A Method for Quantitative Analysis of Solid Phase Dispersion Distribution in Semi-solid Slurry Structure

A technology of semi-solid slurry and dispersion distribution, which is applied in image analysis, image data processing, special data processing applications, etc. It can solve the problems of being unable to quantitatively evaluate the solid phase distribution of semi-solid slurry tissue, and achieve good performance and use Convenience and easy operation

Inactive Publication Date: 2015-09-09
KUNMING UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the above-mentioned shortcomings of being unable to quantitatively evaluate the degree of solid phase distribution in the semi-solid slurry structure, the purpose of the present invention is to provide a method that is simple to operate and can quantitatively evaluate the degree of solid phase distribution in the semi-solid slurry structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Method for Quantitative Analysis of Solid Phase Dispersion Distribution in Semi-solid Slurry Structure
  • A Method for Quantitative Analysis of Solid Phase Dispersion Distribution in Semi-solid Slurry Structure
  • A Method for Quantitative Analysis of Solid Phase Dispersion Distribution in Semi-solid Slurry Structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: The specific steps of the method for the quantitative analysis of the solid phase dispersion distribution in the semi-solid slurry tissue of the present embodiment are:

[0027] (1) According to the structure photo of the semi-solid slurry, the solid-liquid two phases in the structure are distinguished, and the solid phase is separated by binary processing on the picture; in this example, the semi-solid structure to be analyzed is a tin-bronze alloy ,Such as figure 1 As shown, use photoshop and Image J software to figure 1 The solid phase of the semi-solid tissue shown is separated and processed, and the results are as follows figure 2 As shown, the black area is the solid phase;

[0028] (2) Count the number of solid phases and calculate the total area of ​​solid phases, calculate the average area of ​​each solid phase, and then draw the same area as the statistical number and the average area of ​​each solid phase on the photo of the original tissue o...

Embodiment 2

[0030] Embodiment 2: The specific steps of the method for the quantitative analysis of the solid phase dispersion distribution in the semi-solid slurry tissue of the present embodiment are:

[0031] (1) According to the tissue photo of the semi-solid slurry, the solid-liquid two phases in the tissue are distinguished, and the solid phase is separated by dyeing the picture; in this example, the semi-solid tissue to be analyzed is an aluminum-silicon alloy, such as Figure 5 As shown, the result is as Image 6 As shown, the black area is the solid phase;

[0032] (2) Count the number of solid phases and calculate the total area of ​​solid phases, calculate the average area of ​​each solid phase, and then draw the same area as the statistical number and the average area of ​​each solid phase on the photo of the original tissue of the semi-solid slurry The same circles, each circle is distributed in an ideal dispersed state of semi-solid particles. In this example, use Image J so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for quantitatively analyzing solid phase dispersion distribution in semi-solid slurry tissue and belongs to the field of metal semi-solid slurry tissue performance analysis. The method includes separating solid phase in the semi-solid slurry tissue out, calculating the total size of the solid phase, calculating and drawing an ideal dispersion degree distribution pattern of the solid phase, and calculating and obtaining dispersion distribution degree coefficient through comparing an ideal distribution state with a real distribution state of the solid phase. With the method for quantitatively analyzing solid phase dispersion distribution in semi-solid slurry tissue, dispersion distribution degree of the solid phase in the semi-solid tissue can be given quantitatively and the range of the dispersion distribution degree is greater than 0 and smaller than 1. A greater number indicates more even distribution degree of the solid phase in the semi-solid tissue and better performance of the semi-solid tissue. The method for quantitatively analyzing solid phase dispersion distribution in semi-solid slurry tissue is simple to operate and convenient to use.

Description

technical field [0001] The invention relates to a method for quantitatively analyzing the dispersion distribution of the solid phase in the structure of semi-solid slurry, which belongs to the field of analyzing the structure and performance of metal semi-solid slurry. Background technique [0002] Semi-solid metal technology is a technology between liquid and solid forming proposed in the 1970s. It has broad application prospects in the fields of automobiles, aviation, and aerospace due to its characteristics of stable filling, high compactness of parts, small thermal impact on the mold, high mechanical properties, and low forming force. Among them, the preparation of a semi-solid metal slurry with a uniform and fine non-dendritic structure, that is, a semi-solid structure in which the spherical solid phase is uniformly distributed and the liquid phase is uniformly distributed around the solid phase, is the most important in the semi-solid metal forming technology. It is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G06T7/60G06F17/50
Inventor 王佳肖寒周荣周荣峰卢德宏蒋业华吴龙彪
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com