large-scale industrial production, and uniform temperature
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0009] The invention provides a kind of preparation method of cordierite, comprises the following steps:
[0010] 1) Mix ceramic powder containing magnesia, alumina and quartz with sintering aids evenly, add polyvinyl alcohol aqueous solution, disperse evenly, and then isostatically press to form cordierite preforms;
[0011] 2) Microwave sintering the cordierite preform in step (1) to obtain cordierite; the microwave sintering temperature is 1100-1200°C.
[0012] According to the preparation method of the present invention, the ceramic powder and the sintering aid are firstly mixed evenly, then the aqueous solution of polyvinyl alcohol is added to disperse evenly to prepare ceramic slurry, and the cordierite preform is obtained by isostatic pressing, which can make the cordierite preform It has a certain shape and can ensure the minimization of the porosity of the cordierite preform; finally, through microwave sintering, and the temperature of microwave sintering is controlle...
Embodiment 1
[0024] (1) 33 parts by weight of magnesium oxide, 14 parts by weight of alumina, 53 parts by weight of quartz, 0.2 parts by weight of CaO and 0.3 parts by weight of TiO 2 After mixing, disperse in ethanol, electric stirring for 60min to mix evenly, heat and dry to volatilize ethanol.
[0025] (2) Add 5 parts by weight of 6wt% polyvinyl alcohol aqueous solution to the dried mixing system in step (1), stir to make the mixture uniform, granulate, then put it into an isostatic pressing mold, and perform molding on an isostatic pressing machine The preform was obtained, and the forming pressure was 400MPa.
[0026] (3) Put the preform in step (2) in a microwave oven and sinter at 1100° C. for 20 minutes to obtain the cordierite product S1.
Embodiment 2
[0028] (1) 13.5 parts by weight of alumina, 33.5 parts by weight of magnesium oxide, 53 parts by weight of quartz, 0.2 parts by weight of CaO and 0.3 parts by weight of TiO 2 After mixing, disperse in ethanol, electric stirring for 60min to mix evenly, heat and dry to volatilize ethanol.
[0029] (2) Add 5 parts by weight of 6wt% polyvinyl alcohol aqueous solution to the dried mixing system in step (1), stir to make the mixture uniform, granulate, then put it into an isostatic pressing mold, and perform molding on an isostatic pressing machine The preform was obtained, and the forming pressure was 400MPa.
[0030] (3) Put the preform in step (2) in a microwave oven and sinter at 1200° C. for 20 minutes to obtain the cordierite product S2.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com