Thiazole compound, its preparation and application

A compound and thiazole technology, which is applied in the field of thiazole compounds and their preparation and application, can solve the problems of scarcity of corrosion inhibitors, corrosion damage, loss of performance, etc., and achieve the effects of convenient synthesis, inhibition of damage, and strong applicability

Inactive Publication Date: 2014-06-18
INST OF OCEANOLOGY - CHINESE ACAD OF SCI
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although copper ranks after hydrogen in the metal activity sequence table, and its activity is poor, copper is also extremely susceptible to corrosion damage to varying degrees in systems containing chloride ions, sulfates, nitrates and other corrosive media, thus Lose its original various performances, and even bring huge disasters
[0004] At present, although there have been many reports on seawater corrosion inhibitors for metallic copper, the number of corrosion inhibitors that can be used in actual production is extremely rare, and most of them still use traditional benzotriazole compounds as copper corrosion inhibitors. agent, which brings a series of economic and environmental problems to the production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thiazole compound, its preparation and application
  • Thiazole compound, its preparation and application
  • Thiazole compound, its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (5-methyl-[1,3,4]thiadiazole-2-mercapto)-acetic acid (4-hydroxy-3-methoxy-benzylidene)-hydrazide preparation method:

[0035] The chemical reaction equation is:

[0036]

[0037] First, acetic acid and methanol were mixed in an equimolar ratio, and the reaction was dehydrated to obtain methyl acetate (I), the product (I) was mixed with excess hydrazine hydrate, and the reaction was carried out in an oil bath at 80 °C for 2 h to obtain acetyl hydrazide (II), and the reaction product (II) was obtained. II) with excess carbon disulfide in KOH (or NaOH, Ca 2 OH) in an alkaline environment to generate compound (III), and the product (III) was cyclized under the catalysis of concentrated sulfuric acid at an oil bath temperature of 75 ° C for 1.5 h to obtain product (IV), namely -mercapto-5-methyl -[1,3,4]thiadiazole, then in NaOH (or KOH, Ca 2 OH) product (IV) reacts with excess chloroethyl acetate to obtain product (V) under alkaline conditions, reacts product (V) with ...

Embodiment 2

[0046] Conditions: The experimental material is copper (99.999%), (5-methyl-[1,3,4]thiadiazole-2-mercapto)-acetic acid (4-hydroxy-3-methoxy-benzylidene )-hydrazide and emulsifier are prepared as corrosion inhibitor of microemulsion, the medium is 3.5% sodium chloride solution, the dosage is 0.5L, and (5-methyl-[1,3,4]thiadiazole-2 The amount of -mercapto)-acetic acid (4-hydroxy-3-methoxy-benzylidene)-hydrazide is 0.0050 g, the temperature is 25° C., and the pH=7.5.

[0047] The corrosion inhibition efficiencies obtained through experimental tests are: electrochemical impedance spectroscopy 85.11%, dynamic potential polarization 82.03%, showing that it is a corrosion inhibitor with low dosage and high efficiency.

Embodiment 3

[0049] Conditions: The experimental material is copper (99.999%), (5-methyl-[1,3,4]thiadiazole-2-mercapto)-acetic acid (4-hydroxy-3-methoxy-benzylidene )-hydrazide and emulsifier are prepared as corrosion inhibitor of microemulsion, the medium is 3.5% sodium chloride solution, the dosage is 0.5L, and (5-methyl-[1,3,4]thiadiazole-2 The amount of -mercapto)-acetic acid (4-hydroxy-3-methoxy-benzylidene)-hydrazide is 0.0100 g, the temperature is 25° C., and the pH=7.5.

[0050] The corrosion inhibition efficiencies obtained through experimental tests are: electrochemical impedance spectroscopy 91.39%, and dynamic potential polarization 84.55%, showing that it is a corrosion inhibitor with low dosage and high efficiency.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a seawater corrosion inhibitor of copper, that is, a thiazole compound with low toxicity and high efficiency for inhibiting the corrosion to copper and copper products in seawater or common salt mediums, and its preparation and application. The thiazole compound is represented by (5-methyl-[1, 3, 4]thiadiazole-2-mercapto)-acetate(4-hydroxy-3-methoxy-benzylidene)-hydrazide and the structure formula is shown in the specification. The thiazole compound can be used as the seawater corrosion inhibitor of copper to resist corrosion to copper products in seawater or common salt mediums. According to the invention, the corrosion inhibitor disclosed in the invention has the advantages of low consumption, low toxicity, high efficiency, and strong continuous action ability, can effectively resist the corrosion to copper, and has a wide application prospect.

Description

technical field [0001] The invention relates to a copper seawater corrosion inhibitor, namely a low-toxicity and high-efficiency thiazole compound for inhibiting the corrosion of metallic copper and its products in seawater or sodium chloride medium, and its preparation and application. Background technique [0002] With the continuous consumption of various resources on land, the development and utilization of marine resources has become an inevitable way to solve the current resource depletion. However, seawater is a strong electrolyte solution with strong corrosiveness, which greatly limits the development and utilization of marine resources. Therefore, only by solving the corrosion problem of metal materials in seawater can the development and utilization value of marine resources be truly reflected. [0003] Copper has excellent mechanical strength, workability, electrical conductivity, thermal conductivity, solderability and other characteristics, and has been widely ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D285/125C23F11/14
Inventor 李伟华白雪田惠文曹琨侯保荣
Owner INST OF OCEANOLOGY - CHINESE ACAD OF SCI
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com