Modified bamboo fiber reinforced polypropylene composite material and preparation method thereof

A composite material and bamboo fiber technology, which is applied in the field of composite modification of natural bamboo fiber and its composite material with reinforced polypropylene and its preparation, to achieve the effects of large binding energy, high specific modulus, and simple preparation method

Active Publication Date: 2015-07-01
ORINKO NEW MATERIAL CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the plant fiber has not been modified, so it can only be used as a composite material with general performance, which limits the application field of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Homopolypropylene 60 parts

[0054] Copolymerized polypropylene 20 parts

[0055] 10 parts bamboo fiber

[0056] Coupling agent: KH550 1 part

[0057] Compatibilizer: polypropylene grafted maleic anhydride 1 part

[0058] Chemical modifier: 1 part of dihydro-2,5-dioxofuran

[0059] Antioxidant: (1010 / 168=1:1 mass ratio) 0.2 parts

[0060] Heat stabilizer: 0.2 parts of methyl tin mercaptide

[0061] UV absorber: 0.3 parts of phenyl o-hydroxybenzoate

[0062] Dispersant: 0.3 parts of sodium dipolyphosphate

[0063] Processing aid: 0.5 parts of calcium stearate

Embodiment 2

[0065] Homopolypropylene resin 77 parts

[0066] Bamboo fiber 20 parts

[0067] Coupling agent: KH560 2 parts

[0068] Compatibilizer: polypropylene grafted styrene 2 parts

[0069] Chemical modifier: 0.8 parts of chromium picolinate

[0070] Antioxidant: (1010 / DSTDP =1:1 mass ratio) 0.6 parts

[0071] Heat stabilizer: 0.2 parts of octyltin maleate

[0072] UV absorber: 0.2 parts of 2-(2'-hydroxy-5'-methylphenyl)benzotriazole

[0073] Dispersant: sodium triethylhexylphosphate 0.1 part

[0074] Processing aid: 0.2 parts of ethylene bis stearamide

Embodiment 3

[0076] 67 parts of copolymerized polypropylene resin

[0077] Bamboo fiber 30 parts

[0078] Coupling agent: KH570 0.5 parts

[0079] Compatibilizer: polypropylene grafted styrene 0.5 parts

[0080] Chemical modifier: 1.5 parts of aluminate

[0081] Antioxidant: (1010 / DSTDP =1:1 mass ratio) 0.2 parts

[0082] Heat stabilizer: 0.6 parts of stannous sulfate

[0083] UV absorber: 0.6 parts of 2,4-dihydroxybenzophenone

[0084] Dispersant: Sodium Lauryl Sulfate 0.6 parts

[0085] Processing aid: modified ethylene bis stearamide 1.0 parts

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a modified bamboo fiber reinforced polypropylene composite material which comprises polypropylene resin, bamboo fibers, compatilizer, coupling agent, chemical modifier and the like; first, prepared natural fibers are modified and then the fibers are mixed with other components; and the mixture is extruded and formed by a double-screw extruder. According to the preparation method, the production procedures are simple and the production efficiency is improved; and the prepared modified bamboo fibers have more excellent performance, and have the advantages of environmental friendliness, sound absorption, heat insulation, low density, low shrinkage, good processing and forming performance, degradability and excellent integrated mechanical properties.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a composite modification of natural bamboo fiber and its composite material with reinforced polypropylene and a preparation method thereof. [0002] technical background [0003] In recent years, people's awareness of environmental protection has been continuously enhanced, and the environmental pollution caused by plastics with excellent processing performance and used in various industrial products has become a common concern. In particular, fiber-reinforced composite materials are usually composed of glass fibers, carbon fibers, etc. and plastics. Waste disposal is difficult and the production environment is harsh, which adds a great burden to the environment. Therefore, the use of natural fibers as reinforcing materials to make environmentally friendly composites has attracted people's attention. The use of plant fibers and synthetic resins for composite r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/14C08L97/02C08J5/06B29B9/06B29C47/92B29C48/92
CPCB29C47/92B29C47/6087B29C2947/92895B29C47/0011B29C2947/92704B29C48/04B29C48/40B29C48/625B29C48/92B29C2948/92704B29C2948/92895
Inventor 周海安峰任东方
Owner ORINKO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka