High-construction-performance polyurethane paint

A polyurethane coating and construction performance technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve the problems of high cost, slow drying speed, and insufficient solvent release, and achieve low cost, fast drying speed, and toxicity low effect

Active Publication Date: 2012-12-12
SKSHU PAINT
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the bright floor paint has good performance, its cost price is still on the high side, and due to the characteristics of the selecte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A polyurethane coating with high construction performance. The coating is prepared from components A and B at a ratio of 2:1, wherein the specific components and proportions of components A and B are as follows according to the mass ratio:

[0030] A component:

[0031] Soybean Short Oil Alkyd Resin 35%

[0032] Nitrocellulose 5%

[0033] Titanium dioxide 25%

[0034] Talc 20%

[0035] Anti-settling agent 1%

[0036] Defoamer 0.3%

[0037] Leveling agent 0.4%

[0038] Humectant 0.5%

[0039] Composite environmental solvent 12.8%;

[0040] Component B: polyisocyanate curing agent.

[0041] Wherein, the defoamer is a special defoamer for polyurethane, and its main component is modified silicone.

[0042] The leveling agent uses polyacrylate copolymer and fluorocarbon modified polyacrylate components.

[0043] The wetting agent adopts polyether modified dimethyl siloxane copolymer solution as the main component.

[0044] The composite environment-friendly solv...

Embodiment 2

[0048] A polyurethane coating with high construction performance. The coating is prepared from components A and B at a ratio of 2:1, wherein the specific components and proportions of components A and B are as follows according to the mass ratio:

[0049] A component:

[0050] Soy Short Vegetable Oil Alkyd Resin 45%

[0051] Nitrocellulose 3%

[0052] Titanium dioxide 20%

[0053] Talc 15%

[0054] Anti-settling agent 1%

[0055] Defoamer 0.2%

[0056] Leveling agent 0.2%

[0057] Humectant 0.5%

[0058] Composite environmental solvent 15.1%;

[0059] Component B: polyisocyanate curing agent.

[0060] Wherein, the defoamer is a special defoamer for polyurethane, and its main component is modified silicone.

[0061] The leveling agent uses polyacrylate copolymer and fluorocarbon modified polyacrylate components.

[0062] The wetting agent adopts polyether modified dimethyl siloxane copolymer solution as the main component.

[0063] The composite environment-friendly ...

Embodiment 3

[0067] A polyurethane coating with high construction performance. The coating is prepared from components A and B at a ratio of 2:1, wherein the specific components and proportions of components A and B are as follows according to the mass ratio:

[0068] A component:

[0069]Soybean Short Oil Alkyd Resin 40%

[0070] Nitrocellulose 3.5%

[0071] Titanium dioxide 24%

[0072] Talc 18%

[0073] Anti-settling agent 1%

[0074] Defoamer 0.2%

[0075] Leveling agent 0.2%

[0076] Humectant 0.3%

[0077] Composite environmental solvent 12.8%;

[0078] Component B: polyisocyanate curing agent.

[0079] Wherein, the defoamer is a special defoamer for polyurethane, and its main component is modified silicone.

[0080] The leveling agent uses polyacrylate copolymer and fluorocarbon modified polyacrylate components.

[0081] The wetting agent adopts polyether modified dimethyl siloxane copolymer solution as the main component.

[0082] The composite environment-friendly solve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-construction-performance polyurethane (PU) paint which is prepared by using main aggregates of alkyd resin, nitrocellulose, and a modified TDI curing agent. The paint has good construction performance. The paint is prepared from the components of: alkyd resin, nitrocellulose, titanium dioxide, talc, an organic solvent, a surfactant, a siccative, an anti-settling agent, and the modified TDI curing agent. With the components, the prepared PU paint has advantages of high surface drying speed. Under a natural environment, after 50min of natural drying, obtained materials can be fetched, and can be stacked and stored. The paint can be used for batched machine-stage on-line production, and provides good adhesive force for coated topcoat. During a drying early-stage, most of cross-linking reactions are fast. During a drying late-stage, the reactions are relatively slow, such that topcoats have certain dissolving capacity and good adhesive force for primers. A paint film has good flexibility and sealing ability, and is suitable for both soft and hard base materials. Especially, the paint film has good sealing ability for density boards, and assists in preventing oil-emitting or non-drying phenomena during a drying process. The paint provided by the invention is suitable for large-scale machine-stage productions of various solid wood furniture and board furniture.

Description

technical field [0001] The invention relates to a paint with high construction performance, in particular to a polyurethane colored primer. Background technique [0002] At present, the competition in the furniture industry is fierce. With the increase of the cost of raw materials and labor, the profits of the furniture industry are gradually declining. A series of ways to reduce costs, such as the improvement of production efficiency and the replacement of labor by automatic production lines, have gradually become the goals pursued by various furniture industries. This demand requires the coating to have higher construction performance and good environmental applicability. This product can improve production efficiency and is suitable for different construction techniques and different environments. Polyurethane coatings in the prior art, such as a vegetable oil-based environment-friendly bright floor paint disclosed in the invention patent of Chinese Patent No. 2009101607...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/06C09D175/14C09D7/12
Inventor 郑日光
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products