Manufacturing method of papermaking sewage type cationic polyacrylamide
A technology of polyacrylamide and paper-making sewage, which is applied in the field of paper-making sewage-type cationic polyacrylamide, can solve the problems of unreachable, backward technology, high price, etc., and achieve high stability, good adsorption and high purity.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0012] Example 1
[0013] First, the initiation system A is added to the mixed solution of acrylamide and cationic monomer, and then the initiation system B is added. The vertical reaction kettle equipment is used to react for 0.5 hours to 2 hours at normal temperature and pressure to form a transparent gel, which is then processed by Aging at 80-95℃ for 0.5 hours to 2 hours, after the process of granulation→salting out→drying→pulverizing→screening→packaging, the ionicity is between 20%-30% and the molecular weight is 800-12 million. Cationic polyacrylamide product with apparent viscosity greater than 40cP; the initiator system A is azo chemicals added to the mixed solution, which are V40, V44 and V50, and the addition amount is 0.001 times the weight of the mixed solution, and the initiator system is added to the mixed solution. B is an oxidizing agent and a reducing agent, the oxidizing agent is potassium persulfate and sodium persulfate, and the reducing agent is sodium sul...
Example Embodiment
[0014] Example 2
[0015] First, the initiation system A is added to the mixed solution of acrylamide and cationic monomer, and then the initiation system B is added. The vertical reaction kettle equipment is used to react for 0.5 hours to 2 hours at normal temperature and pressure to form a transparent gel, which is then processed by Aging at 80-95℃ for 0.5 hours to 2 hours, after the process of granulation→salting out→drying→pulverizing→screening→packaging, the ionicity is between 20% and 30%, the molecular weight is 800-12 million, and the apparent Cationic polyacrylamide product with a viscosity greater than 40cP; the initiator system A added to the mixed solution is an azo chemical, V59 and V60, and the addition amount is 0.002 times the weight of the mixed solution, and the initiator system B added to the mixed solution is an oxidant and reducing agent, the oxidizing agent is potassium hydrogen persulfate, sodium hydrogen persulfate and ammonium persulfate, the reducing ...
PUM
Property | Measurement | Unit |
---|---|---|
Apparent viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap