A kind of metal cutting fluid and its processing technology

A metal cutting fluid and production process technology, applied in the petroleum industry, lubricating composition, etc., can solve the problems of failing to meet the requirements of environmental protection, harmful to the human body, heavy metals and nitrite ions, etc., to achieve longer service life, good chemical The effect of stability and high technical content

Inactive Publication Date: 2015-10-28
TIANCHANG RUNDA METAL ANTIRUST AUX
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are many kinds of cutting fluids, but most of them contain heavy metals and nitrite ions that are harmful to the human body, which cannot meet the requirements of environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of metal cutting fluid and its processing technology
  • A kind of metal cutting fluid and its processing technology
  • A kind of metal cutting fluid and its processing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Metal cutting fluid, including the following components by mass percentage:

[0039]

[0040]

[0041] 2. Production process:

[0042] A: Synthetic triethanolamine oleic acid soap

[0043] Add triethanolamine and oleic acid to the reaction kettle according to the specified amount, start stirring, and slowly raise the temperature for 3-5°C / 10 minutes to 80±1°C. The temperature rise rate and the controlled temperature do not produce different reactants, and the lubrication of the finished product And anti-rust performance is different, heat preservation reaction at this temperature for 4 hours, to obtain viscous triethanolamine oleic acid soap, standby.

[0044] B: Add 400 kg of deionized water to the reactor, then add a specified amount of sodium tripolyphosphate into the reactor, start stirring, slowly raise the temperature to 60°C, and add triethanolamine oleic acid soap after the sodium tripolyphosphate is completely dissolved. After the oleic acid soap is com...

Embodiment 2

[0047] Metal cutting fluid, including the following components by mass percentage:

[0048]

[0049]

[0050] The production process of metal cutting fluid comprises the following steps:

[0051] A: Synthetic triethanolamine oleic acid soap

[0052] Add the above-mentioned triethanolamine and oleic acid in mass percentage to the reaction vessel, stir, raise the temperature to 81°C for 3°C / 10 minutes, and keep the temperature for 3 hours to obtain triethanolamine oleic acid soap for later use;

[0053] B: Add 300 kg of deionized water into the reaction vessel, then add the above-mentioned sodium tripolyphosphate in terms of mass percentage, stir, heat up to 55°C, add triethanolamine oleic acid soap after the sodium tripolyphosphate is completely dissolved, wait After the oleic acid soap is completely dissolved, add the above-mentioned other components in terms of mass percentages in the above order, and after all the substances are dissolved, raise the temperature of the...

Embodiment 3

[0056] Metal cutting fluid, including the following components by mass percentage:

[0057]

[0058]

[0059] The production process of metal cutting fluid comprises the following steps:

[0060] A: Synthesis of triethanolamine oleic acid soap Add the above-mentioned triethanolamine and oleic acid by mass percentage into the reaction vessel, stir, heat up for 5°C / 10 minutes to 79°C, keep warm for 4.5 hours to obtain triethanolamine oleic acid soap for later use;

[0061] B: Add 500 kg of deionized water to the reaction vessel, then add the above-mentioned sodium tripolyphosphate in terms of mass percentage, stir, heat up to 55°C, and add triethanolamine oleic acid soap after the sodium tripolyphosphate is completely decomposed. After the oleic acid soap is completely dissolved, add the above-mentioned other components in terms of mass percentages in the above order, and after all the substances are dissolved, raise the temperature of the entire reactant to 79 ° C, and ke...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a metal cutting liquid, the metal cutting liquidcomprises following components in percentages by mass: 1-10% of sodium naphthenate, 5-15% of sodium petroleum sulfonate, 8-25% of 32# engine oil, 1-10% of vegetable oleic acid, 7-12% of triethanolamine, 0.5-5% of cocinic acid triethanolamine, 0.5-5% of 42# chlorinated paraffin, 1-5.0% of OP-10 emulsifier, 1-6% of sodium tripolyphosphate, 0.01-0.4% of bactericide, 0.01-0.3% of anti-foaming agent and the balance of de-ionized water. The cutting liquid can provide buffer action provided by the liquid lubricant, chemical adhesive force and excellent extreme pressure lubricating performance provided by the boundary lubrication during the metal processing by combination of the above effective components; the product does not contain nitrite which has serious damage to human body and has no heavy metal ion which pollutes the environment.

Description

technical field [0001] The invention relates to component processing auxiliary materials, in particular to a metal cutting fluid. Background technique [0002] At present, there are many kinds of cutting fluids, but most of them contain heavy metals and nitrite ions that are harmful to the human body, which cannot meet the requirements of environmental protection. Contents of the invention [0003] Based on the above defects in the prior art, the object of the present invention is to provide a metal cutting fluid, which can provide the buffering effect of liquid lubricants, the chemical adhesion and Good extreme pressure lubrication performance, this product does not contain nitrite that is seriously harmful to the human body, and does not pollute the environment with heavy metal ions. [0004] Another object of the present invention is to provide a production process of metal cutting fluid. [0005] A kind of metal cutting fluid provided by the invention comprises the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M173/00C10M177/00C10M169/04C10N40/22C10N30/12C10N30/06C10N30/04
Inventor 林伟江海涛江海波江浩
Owner TIANCHANG RUNDA METAL ANTIRUST AUX
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More