Preparation method of double-surface concave-convex bamboo fiber fabric

A bamboo fiber fabric, double-sided technology, applied in fabrics, textiles, textiles and papermaking, etc., can solve the problems of poor moisture absorption and perspiration, improve pilling performance, improve shrinkage, and increase fabric tightness Effect

Inactive Publication Date: 2013-03-27
SHANGHAI SHUIXING HOME TEXTILE
View PDF7 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the shortcomings of bamboo fiber itself, the corn fiber currently on the market is only used in clothing and yarn.
Traditional summer quilts are basically made by carding and laying nets, which have poor moisture absorption and perspiration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of the double-sided concave-convex bamboo fiber fabric of the present invention comprises the following steps: warping→sizing→reeding→jacquard interweaving, wherein the warp ratio of jacquard interweaving is 45-55%, and the weft ratio is 55-45%, The warp and weft are bamboo fiber and polyester fiber respectively.

[0026] In the present invention, the double-sided concave-convex bamboo fiber fabric adopts a yarn-dyed jacquard double-layer fabric interwoven with one set of warps and two sets of wefts, and one set of wefts (thick D polyester) is a core-filling weft, and its function is mainly to increase The thickness and elasticity of the fabric make the pattern full; at the bottom of the fabric, a set of weft threads is cleverly used to interweave with two sets of warp threads on the outside and inside.

[0027] In the present invention, the warping is carried out by a warping frame, the diameter of the warp beam is 1000mm, the warping speed is 10...

Embodiment 1

[0036] Warping→sizing→reeding→jacquard interweaving.

[0037] The warp and weft are respectively bamboo fiber and polyester fiber, wherein the ratio of bamboo fiber to polyester fiber is 45:55.

[0038] The warping is carried out by a warping frame, the diameter of the warp beam is 1000mm, the warping speed is 100m / min-125m / min, and the number of warp ends is 6782. The warping frame is a U-shaped frame type shuttle.

[0039] The sizing is layered into the drying room through the sizing machine through the sizing machine. The tension in each zone of the sizing machine is kept balanced. The single size tank has wet split twisting. The maximum pressure of the main sizing roller is 40kN, and the sizing temperature is 93°C . The slurry includes PVA179937.5kg, DF-A 55kg and TX991 8kg.

[0040] The reed number of the reed is 56 / 2.

[0041]The type of the interweaving loom is a GAMMA type rapier loom, and the weaving structure is a compact jacquard fabric. The process conditions o...

Embodiment 2

[0045] Warping→sizing→reeding→jacquard interweaving.

[0046] The warp and weft are respectively bamboo fiber and polyester fiber, wherein the ratio of bamboo fiber to polyester fiber is 50:50.

[0047] The warping is carried out by a warping frame, the diameter of the warp beam is 1000mm, the warping speed is 100m / min-125m / min, and the number of warp ends is 6782. The warping frame is a U-shaped frame type shuttle.

[0048] The sizing is layered into the drying room through the sizing machine through the sizing machine. The tension in each zone of the sizing machine is kept balanced. The single size tank has wet split twisting. The maximum pressure of the main sizing roller is 40kN, and the sizing temperature is 93°C . The slurry includes PVA1799 37.5kg, DF-A 55kg and TX991 8kg.

[0049] The reed number of the reed is 56 / 2.

[0050] The type of the interweaving loom is a GAMMA type rapier loom, and the weaving structure is a compact jacquard fabric. The process conditions...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a double-surface concave-convex bamboo fiber fabric, comprising the following steps: beaming, slashing, reeding and jacquard-interweaving, wherein in the process of jacquard-interweaving, the warp yarns account for 45-55% and the weft yarns account for 55-45%; and the warp yarns and the weft yarns are respectively bamboo fibers and polyester fibers. In comparison with the prior art, the core filling warp or core filling weft is added between the surface and inner wefts or between the surface and inner warps or between the surface and inner layers of the fabric, so that the fabric is thick and elastic, and the patterns, if quilted on the fabric, are permanently embossed, so the fabric is thick and decorative; by a remarkable difference of different materials as well as weft and warp yarns differing in thickness in shrinkage performance, a plastic effect is formed, and an original and unique double-surface concave-convex effect is guaranteed; the fabric is strong in three-dimensional sense, softer in touch and more friendly to the skin, and the fabric provides a more comfortable sleep microenvironment for the users; therefore, the purpose of the invention is achieved.

Description

technical field [0001] The invention relates to a preparation method of a bamboo fiber fabric, in particular to a preparation method of a double-sided concave-convex bamboo fiber fabric. Background technique [0002] Bamboo fiber is a natural and environmentally friendly degradable fiber, which is made of bamboo and processed by special technology. The whole process of bamboo fiber manufacturing adopts high-tech means. It is the fifth largest natural textile element after the four natural fibers of cotton, linen, wool and silk. It is a real "ecological fiber" with good air permeability and instant water absorption. Antibacterial, antibacterial, anti-mite and deodorant. [0003] Bamboo fiber not only has excellent manufacturing characteristics and wider uses, but also belongs to textiles that are beneficial to human health. It is one of the leading products in the new environmental protection fiber market in the 21st century. As an environmentally friendly new fiber, bamboo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D21/00D03D15/00D03D15/217D03D15/283D03D15/50D03D15/54D03D15/567
Inventor 沈守兵陈秀苗
Owner SHANGHAI SHUIXING HOME TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com