Silver phosphate/titanium dioxide composite material for photochemical catalysis and preparation method thereof

A technology of titanium dioxide and composite materials, applied in the field of photocatalysis, can solve problems such as silver phosphate corrosion and reduce structural stability, and achieve the effects of increasing active points, easy operation, and large specific surface area

Inactive Publication Date: 2013-02-27
WUHAN INSTITUTE OF TECHNOLOGY
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, silver phosphate is slightly soluble in water, which reduces its structural stability
Moreover, the photocatalytic process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1:

[0021] 1) Preparation of titanium dioxide: Dissolve 5 mL of titanium tetraisopropoxide in 30 mL of isopropanol, adjust the pH of the solution to 1 with concentrated hydrochloric acid; take another 0.5 mL of deionized water and dissolve it in 8 mL of isopropanol; mix the above two solutions Alternately filter through cellulose filter paper, and then use 50 mL of ethanol to wash away unreacted titanium tetraisopropoxide; finally, place the cellulose filter paper attached with titanium dioxide gel at 450 o In an air atmosphere, remove the cellulose filter paper to obtain titanium dioxide;

[0022] 2) Dissolve 0.003 mol of sodium dihydrogen phosphate in 20 mL of deionized water, and then take 0.06 g of titanium dioxide to ultrasonically disperse it in the above solution;

[0023] 3) Dissolve 0.004mol of silver acetate in 20mL of deionized water, slowly add it dropwise to the solution obtained in step 2 under magnetic stirring conditions, continue to react for...

Example Embodiment

[0024] Example 2:

[0025] 1) Same as step 1 of Example 1;

[0026] 2) Dissolve 0.006mol of potassium dihydrogen phosphate in 20mL of deionized water, and then take 0.08g of titanium dioxide to ultrasonically disperse it in the above solution;

[0027] 3) Dissolve 0.008mol of silver acetate in 20mL of deionized water, slowly add it dropwise to the solution obtained in step 2 under magnetic stirring conditions, continue to react for 6 hours after the dropwise addition, filter, wash, 60 o The silver phosphate / titanium dioxide composite material was obtained by vacuum drying under C.

Example Embodiment

[0028] Example 3:

[0029] 1) Same as step 1 of Example 1;

[0030] 2) Dissolve 0.003 mol of sodium dihydrogen phosphate in 20 mL of deionized water, and then take 0.06 g of titanium dioxide to ultrasonically disperse it in the above solution;

[0031] 3) Dissolve 0.004mol of silver nitrate in 20mL of deionized water, slowly add it dropwise to the solution obtained in step 2 under magnetic stirring conditions, continue to react for 6 hours after the dropwise addition, filter, wash, 60 o The silver phosphate / titanium dioxide composite material was obtained by vacuum drying under C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a silver phosphate/titanium dioxide composite material for photochemical catalysis and a preparation method thereof. The preparation method comprises the following steps of (1) preparing titanium dioxide; (2) dissolving a certain amount of dihydric phosphate into deionized water to prepare a solution with the concentration of 0.05-0.5mol/L and then dispersing 0.05-0.1g of titanium dioxide obtained in the step (1) in the solution; and (3) dissolving a certain amount of silver salt in the deionized water to prepare a solution with the concentration of 0.05-0.5mol/L and then adding the solution into the solution obtained in the step (2) under the magnetic stirring condition in a dropwide mode; continuing to perform reaction for 6 hours after dropwise addition and then performing filtering, washing and vacuum drying at 60 DEG C to obtain the silver phosphate/titanium dioxide composite material. The silver phosphate/titanium dioxide composite material for the photochemical catalysis has the remarkable advantages of effectively avoiding composition of photogenerated electrons and holes, promoting the photochemical catalysis process, increasing an active point of the photochemical catalysis and being simple in preparation method.

Description

technical field [0001] The invention relates to a high-efficiency photocatalyst silver phosphate / titanium dioxide composite material and a preparation method thereof, belonging to the field of photocatalysis. Background technique [0002] With the rapid development of social economy, environmental problems are becoming more and more serious. Using photocatalysis to eliminate and degrade organic pollutants in wastewater is an effective pollution control method, and it is also one of the research hotspots in the field of environmental protection. In recent years, people have researched and developed many semiconductor photocatalysts, among which silver phosphate, a highly efficient visible light catalyst, has received more and more attention. However, silver phosphate is slightly soluble in water, which reduces its structural stability. Moreover, the photocatalytic process is usually accompanied by the conversion of silver ions to elemental silver, resulting in the photocorr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J27/18
Inventor 陈郁勃李亮刘玉兰郑华明喻湘华
Owner WUHAN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap