High-temperature and high-humidity rapid drying process method for wood

A high-temperature, high-humidity drying and fast-drying technology, which is applied in the wood drying process and the high-temperature, high-humidity fast drying process of wood, can solve the problems of fast-growing wood being easy to deform and crack, reducing the grade of fast-growing wood, and prone to shrinkage and collapse. The effects of shrinkage and collapse, uniform distribution of moisture content, and broadening of use channels

Active Publication Date: 2013-04-03
贵州保城新材料有限公司
View PDF9 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, fast-growing wood grows faster and makes it more prone to deformation and cracking, especially during the drying process, it is prone to shrinkage and collapse, which not only reduces the grade of fast-growing wood and reduces the yield of wood, but also makes fast-growing wood easy to deform and crack during later use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Humidification and heating steps: stack 5 pieces of fast-growing poplar wood with a thickness of 2mm together to form a stack, use trays and spacers with uniform specifications, and the distance between the spacers and the end of the wood during stacking is within 3cm, and the distance between the spacers At 15-25cm, the spacers are arranged in a straight line in the vertical direction, and the briquettes are pressed on the stacked wood pile; then the fast-growing poplar wood is stacked in the drying kiln, the kiln door is closed, and the humidification valve is opened. Quick humidification directly humidifies to relative humidity ≥ 98%, so that the drying kiln is filled with water vapor.

[0029] (2) Heating and humidification pretreatment steps: keep the humidification valve open, keep the relative humidity ≥ 98%, then open the heating valve for the first time and quickly heat until the dry bulb temperature is 1°C higher than the wet bulb temperature and keep it fo...

Embodiment 2

[0033] (1) Humidification and heating steps: stack 2 pieces of maple wood with a thickness of 24mm together to form a whole stack, use pallets and spacers with uniform specifications, and when stacking, the distance between the spacers and the end of the wood is within 3cm, and the distance between the spacers is 15~ 25cm, the spacers are neatly arranged in a straight line in the vertical direction, and the briquettes are pressed on the stacked wood pile, then the wood is stacked in the drying kiln, the kiln door is closed, and the humidification valve is opened to quickly humidify inward and directly humidify to relative humidity. ≥98%, so that the drying kiln is filled with water vapor.

[0034] (2) Heating and humidification pretreatment steps: keep the humidification valve open, keep the relative humidity ≥ 98%, then open the heating valve for the first time and quickly heat until the dry bulb temperature is 2°C higher than the wet bulb temperature and keep it for 6 hours. ...

Embodiment 3

[0038] (1) Humidification and heating steps: Use the conventional stacking method to stack the 50mm thick Qinggang wood, and use pallets and spacers with uniform specifications. The strips are neatly formed into a straight line in the vertical direction, and the briquettes are pressed on the stacked wood pile; then the wood is stacked in the drying kiln, the kiln door is closed, and the humidification valve is opened to quickly humidify inward and directly humidify to a relative humidity of ≥98%. , so that the drying kiln is filled with water vapor.

[0039] (2) Heating and humidification pretreatment steps: keep the humidification valve open, keep the relative humidity ≥ 98%, then open the heating valve for the first time and quickly heat until the dry bulb temperature is 1.5°C higher than the wet bulb temperature and keep it for 7 hours.

[0040] (3) High-temperature and high-humidity drying step: continuous humidification to control the relative humidity in the drying kiln ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a wood drying process technology, in particular to a high-temperature and high-humidity rapid drying process method for wood, belonging to the field of wood processing. The high-temperature and high-humidity rapid drying process method comprise the following steps of: (1) humidifying and heating; (2) heating and humidifying pretreatment; and (3) high-temperature and high-humidity drying. According to the invention, the drying process problems that the traditional drying process cannot be used for drying hardwood, difficultly-dried hardwood and fast growing wood easily undergoing shrinkage and collapse after drying are solved, the dried wood is uniform in the distribution of moisture content and low in moisture content gradient in a thickness direction, and the defect that the fast growing wood is shrunk and collapsed after being dried is overcome. Meanwhile, the process flow of the traditional drying technology is simplified, and the most common drying process method with broadest applicable range is formed, is suitable for any varieties of tree wood with the thickness below 100mm and is easier to master by a technician.

Description

technical field [0001] The invention relates to a wood drying process technology, in particular to a high-temperature, high-humidity rapid drying process for wood, which belongs to the field of wood processing. Background technique [0002] Wood is an anisotropic material. The structure of sapwood and heartwood of wood is different, even if the structure of different sapwood or heartwood of the same tree is different, this determines that the "research and application of wood" is a A highly practical subject. As a key process of wood processing and utilization, wood drying also shows its practical characteristics. Therefore, for the research and application of wood drying technology, on the one hand, it is necessary to strengthen the study and research of wood drying theoretical knowledge, including wood characteristics, especially permeability, the characteristics and causes of wood drying defects, the movement state and residual moisture in wood. At the same time, it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F26B9/06F26B3/04F26B1/00F26B21/08F26B21/10
Inventor 葛克宇潘成锋
Owner 贵州保城新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com