Method for preparing high-bulk eucalyptus alkaline peroxide mechanical pulp

A technology of hydrogen peroxide and bulk thickness, which is applied in textiles, papermaking, and fiber raw material processing. It can solve the problems of not being able to meet a large number of needs, reduce paper stiffness, and insufficient resources, so as to reduce chemical consumption and increase fine fibers. content, the effect of reducing energy consumption

Active Publication Date: 2012-10-24
GUANGXI JINGUI PULP PAPER
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Yet the poplar wood that adopts in the raw material of this inventive method, grows mostly in northern region, and growth period is long, and resource amount is insufficient, can't satisfy the large demand of wood raw material of papermaking industry; If it is too large, the flexibility of the fiber is improved, the stiffness of the paper is reduced, and the bulk is reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A method for preparing high-bulk eucalyptus alkaline hydrogen peroxide mechanical pulp, carried out in the following steps:

[0032] (1) Heat treatment and washing of raw materials: take the peeled eucalyptus wood that has been stored for 3 months, cut it into eucalyptus chips with a length of 7-45mm, a thickness of 3-7mm, and a width of 5-20mm, heat it to 60°C with secondary steam, and heat it to 88°C Wash with water to remove knots and gravel;

[0033] (2) Pre-steaming: pre-steaming the washed eucalyptus chips at 88°C for 18 minutes;

[0034] (3) Extrusion and impregnation: Extrude the pre-steamed eucalyptus chips with a wood chip press with a compression ratio of 1:2.8~4, with a torque of 180kNm. The extruded eucalyptus chips can absorb the liquid better due to the sponge effect; Impregnated in the liquid medicine after pressing, the composition of the liquid medicine is: H 2 o 2 , the dosage is 1.7% of the absolute dry wood chip weight; NaOH, the dosage is 1.6% o...

Embodiment 2

[0045] A method for preparing high-bulk eucalyptus alkaline hydrogen peroxide mechanical pulp, carried out in the following steps:

[0046] (1) Heat treatment and washing of raw materials: Take the peeled eucalyptus wood that has been stored for 6 months, cut it into eucalyptus chips with a length of 7-45mm, a thickness of 3-7mm, and a width of 5-20mm, heat to 50°C, wash with 85°C water, remove Knots and gravel;

[0047] (2) Pre-steaming: the washed eucalyptus chips are pre-steamed at 85°C for 15 minutes;

[0048] (3) Extrusion and impregnation: Extrude the pre-steamed eucalyptus chips with a wood chip press with a compression ratio of 1:2.8~4, with a torque of 180kNm. The extruded eucalyptus chips can absorb the liquid better due to the sponge effect. After being squeezed, it is immersed in the liquid medicine, and the composition of the liquid medicine is: H 2 o 2 , the dosage is 2% of the weight of the absolute dry wood chips; NaOH, the dosage is 1.6% of the weight of th...

Embodiment 3

[0059] A method for preparing high-bulk eucalyptus alkaline hydrogen peroxide mechanical pulp, carried out in the following steps:

[0060] (1) Heat treatment and washing of raw materials: take 50% of the peeled eucalyptus wood stored for 3 months and 6 months each, cut into eucalyptus chips with a length of 7~45mm, a thickness of 3~7mm, and a width of 5~20mm, and heat them with secondary steam To 55°C, wash with 90°C water to remove wood knots and gravel;

[0061] (2) Pre-steaming: the washed eucalyptus chips are pre-steamed at 90°C for 20 minutes;

[0062] (3) Extrusion and impregnation: Extrude the pre-steamed eucalyptus chips with a wood chip press with a compression ratio of 1:2.8~4, with a torque of 180kNm. The extruded eucalyptus chips can absorb the liquid better due to the sponge effect; Impregnated in the liquid medicine after pressing, the composition of the liquid medicine is: H 2 o 2 , the dosage is 1.9% of the absolute dry wood chip weight; NaOH, the dosage is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing high-bulk eucalyptus alkaline peroxide mechanical pulp. The method includes the steps of raw material heating, washing, pre-steaming, extrusion, steeping, reacting, high consistency refining, bleaching, latency removal, low consistency refining, screening, concentrating, and pulp washing for formation of finished pulp. The method uses eucalyptus as raw material, lowers consumption of NaOH and changes refining ways, and accordingly consumption is lowered, and cost is reduced. In addition, bulk of the eucalyptus alkaline peroxide mechanical pulp is increased from lower than 2.8cm<3> / g to more than 3.5cm<3> / g, and paperboard bulkiness is improved greatly.

Description

technical field [0001] The invention belongs to the technical field of alkaline hydrogen peroxide mechanical pulp, in particular to a method for preparing high bulk eucalyptus alkaline hydrogen peroxide mechanical pulp. Background technique [0002] Alkaline Peroxide Mechanical Pulp (Alkaline Peroxide Mechanical Pulp), referred to as APMP, is an energy-saving and environmentally friendly pulping technology introduced in the 1980s. Its pulping feature is the combination of pulping and bleaching. The bleaching process is completed at the same time as pulping; because no sulfite is used in the pulping process, and the wastewater does not contain sulfur compounds, environmental protection is relatively easy; the number of impregnation stages, NaOH, H 2 o 2 It has the outstanding advantages of high yield, high whiteness, high strength and low pollution, and wide adaptability of raw materials. It is a fast-growing and promising chemical-mechanical pulping method. [0003] China...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21C5/00
Inventor 钟义昌郑锦国饶建山
Owner GUANGXI JINGUI PULP PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap