Ultraviolet light-cured hydrophilic coating and preparation method thereof

A hydrophilic coating, ultraviolet light technology, applied in polyamide coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of high cost, serious energy consumption, low efficiency and so on

Inactive Publication Date: 2012-12-12
郭文迅
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hydrophilic coatings currently used all adopt the heat-baked coating method, which con

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet light-cured hydrophilic coating and preparation method thereof
  • Ultraviolet light-cured hydrophilic coating and preparation method thereof
  • Ultraviolet light-cured hydrophilic coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example: Preparation of UV-curable hydrophilic coating:

[0028] The hydrophilic unsaturated polyester amide urea is mixed with acrylate monomer and initiator 184 at a weight ratio of 20:10:1, and then 3% of the total surfactant, 0.05% of the defoamer and the The total amount of 100% water is put into a container with a stirrer, placed in a water bath, protected by nitrogen, and stirred at 25°C for 30 minutes to prepare a brown-black liquid UV curable hydrophilic paint with a certain viscosity.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an ultraviolet light-cured hydrophilic coating and a preparation method thereof. The method comprises the steps of mixing hydrophilic unsaturated polyester-urea amide, acrylic ester crosslinking monomers and an initiator according to a certain ratio; adding a proper amount of auxiliary agents and a diluent; stirring at a temperature of 25 DEG C, and thus the brownish black ultraviolet light-cured hydrophilic coating having a certain viscosity is obtained. The ultraviolet light-cured hydrophilic coating employs ultraviolet light to cure for film formation, has the characteristics of high efficiency, energy conservation and good hydrophilicity. The ultraviolet light-cured hydrophilic coating is expected to be used for hydrophilic coating of hydrophilic aluminium foil, plastic, glass, and the like, and provides excellent hydrophilic performance for the above.

Description

technical field [0001] The invention relates to a chemically synthesized hydrophilic polymer coating and a method thereof. Using unsaturated diacid (anhydride) (maleic anhydride or fumaric acid) and C 2 ~C 4 Fatty dihydric alcohol, diethylene glycol, and urea are copolymerized to obtain a hydrophilic unsaturated polyester amide urea matrix resin. This kind of resin is mixed with acrylate cross-linking monomer, and one or more of 1173, 184, TPO is used as an initiator, and additives and diluents are added to prepare a UV-curable hydrophilic coating. This type of hydrophilic coating can be used as hydrophilic coating for substrates such as glass, plastic, copper sheet (foil), aluminum sheet (foil) and the like. When used in glass, it can improve the anti-fog, anti-fouling, and light transmittance of glass; when used in plastic, it can improve its biocompatibility; when used in aluminum foil, it can improve the heat exchange effect of aluminum foil used in air conditioners, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D177/12C09D175/02C09D7/12
Inventor 郭文迅
Owner 郭文迅
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap