Semi-solid extruding and casting molding mould and molding process of compressor crankshaft and

A compressor crankshaft and semi-solid extrusion technology, which is applied in the field of compressor crankshaft forming, can solve the problems that have not been seen in the application of semi-solid forming technology to compressor crankshafts, and achieve reduced defects, less machining allowance, shrinkage and shrinkage cavities The effect of less defects

Inactive Publication Date: 2012-10-31
XI AN JIAOTONG UNIV
View PDF4 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] So far, there are no relevant reports on the application of sem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Semi-solid extruding and casting molding mould and molding process of compressor crankshaft and

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] The present invention will be described in detail below in conjunction with the accompanying drawings.

[0023] With reference to accompanying drawing, a kind of compressor crankshaft semi-solid extrusion casting molding mold comprises upper mold 6 and lower mold 8, and upper mold 6 and lower mold 8 are respectively fixed on the upper and lower mold base of extrusion casting machine, and upper mold 6 and the lower mold 8 are molded to form a closed space which is the cavity of the compressor crankshaft extrusion casting 7, and the center of the cavity is a splitter cone, which divides the semi-solid slurry into the cavity of the circumferentially distributed compressor crankshaft. It can be used to form more than 2 compressor crankshafts. The punch 10 enters the cavity through the hole in the center of the lower die 8, pushes the slurry on the barrel of the extrusion casting forming equipment into the cavity, and after the filling is completed Carry out pressure mainten...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a semi-solid extruding and casting molding mould and molding process of a compressor crankshaft. The mould comprises an upper mould and a lower mould, wherein a closed space is formed by carrying out die assembly on the upper mould and the lower mould and serves as a cavity of a extruding and casting piece of the compressor crankshaft; a puncher pin passes through a hole at the center of the lower mould to enter the cavity; a template of the upper mould is fixedly connected with a lug boss part at the top of the upper mould through a pressing rod; the top of a mould core is fixedly connected to the template of the upper mould through a thread; a piston rod passes through the center of the template of the upper mould; the flange end at the lower part of the piston rod is in threaded connection with a pressurizing plate to drive the pressurizing plate to move in the space of a groove at the upper part of the upper mould; the bottom face of the pressurizing plate is connected with an annular lug boss; and the mould core passes through a middle hole of the annular lug boss and is inserted into the top of the mould cavity. In the molding process, semi-solid slurry is adopted to fill the mould, a casting temperature is low, and a mould filling process is gentle; and an extruding and casting method is adopted for molding. Therefore, the molding mould and the molding process have the advantages that the material utilization rate is high, the service life of the molding mould is long, tissues of a molded piece are dense, and the production efficiency is high.

Description

technical field [0001] The invention belongs to the technical field of compressor crankshaft forming, and in particular relates to a compressor crankshaft semi-solid extrusion casting forming die and forming process. Background technique [0002] At present, the production of compressor crankshaft mainly adopts the method of metal mold gravity casting. Due to the large gating and riser system, the material utilization rate is low, the scrap rate is high, the processing volume of castings is large, and the production efficiency is low. [0003] The semi-solid forming technology originated in the 1970s, has gone through basic research, technology development, and equipment development, and has now entered the stage of industrial application. Compared with liquid metal casting, semi-solid metal has a certain volume fraction of spherical primary solid phase, and semi-solid metal formed parts are dense, with high mechanical properties, less machining, and long mold life; compared...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D17/22
Inventor 赵升吨林文捷张琦张晨阳陶文琉赵承伟
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap