Dual organic modified cement-base expanded perlite fireproof thermal-insulation board and preparation method thereof

A technology of expanded perlite and fireproof thermal insulation board is applied in the field of double organic modified cement-based expanded perlite fireproof thermal insulation board and its preparation, which can solve the problems of low density and low elastic modulus, and achieve low elastic modulus and use Long life and good weather resistance

Inactive Publication Date: 2012-12-12
宁波荣山新型材料有限公司
View PDF7 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a double organically modified cement-based expanded perlite fireproof insulation board and its preparation method. The fireproof insulation board has strong deformation resistance, good crack resistance, impact resistance, and good weather resistance. Long service life, and has the advantages of high strength, high stability, low density, low elastic modulus, making up for the lack of elasticity of other inorganic insulation board systems, this method has high production efficiency and simple operation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dual organic modified cement-base expanded perlite fireproof thermal-insulation board and preparation method thereof
  • Dual organic modified cement-base expanded perlite fireproof thermal-insulation board and preparation method thereof
  • Dual organic modified cement-base expanded perlite fireproof thermal-insulation board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Take each raw material by the following weight: 52.5 grade cement 20kg, bulk density is 70kg of organically modified expanded perlite of 80g / L, active filler silica powder 2kg, polymer emulsion 7.4kg, additive superplasticizer 0.6kg; After the above raw materials are mixed evenly, 60kg of water is added, stirred into a semi-dry material by a self-falling mixer, filled into a mold, and pressed into a fireproof insulation board with a compression ratio of 1.8 by a pressing plate equipment, and obtained after several hours of high-temperature steam curing. finished product.

Embodiment 2

[0040] Take each raw material by the following weight: 52.5 grade cement 25kg, bulk density is 65kg of organically modified expanded perlite of 75g / L, active filler fly ash 1kg, polymer emulsion 9kg, additive early strength agent 1kg; After mixing evenly, add 45kg of water, stir it into a semi-dry material with a self-falling mixer, fill it into a mold, and use a pressing plate equipment to press it into a fireproof insulation board with a compression ratio of 2.5. After several hours of high-temperature steam curing, the finished product is obtained.

Embodiment 3

[0042] Take each raw material by the following weight: 15kg of 52.5 grade cement, 80kg of organically modified expanded perlite with a bulk density of 100g / L, 4.6kg of polymer emulsion, and 0.4kg of additive water repellent; after mixing the above raw materials uniformly, add 55kg of water is stirred into a semi-dry material by a self-falling mixer, filled into a mold, and pressed into a fireproof insulation board with a compression ratio of 1.5 using a pressing plate equipment, and the finished product is obtained after several hours of high-temperature steam curing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to view more

Abstract

The invention relates to a dual organic modified cement-base expanded perlite fireproof thermal-insulation board and a preparation method thereof. The dual organic modified cement-base expanded perlite fireproof thermal-insulation board mainly comprises the following components in percentage by weight: 50-80% of organic modified expanded perlite, 20-35% of Portland cement, 5-10% of polymer emulsion, 0-3% of active filler and 0.5-1% of additive. The preparation method comprises the following steps: evenly mixing raw materials, adding water, stirring to obtain a semidry material, filling the semidry material into a mold, compacting into a fireproof thermal-insulation board, and finally, carrying out high temperature steam curing for several hours. The dual organic modified cement-base expanded perlite fireproof thermal-insulation board not only has the advantages of strong deformation resistance, favorable crack resistance, shock resistance, favorable weather resistance, long service life, favorable fire resistance (Grade A) and the like in the Portland cement-base expanded perlite inorganic thermal-insulation board, but also has the advantages of high strength, low density and low elastic modulus. The invention has the characteristic of high production efficiency, and can implement large-scale production.

Description

technical field [0001] The invention belongs to the field of expanded perlite fireproof insulation board and its preparation, in particular to a double organic modified cement-based expanded perlite fireproof insulation board and its preparation method. Background technique [0002] In recent years, fires of building external insulation materials have occurred one after another in China, causing serious casualties and property losses. Flammable and combustible building external insulation materials have become a new kind of fire hazard, and the fires caused by them have shown a trend of frequent occurrence. Therefore, the fire safety of external wall insulation materials has become the focus of the fire departments. Among the large-scale application of building energy-saving thermal insulation materials, polystyrene foam board has become the most mainstream external thermal insulation material because of its light weight, good thermal insulation and thermal insulation. How...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/18
Inventor 王小山王智宇阮华李陆宝屠浩驰高锦秀
Owner 宁波荣山新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap