Buckling deformation-resistant glass fiber reinforced polycarbonate resin and preparation method thereof

A technology of polycarbonate resin and polycarbonate, which is applied in the field of glass fiber reinforced polycarbonate resin and its preparation, can solve the problems of inconvenient material selection, and achieve the effects of stable size, improved warping performance, and consistent shrinkage

Active Publication Date: 2012-10-10
SHANGHAI KUMHO SUNNY PLASTICS
View PDF9 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the reinforced glass fiber is a combination of various glass fibers, which is not convenient for material selection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Buckling deformation-resistant glass fiber reinforced polycarbonate resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Example 1 Preparation of glass fiber reinforced polycarbonate resin of the present invention (1)

[0048] (1) Weigh each raw material according to the following weight ratio: 43 parts of PC-300-15, 7 parts of toughening agent EXL2678, 50 parts of glass fiber CSG 3PA-830, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 168 , 0.2 parts of internal lubricant PETS;

[0049] (2) Mix the above raw materials (excluding glass fiber) in a medium-speed mixer for 20 minutes;

[0050] (3) Put the above-mentioned mixed raw materials into a twin-screw extruder with a melting temperature of 200-280°C, side-feed the glass fiber, melt extrude, and granulate. The temperature of each zone of the twin-screw extruder is: 1 The temperature in Zone 2 is 200-280°C, the temperature in Zone 3-4 is 200-280°C, the temperature in Zone 5-6 is 200-280°C, and the temperature in Zone 7-8 is 200-280°C. Control the temperature in Zone 9-10 to be 200-280°C.

Embodiment 2

[0051] Example 2 Preparation of glass fiber reinforced polycarbonate resin of the present invention (2)

[0052] (1) Weigh each raw material according to the following weight ratio: 77 parts of PC-300-15, 3 parts of toughening agent EXL2678, 20 parts of glass fiber CSG 3PA-830, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 168 , 0.2 parts of internal lubricant PETS;

[0053] (2) Mix the above raw materials (excluding glass fiber) in a medium-speed mixer for 20 minutes;

[0054] (3) Put the above-mentioned mixed raw materials into a twin-screw extruder with a melting temperature of 200-280°C, side-feed the glass fiber, melt extrude, and granulate. The temperature of each zone of the twin-screw extruder is: 1 The temperature in Zone 2 is 200-280°C, the temperature in Zone 3-4 is 200-280°C, the temperature in Zone 5-6 is 200-280°C, and the temperature in Zone 7-8 is 200-280°C. Control the temperature in Zone 9-10 to be 200-280°C.

Embodiment 3

[0055] Example 3 Preparation of glass fiber reinforced polycarbonate resin of the present invention (3)

[0056] (1) Weigh each raw material according to the following weight ratio: 60 parts of polyethylene carbonate (weight average molecular weight 18000), 5 parts of toughening agent EXL2678, 35 parts of glass fiber (width-to-diameter ratio 2:1, length 6mm) , 0.5 part of antioxidant 1010, 0.5 part of antioxidant 168, 0.5 part of internal lubricant PETS, 0.5 part of release agent polyethylene wax;

[0057] (2) Mix the above raw materials (excluding glass fiber) in a medium speed mixer for 10 minutes;

[0058] (3) Put the above-mentioned mixed raw materials into a twin-screw extruder with a melting temperature of 200-280°C, side-feed the glass fiber, melt extrude, and granulate. The temperature of each zone of the twin-screw extruder is: 1 The temperature in Zone 2 is 200-280°C, the temperature in Zone 3-4 is 200-280°C, the temperature in Zone 5-6 is 200-280°C, and the tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides buckling deformation-resistant glass fiber reinforced polycarbonate resin. The buckling deformation-resistant glass fiber reinforced polycarbonate resin is prepared from the following raw materials in part by weight: 43 to 77 parts of polycarbonate, 3 to 7 parts of flexibilizer, 20 to 50 parts of glass fiber, and 0 to 2 parts of aid; and the glass fiber is short fiber of which the width diameter ratio is (2:1)-(6:1), and the length is 3 to 6mm. The invention also provides a preparation method for the buckling deformation-resistant glass fiber reinforced polycarbonate resin. The method comprises the following steps of: weighing raw materials in a weight ratio; mixing polycarbonate, flexibilizer, and aid in a mixer for 10 to 30 minutes; and feeding the mixed raw materials into a twin-screw extruder, performing side feeding of the glass fiber, performing melt extrusion, and pelleting. The buckling deformation-resistant glass fiber reinforced polycarbonate resin has the advantages that the added glass fiber is special-shaped glass fiber which is high in width diameter ratio, so that when melt flows, the orientation of the glass fiber is avoided; therefore, the shrinkage rates in the horizontal and longitudinal directions are consistent with each other, and the buckling performance of a final product is improved; the rigidity and the flowability are improved, and the glass fiber reinforced polycarbonate resin is excellent is comprehensive mechanical property; and raw materials have few varieties, so that materials can be selected conveniently, and the actual production and operation can be realized conveniently.

Description

technical field [0001] The invention relates to a modified polycarbonate resin, in particular to a warpage-resistant glass fiber reinforced polycarbonate resin and a preparation method thereof. Background technique [0002] The chemical name of polycarbonate (Polycarbonate, PC) is 2,2'-bis(4-hydroxyphenyl)propane polycarbonate, which is a non-crystalline engineering plastic with excellent impact strength, thermal stability and gloss. , Antibacterial properties, flame retardant properties and anti-pollution properties. Glass fiber reinforced polycarbonate improves the mechanical properties and rigidity of polycarbonate, the linear expansion coefficient is greatly reduced, the dimensional stability is greatly improved, and the molding shrinkage rate is significantly reduced. At the same time, it overcomes the stress cracking resistance and fatigue strength of polycarbonate. It can be used to replace aluminum, zinc and other die-casting load parts and products with extremely h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L25/10C08L33/12C08K7/14B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/875B29C48/92B29C2948/92704B29C2948/92895
Inventor 杨春华李文强李强罗明华辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com