A technology of hollow glass microspheres and composite materials, which can be applied in the fields of analysis of materials, material thermal analysis, material analysis using radiation diffraction, etc., and can solve the problems of less research on alloys.

Inactive Publication Date: 2013-05-22
ZHONGBEI UNIV
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are relatively few researches on the plasti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material modified by nylon 11-based hollow glass bead and performance test method
  • Composite material modified by nylon 11-based hollow glass bead and performance test method
  • Composite material modified by nylon 11-based hollow glass bead and performance test method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0033] The present invention will be further described below in conjunction with the accompanying drawings and embodiments.

[0034] 1. Preparation of Nylon 11 / Hollow Glass Microsphere Composite

[0035] 1.1 baking material

[0036] Nylon 11 and glass microspheres were placed in an oven for vacuum drying at 80°C and a vacuum pump pressure of 0.09Mpa for 12 hours. After drying, the materials are grouped and labeled with plastic wrap, and placed in a desiccator to maintain a low moisture content.

[0037] 1.2 Ingredients

[0038] According to the recipe requirements, proportioning respectively. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method and a test method of a composite material modified by nylon 11-based hollow glass bead. The preparation method comprises the steps of firstly putting nylon 11 and hollow glass beads into an oven at 80 DEG C and 0.09 MPa of the pressure of a vacuum pump to be dried for 12 hours in vacuum; respectively proportioning the nylon 11 and the hollow glass beads according to the required volume required in the formula; preparing materials by an extruder; drying the extruded materials; and injecting the materials to be formed. The test method comprises the steps of filling the nylon 11 with the hollow glass beads to be modified, extruding, pelletizing and preparing the composite material into a standard sample in a molten state by a double-screw extruder, and then testing various kinds of mechanical properties and the crystallization behavior of the sample. By analyzing the results, the influence of the glass beads of different content on the mechanical property and the crystallization behavior of the sample can be achieved, and the nylon 11-based modified composite material with better performance can be prepared.

Description

technical field [0001] The invention relates to the research and performance test of a nylon 11-based hollow glass microsphere modified composite material, in particular to the research and performance test of a nylon 11 / hollow glass microsphere composite material. Background technique [0002] With the rapid development of society and science and technology, the performance of a single material can no longer meet the growing situation, and high performance, multifunctionality and compounding have become the inevitable trend of material development. Compared with other polyamide materials, nylon 11 has the advantages of low water absorption, good oil resistance, low temperature resistance, good elastic memory effect, good stress crack resistance, and easy processing. However, the performance of pure nylon 11 can no longer meet the special requirements of various products for material performance, and its relatively high market price also limits the further expansion of its a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29B9/06B29C45/00B29C47/92B29B13/06C08L77/02C08K7/28G01N3/00G01N3/08G01N3/20G01N25/14G01N23/20B29C48/92
CPCB29C48/40
Inventor 王志强焦晨旭胡国胜苏忠旭谢文李迎春杨云峰郭云霞赵勃
Owner ZHONGBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap