Argentiferous gold-simulating copper alloy and preparation method thereof

A technology of copper alloy and imitation gold, applied in the field of alloy materials, can solve the problems such as the copper alloy that cannot well reflect the anti-discoloration performance, cannot reach the imitation gold, and the copper alloy is not easy to cut, so as to improve the anti-discoloration performance and easy Processing, the effect that is conducive to processing and molding

Inactive Publication Date: 2013-01-16
HANGZHOU ZHENDA HARDWARE MACHINERY
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is mainly to solve the difficult-to-cut performance of copper alloy, so as to obtain an easy-to-cut copper alloy. Although the copper alloy has certain anti-discoloration performance in artificial sweat or salt spray atmosphere, but because it is a white copper alloy , on the one hand, it cannot meet the requirements of gold-like copper alloy; on the other hand, it cannot reflect its anti-tarnish performance well.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Argentiferous gold-simulating copper alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A silver-containing imitation gold-copper alloy, the alloy is mainly composed of the following raw materials in weight percentage:

[0032] Ag: 5%; Zn: 25%; Al: 2.0%; Si: 0.05; the balance is Cu, and the sum of weight percentages of all elements is 100%.

[0033] The silver-containing imitation gold-copper alloy is prepared according to the following method:

[0034] A. Smelting: Weigh each raw material according to the above weight percentage, clean the above raw materials with acid, which can effectively remove the oxide layer on the metal surface, dry it after cleaning with acid, and then load it in batches In the crucible of the vacuum intermediate frequency induction melting furnace, the temperature is controlled at 1225°C to melt to clear liquid, then melted and stirred for 30 minutes, and then poured into a Ф70 water-cooled red copper crystallizer to obtain silver-containing imitation gold alloy ingots;

[0035] B, annealing treatment: under the condition that t...

Embodiment 2

[0038] A silver-containing imitation gold-copper alloy, the alloy is mainly composed of the following raw materials in weight percentage:

[0039] Ag: 5%; Zn: 25%; Al: 3.6%; In: 0.4%; Ni: 1%; the balance is Cu, and the sum of weight percentages of all elements is 100%.

[0040] The silver-containing imitation gold-copper alloy is prepared according to the following method:

[0041] A. Smelting: Weigh each raw material according to the above weight percentage, clean the above raw materials with acid, which can effectively remove the oxide layer on the metal surface, dry it after cleaning with acid, and then load it in batches In the crucible of the vacuum intermediate frequency induction melting furnace, the temperature is controlled at 1200 ° C to melt to clear liquid, then melt and stir for 60 minutes, and then pour it into a Ф70 water-cooled red copper crystallizer to obtain silver-containing imitation gold alloy ingots;

[0042] B, annealing treatment: under the condition ...

Embodiment 3

[0045] A silver-containing imitation gold-copper alloy, the alloy is mainly composed of the following raw materials in weight percentage:

[0046] Ag: 20%; Zn: 0.4%; toner: 1%, the toner is selected from one of aluminum, indium, nickel, tin; RE: 1%; Si: 1%; the balance is Cu, the sum of weight percentages of all elements is 100%.

[0047] The silver-containing imitation gold-copper alloy is prepared according to the following method:

[0048] A. Smelting: Weigh each raw material according to the above weight percentage, clean the above raw materials with acid, which can effectively remove the oxide layer on the metal surface, dry it after cleaning with acid, and then load it in batches In the crucible of the vacuum intermediate frequency induction melting furnace, the temperature is controlled at 1300 ° C to melt to clear liquid, then melt and stir for 10 minutes, and then pour it into a Ф70 water-cooled copper crystallizer to obtain silver-containing imitation gold alloy ing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to argentiferous gold-simulating copper alloy and a preparation method thereof and belongs to the technical field of alloy materials. The argentiferous gold-simulating copper alloy aims to solve the technical problems of poor color change resistance and gold-simulating effect of copper alloy in the prior art, and mainly comprises, by weight, 1%-20% of Ag, 0.5%-40% of Zn, not more than 1% of Si, not more than 1% of RE, 0.4-5.0% of color matching agents and the balance Cu. The preparation method includes: melting the raw materials at the temperature of 1200-1300 DEG C, performing annealing treatment at the temperature of 500-600 DEG C, forging and performing hot rolling so that the argentiferous gold-simulating copper alloy is obtained. The argentiferous gold-simulating copper alloy is high in color change resistance and good in gold-simulating effect and has the advantages of capability of achieving apparent color and luster of 14K-18K gold, simple technical process, good processability and easiness in processing.

Description

technical field [0001] The invention relates to an imitation gold-copper alloy, in particular to a silver-containing imitation gold-copper alloy and a preparation method thereof, belonging to the technical field of alloy materials. Background technique [0002] Gold has a beautiful golden yellow color, good chemical stability, and has the function of preserving value. Therefore, it has long been the material of choice for products such as jewelry, art sculptures, religious supplies, and prizes. However, in recent years, with the change of people's consumption concept, more attention is paid to the novelty of styles for jewelry, art sculptures, religious articles, prizes, etc., and the requirements for the value preservation function are weakened. Therefore, cheap and attractive imitation gold alloy products obtain people's general attention. [0003] At present, domestic imitation gold products are mainly imitation gold electroplating products and copper-based imitation gol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C9/00C22C1/02C22F1/08
Inventor 张正良
Owner HANGZHOU ZHENDA HARDWARE MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com